Schmidt, George F. | Engineering Papers

NASA NTRS1981

Development of battery separator composites

Improved inorganic-organic separators developed by NASA were commercially prepared. A single-ply asbestos substrate was developed, as well as alternative substrates based on cellulose and on polypropylene fibers. The single-ply asbestos was bound with butyl rubber and was functionally superior to the formerly used polyphenylene oxide saturated sheet. Commercially prepared separators exhibited better measured separator properties than the NASA standard. Cycle life in Ni/Zn and Ag/Zn cells was related to substrate, decreasing in the order; asbestos cellulose paper nonwoven polypropylene. The cycle life of solvent-coated separators was better than aqueous in Ni/Zn cells, while aqueous coatings were better in Ag/Zn cells.

Schmidt, George F.↗

NASA NTRS1980

Alkaline battery, separator therefore

An improved battery separator for alkaline battery cells has low resistance to electrolyte ion transfer and high resistance to electrode ion transfer. The separator is formed by applying an improved coating to an electrolyte absorber. The absorber, preferably, is a flexible, fibrous, and porous substrate that is resistant to strong alkali and oxidation. The coating composition includes an admixture of a polymeric binder, a hydrolyzable polymeric ester and inert fillers. The coating composition is substantially free of reactive fillers and plasticizers commonly employed as porosity promoting agents in separator coatings. When the separator is immersed in electrolyte, the polymeric ester of the film coating reacts with the electrolyte forming a salt and an alcohol. The alcohol goes into solution with the electrolyte while the salt imbibes electrolyte into the coating composition. When the salt is formed, it expands the polymeric chains of the binder to provide a film coating substantially permeable to electrolyte ion transfer but relatively impermeable to electrode ion transfer during use.

Schmidt, George F.↗