Nanoindentation mapping defects filtration for heterogeneous materials using generative adversarial networks

Advanced composite materials with multiple phases and heterogeneous microstructure necessitate spatial mapping characterization of elastic modulus to develop constitutive relations and overall mechanical response. Such modulus mapping can be obtained using the nanoindentation technique, where the indenter tip raster over the selected microstructure region. Typically, a surface preparation procedure is done in the specimens to ensure proper contact between the indenter tip and sample surface. However, a near-perfect surface finish is unachievable in heterogeneous materials, primarily with ceramic reinforcements, due to the differential material removal rate during polishing. Thus, the nanoindenter records localized erroneous measurements due to differences in surface roughness and corresponding force response. This study establishes a novel deep learning-based strategy to rectify incorrect experimental spatial measurements acquire during nanoindentation modulus mapping. Here, the integrated bicubic interpolation and generative adversarial networks (GANs) model was trained using 14 ceramic and 18 metallic data sets, each comprising 65,536 measurements. The developed algorithm was validated against experimental measurements on four unknown specimens. The standard deviation in measured elastic modulus reduces by ~50% in ceramics and ~72% in metallic samples. This computational framework proposes a novel approach to reducing uncertainty in materials’ properties using state-of-the-art computer vision techniques.

36 MATERIALS SCIENCE↗

Unveiling enhanced oxidation resistance and mechanical integrity of multicomponent ultra–high temperature carbides

The development of a new class of multicomponent ultra-high temperature ceramics (MC-UHTCs), often referred to as high-entropy UHTCs, has gained increased interest due to the possibility of improved thermomechanical and oxidation properties. In this study, a systematic approach by gradual addition in the UHTC components ranging from a binary to a dense quaternary (Ta,Nb,Hf,Ti)C is synthesized using spark plasma sintering (SPS). The solid solutioning was the critical factor in homogenizing the composition in the multicomponent system. The segregation of NbC and HfC was seen in binary and ternary UHTC systems, while a single-phase homogeneity was observed in the quaternary UHTC improving its hardness up to 34.8 GPa. The presence of closely spaced slip lines in the MC-UHTCs enhances resistance to indentation damage up to 72% at an applied load of 200 N. The formation of complex mixed oxide phase of Hf6Ta2O17 ensued in the lower to negligible oxidation even up to 3 min of plasma exposure with temperature exceeding 2800°C. In sum, though the entropy remains medium (0.96R) for the selected system, the quaternary UHTC system undoubtedly has significantly better thermomechanical performance when compared to established baseline UHTCs. Furthermore, this raises the debate on the justification for calling a multicomponent system a “high entropy” to be seen in a new light. The developed MC-UHTCs elicits the paradigm of this new class of UHTCs expanding their potential in thermal protection systems for hypersonic applications.

36 MATERIALS SCIENCE↗

Crystallization Mechanism in Spark Plasma Sintered Bulk Metallic Glass Analyzed using Small Angle Neutron Scattering

Understanding the thermal stability of metallic glasses is critical to determining their safe temperatures of service. In this paper, the crystallization mechanism in spark plasma sintered Fe 48 Cr 15 Mo 14 Y 2 C15B6 metallic glass is established by analyzing the crystal size distribution using x-ray diffraction, transmission electron microscopy and in-situ small angle neutron scattering. Isothermal annealing at 700 °C and 725 °C for 100 min resulted in the formation of (Fe,Cr) 23 C 6 crystals, measured from transmission electron micrographs, to be from 10 to 30 nm. The small angle neutron scattering intensity measured in-situ, over a Q-range of 0.02 to 0.3 Å -1 , during isothermal annealing of the sintered samples, confirmed the presence of (Fe,Cr) 23 C 6 crystals. The measured scattering intensity, fitted by the maximum entropy model, over the Q-range of 0.02 to 0.06 Å -1 , revealed that the crystals had radii ranging from 3 to 18 nm. The total volume fraction of crystals were estimated to be 0.13 and 0.22 upon isothermal annealing at 700 °C and 725 °C for 100 min respectively. The mechanism of crystallization in this spark plasma sintered iron based metallic glass was established to be from pre-existing nuclei as confirmed by Avrami exponents of 0.25 ± 0.01 and 0.39 ± 0.01 at the aforesaid temperatures.

42 ENGINEERING↗