Improving Qubit Coherence Time Through Detailed Materials Analysis
This study investigates the defects, imperfections, and variations in Nb thin films deposited on sapphire substrates. Two samples, W114 and W118, were fabricated using DC Magnetron Sputtering and Electron Cyclotron Resonance (ECR), respectively. Each sample was analyzed at five distinct spots to compare elemental homogeneity and variations in oxide layers. Scanning Electron Microscopy (SEM) was employed to examine surface morphology, while Energy Dispersive X-ray Spectroscopy (EDS) and X-ray Photoelectron Spectroscopy (XPS) provided elemental and chemical state analyses. SEM revealed distinct structures in W114 and a uniform surface in W118. EDS showed higher aluminum signals in W118, indicating a thinner film in comparison to W114. XPS detected a higher Nb₂O₅ signal in W118, in comparison to W114, which can be attributed to the presence of a thicker Nb₂O₅ layer in W118. These findings highlight the critical role of precise material characterization in advancing quantum computing technologies.