Anisotropic Structural Collapse of Mg 3 Sb 2 and Mg 3 Bi 2 at High Pressure
Alloys between Mg 3 Sb 2 and Mg 3 Bi 2 have recently been shown to be exceptional thermoelectric materials due in part to their anomalously low thermal conductivity. In the present study, in situ high-pressure synchrotron X-ray diffraction was used to investigate the structure and bonding in Mg 3 Sb 2 and Mg 3 Bi 2 at pressures up to 50 GPa. Our results confirm prior predictions of isotropic in-plane and out-of-plane compressibility but reveal large disparities between the bond strength of the two distinct Mg sites. Using single-crystal diffraction, we show that the octahedral Mg–Sb bonds are significantly more compressible than the tetrahedral Mg–Sb bonds in Mg 3 Sb 2 , which lends support to prior arguments that the weaker octahedral Mg bonds are responsible for the anomalous thermal properties of Mg 3 Sb 2 and Mg 3 Bi 2 . Further, we report the discovery of a displacive and reversible phase transition in both Mg 3 Sb 2 and Mg 3 Bi 2 above 7.8 and 4.0 GPa, respectively. Furthermore, the transition to the high-pressure structure involves a highly anisotropic volume collapse, in which the out-of-plane axis compresses significantly more than the in-plane axes. Single-crystal diffraction at high pressure was used to solve the monoclinic high-pressure structure ( C 2/ m ), which is a distorted variant of the ambient-pressure structure containing four unique Mg coordination environments.