NASA NTRS1991

Comparison of dynamic fatigue behavior between SiC whisker-reinforced composite and monolithic silicon nitrides

The dynamic fatigue behavior of 30 vol percent silicon nitride whisker-reinforced composite and monolithic silicon nitrides were determined as a function of temperature from 1100 to 1300 C in ambient air. The fatigue susceptibility parameter, n, decreased from 88.1 to 20.1 for the composite material, and from 50.8 to 40.4 for the monolithic, with increasing temperature from 1100 to 1300 C. A transition in the dynamic fatigue curve occurred for the composite material at a low stressing rate of 2 MPa/min at 1300 C, resulting in a very low value of n equals 5.8. Fractographic analysis showed that glassy phases in the slow crack growth region were more pronounced in the composite compared to the monolithic material, implying that SiC whisker addition promotes the formation of glass rich phases at the grain boundaries, thereby enhancing fatigue. These results indicate that SiC whisker addition to Si3 N4 matrix substantially deteriorates fatigue resistance inherent to the matrix base material for this selected material system.

Choi, Sung R.↗

NASA NTRS1990

Delamination Mechanisms of Thermal and Environmental Barrier Coatings on SiC/SiC Ceramic Matrix Composites

Advanced ceramic thermal barrier coatings will play an increasingly important role in future gas turbine engines because of their ability to effectively protect the engine components and further raise engine temperatures. However, the coating durability issue remains a major concern with the ever-increasing temperature requirements. In this paper, thermal cyclic response and delamination failure modes of a ZrO2-8wt%Y2O3 and mullite/BSAS thermal/environmental barrier coating system on SiC/SiC ceramic matrix composites were investigated using a laser high-heat-flux technique. The coating degradation and delamination processes were monitored in real time by measuring coating apparent conductivity changes during the cyclic tests under realistic engine temperature and stress gradients, utilizing the fact that delamination cracking causes an apparent decrease in the measured thermal conductivity. The ceramic coating crack initiation and propagation driving forces under the cyclic thermal loads, in conjunction with the mechanical testing results, will be discussed.

Zhu, Dongming↗

NASA NTRS1990

Surface Cracking and Interface Reaction Associated Delamination Failure of Thermal and Environmental Barrier

In this paper, surface cracking and interface reactions of a ZrO2-8wt%Y2O3 and mullite/BSAS/Si thermal and environmental barrier coating system on SiC/SiC ceramic matrix composites were characterized after long-term combined laser thermal gradient and furnace cyclic tests in a water vapor containing environment. The surface cracking was analyzed based on the coating thermal gradient sintering behavior and thermal expansion mismatch stress characteristics under the thermal cyclic conditions. The interface reactions that were largely enhanced by the coating surface cracking in the water vapor environment were investigated in detail, and the reaction phases were identified for the coating system after the long-term exposure. The accelerated coating delamination failure was attributed to the increased delamination driving force under the thermal gradient cyclic loading and the reduced interface adhesion due to the detrimental interface reactions. The coating design issues will also be discussed based on the observed failure mechanisms under the high-heat-flux test conditions.

Zhu, Dongming↗

NASA NTRS1990

Mechanical behavior and failure phenomenon of an in situ-toughened silicon nitride

The Weibull modulus, fracture toughness and crack growth resistance of an in-situ toughened, silicon nitride material used to manufacture a turbine combustor were determined from room temperature to 1371 C. The material exhibited an elongated grain structure that resulted in improved fracture toughness, nonlinear crack growth resistance, and good elevated temperature strength. However, low temperature strength was limited by grains of excessive length (30 to 100 microns). These excessively long grains were surrounded by regions rich in sintering additives.

Salem, Jonathan A.↗