Engineering topics

Sanjurjo, A.

Publications and source records attributed to Sanjurjo, A..

16 records

NASA NTRS1986

Characterization of solar-grade silicon produced by the SiF4-Na process

A process was developed for producing low cost solar grade silicon by the reaction between SiF4 gas and sodium metal. The results of the characterization of the silicon are presented. These results include impurity levels, electronic properties of the silicon after crystal growth, and the performance of solar photovoltaic cells fabricated from wafers of the single crystals. The efficiency of the solar cells fabricated from semiconductor silicon and SiF4-Na silicon was the same.

Sanjurjo, A.↗

NASA NTRS1983

Two-Temperature-Zone Silicon Reactor

When high purity silicon is synthesized by reduction of silicon tetrafluoride by sodium, very-fast highly exothermic reaction takes place. Controlled reaction is proposed in which SiF4-pressurized vertical reactor operates with two temperature zones. Liquid sodium feeds from nozzle at top of rector without reacting with SiF4. When sodium reaches higher temperature region at bottom, reaction takes place immediately.

Sanjurjo, A.↗

NASA NTRS1983

Liner for Silicon Reactor

Coating of sodium tetrafluoride minimizes contaminating high-purity silicon during removal from reactor chamber. Using an NaF liner, reaction products are removed by simply turning reactor chamber updside down. Liner acts as seeding agent for NaF formed during reaction and insulates nickel walls from hot reaction products.

Sanjurjo, A.↗

NASA NTRS1982

Extracting Silicon From Sodium-Process Products

New acid leaching process purifies silicon produced in reaction between silicon fluoride and sodium. Concentration of sodium fluoride and other impurities and byproducts remaining in silicon are within acceptable ranges for semi-conductor devices. Leaching process makes sodium reduction process more attractive for making large quantities of silicon for solar cells.

Kapur, V.↗

NASA NTRS1982

Producing High-Purity Silicon With Sodium

Simple technique for producing silicon for solar cells employs solid sodium to reduce silicon fluoride. Since solid rather than liquid sodium is used, careful temperature control is unnecessary, and simple feed equipment is used. Technique is energy-efficient, since reaction produces enough heat to sustain itself.

Sanjurjo, A.↗

NASA NTRS1982

Nonclogging Liquid-Sodium Nozzles

Reacting liquid sodium with gaseous silicon tetrafluoride effective way of producing high-purity silicon for solar cells; but liquid sodium is such active substance, it readily clogs nozzle through which it is introduced into reactor. Flowing through constriction around sodium-delivery nozzle, silicon tetrafluoride gas cools liquid sodium emerging from nozzle. Sodium-delivery nozzle consists of stainless-steel tube with one-fourth inch outside diameter.

Sanjurjo, A.↗

NASA NTRS1982

Bipulsating Technique for Silicon Production

Method controls reaction temperature and rate of reaction of sodium and silicon tetrafluoride by alternately adding measured amounts of reactants. Technique used in large reactor, where heat dissipation becomes serious problem, to control reactor temperatures. Highly efficient method, which would utilize almost 100 percent of raw materials.

Sanjurjo, A.↗

NASA NTRS1982

Separating Silicon From Si/NaF Mixtures

New method of extracting silicon from mixture produced when silicon tetrafluoride is reduced by sodium takes advantage of lower melting point of NaF. Method is effective at temperatures up to 400 degrees C below melting point of Si. Results in energy and economic savings: simpler and smaller furnaces, less volatization loss, and high percentage of separation.

Sanjurjo, A.↗

NASA NTRS1981

Silicon by sodium reduction of silicon tetrafluoride

High purity silicon can be prepared from the reaction of Na with SiF4 to form Si and NaF. The SiF4 is obtained from inexpensive H2SiF6 by precipitation and decomposition of Na2SiF6. Concentrations of B and P are each in the 0.1 ppm wt range in the product Si, separated from NaF by aqueous leaching.

Sanjurjo, A.↗

NASA NTRS1980

Novel duplex vapor-electrochemical method for silicon solar cells

A process was developed for the economic production of high purity Si from inexpensive reactants, based on the Na reduction of SiF4 gas. The products of reaction (NaF, Si) are separated by either aqueous leaching or by direct melting of the NaF-Si product mixture. Impurities known to degrade solar cell performance are all present at sufficiently low concentrations so that melt solidification (e.g., Czochralski) will provide a silicon material suitable for solar cells.

