Brandon Hearley | Engineering Papers

NASA NTRS2026

Benchmarking Bayesian Optimization Frameworks and Acquisition Strategies for Materials Discovery and Autonomous Laboratories

Bayesian optimization (BO) can accelerate materials discovery by guiding expensive experiments toward the most promising processing conditions. We systematically compare five BO surrogate and framework combinations (Gaussian processes in Ax, Gaussian processes and Monte-Carlo neural networks in BayBE, random forests in Lolopy, and tree-structured Parzen (TPE) estimators in Hyperopt) on three benchmarks that mimic common materials design tasks (a discrete solid-electrolyte composition space, a hybrid discrete/continuous laminate-composite design problem solved with micromechanics modeling, and the continuous Ishigami analytic function which is a standard optimization benchmark). Each BO surrogate is paired with posterior mean, probability of improvement, and expected improvement acquisition functions and run for 100 trials from randomized initial samples with uniform random search providing a control. Across five random seeds per setting, BayBE’s Gaussian-process surrogate with expected improvement consistently reached ≥95 % of the known optimum in the fewest evaluations, while Lolopy’s random forest matched or exceeded GP performance on purely categorical or mixed spaces at a higher computational cost. Posterior mean alone often stagnated at local optima, underscoring the need for exploration, whereas probability and expected improvement balanced exploration and exploitation leading to better optimization in fewer trials. Execution times ranged from milliseconds for TPE to minutes for neural-network and random-forest surrogates. These results establish baseline expectations for BO in automated materials laboratories and highlight expected improvement with Gaussian processes as a reliable first choice, with random forests offering a strong alternative when categorical variables dominate. The benchmark suite and code are released to facilitate future surrogate, acquisition, and constraint-handling research in data-driven materials optimization.

Bayesian optimization↗

NASA NTRSDate not supplied

In-Situ Scanning Electron Microscope Experiments for Microscale Mechanical Testing and Validated Modeling of Fiber Reinforced Thermoplastics

A novel, in-situ, scanning electron microscope (SEM) mechanical testing capability for materials at the microscale which provides experimental validation to a machine learning (ML) toolset for full-field validation of physics-based micromechanics models is being developed by researchers at NASA Glenn Research Center. These are enabling technologies for the integration of multiscale digital twins for materials into system level models which will result in the improved performance, material discovery, reduced production cost and time, rapid characterization, and prognostic structural health monitoring (SHM) for materials and structures for extreme environments in support of NASA space exploration missions. In order to bridge the material structure-to-system gap for digital twins, physics-based models must be experimentally validated at multiple length scales. Seminal microscale experiments, conducted at the Air Force Research Laboratory (AFRL), were limited to transverse compression of single-layer, unidirectional thermoset polymer matrix composite (PMC) micropillar specimens [1]. The early phases of the current project followed those initial results and setup to reproduce the compression testing of PMC material on the custom-built piezoelectric actuated micromechanical testing rig built by MicroTesting Solutions LLC. In this work, samples of thermoplastic PMC material were first machined into 3 mm cubes, and then further machining and final milling was done using a Focused Ion Beam (FIB). The initial experiment was done on a pillar roughly 20 µm x 20 µm x 40 µm tall. Additional pillars were milled with final sizes ranging from 20 µm x 20 µm x 40 µm tall to 40 µm x 40 µm x 65 µm tall. A speckle pattern for in-situ full-field measurements using Digital Image Correlation (DIC) was applied with platinum, which was coated on the surface, and then the FIB was used to mill away some of the coating to produce an irregular pattern of Pt on the pillar surface. The samples were loaded into the custom testing rig and placed into the SEM and loaded under compression until failure. Images were collected in the SEM during testing. Post-processing of the images was conducted using DIC to obtain full-field displacement and strain measurements elucidating the role of the matrix as well as fiber-fiber interaction at the microscale within the composite subjected to compression loading well into the non-linear regime of the material. Moreover, the evolution of fiber-matrix debonding and matrix cracking is observed in-situ at the microscale. This data, along with images segmented with a newly developed ML toolset [2], was used to create and validate physics-based micromechanics models. An image of the failed micropillar is shown in Figure 1. The techniques developed in the initial compression experiment was tailored to the validation needs of the models and expanded to include different sized samples as well as possibly tension and fatigue.

Laura Wilson↗