Summary Abstract: Growth and Alloying of Pd Films on Mo(110) Surfaces

Alloying in small metal particles and in very thin films has recently received considerable attention. In the past it has been generally assumed that alloying is insignificant up to temperatures. Thus many epitaxy experiments of metals on metals with complete miscibility were performed at temperatures between 200 and 400 C and analyzed assuming no alloying. In particular, alloying was not suspected if the film material was not soluble in the substrate. In the present study, which was stimulated by annealing-induced CO adsorption anomalies on thin film surfaces, it has become evident that low temperature alloying can occur in thin films on a metal substrate which is refractory and has very strong interatomic bonds (as evidenced by a high sublimation energy) provided that the substrate is soluble in the film material. A good example of such a film-substrate combination is Pd on Mo. The solubility of Pd in Mo is very at temperatures below 1000 K but Pd can dissolve slightly more than 40 at. % Mo even at low temperatures.

Park, Ch. E.↗
NASA NTRS1983

On some derivatives of phenylethers, 2

Products and the synthesis of chloronitrobenzol with certain phenolates are discussed, as is the p-oxyphenylether occasionally produced. Yield, melting point, and physical description are given for each product. The products include 2,4'-dinitrophenylether; 2,2'-dinitrophenylether; p-nitrophenylether-p-oxybenzoic acid and its methylester; p-aminophenylether-p-oxybenzoic acid, its sulfate, and its barium salt; and p-oxypenylether.

Haeussermann, C.↗
NASA NTRS1981

Silicide surface phases on gold

The crystalline silicide layers formed on (111) and (100) surfaces of Au films on various Si single-crystal substrates are studied by LEED and AES in conjunction with sputter-depth profiling as a function of annealing temperature. On the (111) surface, three basic silicide structures are obtained corresponding to layers of various thicknesses as obtained by different preparation conditions. The (100) surface shows only two different structures. None of the structures is compatible with the various bulk silicide structures deduced from X-ray diffraction. Using LEED as a criterion for the presence or absence of silicide on the surface, smaller layer thicknesses are obtained than reported previously on the basis of AES studies.

Green, A. K.↗
NASA NTRS1978

The co-adsorption of copper and oxygen on a tungsten 100 plane-type surface

The coadsorption of Cu on O2 and a W 100 plane-type surface is studied by Auger electron spectroscopy, thermal desorption, low energy electron diffraction and by work function change measurements. It is shown that the presence of Cu on the surface initially decreases the sticking coefficient of O2. For longer oxygen exposures and for higher adsorption temperatures, the coverage of preadsorbed oxygen reaches values larger than those on the clean surface for the same O2 exposure. Except at the highest values and temperatures of the coverage of preadsorbed oxygen, the sticking coefficient for copper is unity and is independent of the oxygen coverage in the range studied. Coadsorption at room temperatures does not produce any long range order while coadsorption at elevated temperature leads to ordered structures. The saturation coverage of the two dimensional coadsorbate at 800 K is given by a relation. The work function is a complicated function of the coverage of preadsorbed oxygen and the coverage of preadsorbed Cu and is determined predominantly by the temperature at which oxygen is adsorbed. At high temperatures the sequence of adsorption has no influence, in contrast to the room temperature behavior.

Bauer, E.↗
NASA NTRS1977

The adsorption and early stages of condensation of Ag and Au on W single-crystal surfaces

Silver and gold were evaporated up to several monolayers in thickness onto W single-crystal surfaces of the 110 and 100 plane types in the temperature range between 300 and 1300 K. The mode of growth and the structure of the layers were studied by Auger electron spectroscopy and low-energy electron diffraction. The results are compared with thermal desorption spectroscopy data and work-function change measurements. They show certain similarities but also some striking differences between the two systems Ag/W and Au/W as well as a strong crystallographic anisotropy of adsorption and condensation.

Bauer, E.↗
NASA NTRS1976

Adsorption of oxygen on W/100/ - Adsorption kinetics and structure

The adsorption of oxygen on W(100) single-crystal surfaces is studied by Auger electron spectroscopy (AES), flash desorption, low-energy electron diffraction (LEED), and retarding-field work-function measurements. The AES results reveal stepwise changes in the sticking coefficients in the coverage range 0 to 1 and activated adsorption at higher coverages. Upon room-temperature adsorption, a series of complex LEED patterns is observed. In layers adsorbed at 1050 K and cooled to room temperature, the p(2 x 1) structure is the first ordered structure observed. This structure shows a reversible order-disorder transition between 700 and 1000 K and is characterized by a work function which is lower than that of the clean surface. Heating room-temperature adsorbates changes their structure irreversibly. At temperatures below 750 K, some new structures are observed.

Bauer, E.↗
NASA NTRS1976

Formation, structure, and orientation of gold silicide on gold surfaces

The formation of gold silicide on Au films evaporated onto Si(111) surfaces is studied by Auger electron spectroscopy (AES) and low-energy electron diffraction (LEED). Surface condition, film thickness, deposition temperature, annealing temperature, and heating rate during annealing are varied. Several oriented crystalline silicide layers are observed.

Green, A. K.↗
NASA NTRS1975

Thermal desorption of metals from tungsten single crystal surfaces

After a short review of experimental methods used to determine desorption energies and frequencies the assumptions underlying the theoretical analysis of experimental data are discussed. Recent experimental results on the flash desorption of Cu, Ag, and Au from clean, well characterized W (110) and (100) surfaces are presented and analyzed in detail with respect to the coverage dependence. The results obtained clearly reveal the limitations of previous analytical methods and of the experimental technique per se (such as structure and phase changes below and in the temperature region in which desorption occurs).

Bauer, E.↗
NASA NTRS1974

Adsorption and condensation of Cu on W single-crystal surfaces

The adsorption and condensation of Cu up to several monolayers in thickness on tungsten 110 and 100 single-crystal surfaces are studied by combining low-energy electron diffraction, Auger electron spectroscopy, thermal desorption spectroscopy, work-function measurements, and quartz microbalance thickness measurements in one experimental system. The results show drastic differences in the evolution of the structure, work function, and desorption behavior between 110 and 100 surfaces. These differences are understandable in terms of the atomic roughness of the surfaces.

Bauer, E.↗