Nanis, L.↗

NASA NTRS1979

Novel duplex vapor: Electrochemical method for silicon solar cells

The scaled up chemical reactor for a SiF4-Na reaction system is examined for increased reaction rate and production rate. The reaction system which now produces 5 kg batches of mixed Si and NaF is evaluated. The reactor design is described along with an analysis of the increased capacity of the Na chip feeder. The reactor procedure is discussed and Si coalescence in the reaction products is diagnosed.

Nanis, L.↗

NASA NTRS1979

Novel duplex vapor-electrochemical method for silicon solar cells

The dependence of the SiF4 Na reaction initiation time and of the efficiency of the reaction on Na particle size and reaction temperature were studied. Close to 100 percent utilization of Na was obtained, and formation of byproduct fluoro-silicate was decreased to below 10 percent. A SiF4 Na reactor was built to scale up the reaction by a factor of about four and is now being tested. A scaled up melting system was built and successfully used to separate Si from kilogram quantities of SiF4 NaF mixtures. Support studies of the volatilization of NaF performed in a smaller melting system indicated minimal loss of NaF as vapor at 1410 C. The wetting of graphite was also investigated to determine the constituents of the NaF phase which promote good wetting.

Nanis, L.↗

NASA NTRS1979

Novel duplex vapor-electrochemical method for silicon solar cells

Optimization studies were carried out for the SiF4-Na reaction with solid Na feed. The goals of the study were the consistent production of high purity reaction products and the gathering of relevant information needed to scale-up the reactor. Parameters studied include: (1) effect of surface to volume ratio of Na slices on the extent of reaction; (2) effect of Na surface oxidation on the extent of reaction; (3) effect of external heating on the extent of SiF4-Na reaction; (4) effect of Na slice addition rate on extent of the reaction; and (5) SiF4-Na reaction - high pressure experiments. An investigation was also made of the possible role played by NaF as a fluxing agent during the separation of silicon by melting of the reaction product (Si + NaF) mixture. Since silicon can be produced by the thermite reaction between Na2SiF6 and Na, studies were initiated to gather information on parameters which control the efficiency of the thermite reaction.

Nanis, L.↗

NASA NTRS1978

Novel duplex vapor electrochemical method for silicon solar cells

Progress in the development of low-cost solar arrays is reported. Topics covered include: (1) development of a simplified feed system for the Na used in the Na-SiF4 reactor; (2) production of high purity silicon through the reduction of sodium fluosilicate with sodium metal; (3) the leaching process for recovering silicon from the reaction products of the SiF4-Na reaction; and (4) silicon separation by the melting of the reaction product.

Kapur, V.↗

NASA NTRS1977

Novel duplex vapor-electrochemical method for silicon solar cells

Silicon obtained by the SiF4-Na reaction was analyzed by spark source mass spectrometry (SSMS). Silicon samples prepared from induction melted powder were evaluated for electrical properties using four point probe conductivity and thermoelectric methods. SiF4-Na reaction under P sub SiF4 greater than 1 atmosphere. The amount of silicon produced was increased from 25 g per batch (in the glass reactor) to greater than 70 g per batch in the stainless steel reactor. The study of the effects of reaction variables such as P sub SiF4 and maximum temperature attained on the particle size of silicon powder showed that the silicon particle size tends to grow larger with increasing pressure of the SiF4 gas in the reaction system.

Kapur, V. K.↗

NASA NTRS1977

Novel duplex vapor-electrochemical method for silicon solar cells

Silicon was produced by alternate pulse feeding of the reactants SiF4 gas and liquid sodium. The average temperature in the reactor could be controlled, by regulating the amount of reactant in each pulse. Silicon tetrafluoride gas was analyzed by mass spectrometry to determine the nature and amount of contained volatile impurities which included silicon oxyfluorides, sulfur oxyfluorides, and sulfur dioxide. Sodium metal was analyzed by emission spectrography, and it was found to contain only calcium and copper as impurities.

Kapur, V. K.↗