Engineering Papers⌕ Search

SEARCH · Engineering Papers

Results for “single-crystalline LiNi0.8Co0.1Mn0.1O2”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

F and N Rich Solid Electrolyte for Stable All-Solid-State Battery

We report the instability of sulfide solid electrolytes to Li anode and high-voltage LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC811) cathodes limits the cyclic performance of all-solid-state lithium battery (ASSLB). Herein, the stability of Li 6 PS 5 Cl against Li anode is enhanced by mixing a small amount (0.32 wt%) of CuF 2 -LiNO 3 (CL) into Li 6 PS 5 Cl electrolyte layer to in-situ form a mixed-conductive-lithiophobic and self-healing LiF-Li 3 N-Cu solid electrolyte interphase (SEI) at Li 6 PS 5 Cl-CL/Li interface. The critical current density (CCD) of Li 6 PS 5 Cl-CuF 2 -LiNO 3 increases to 1.4 mA cm –2 /1.4 mAh cm –2 at room temperature, which is much higher than that of pristine Li 6 PS 5 Cl (0.4 mA cm –2 /0.4 mAh cm –2 ) even though mixing 0.32 wt% CL into Li 6 PS 5 Cl slightly reduces the ionic conductivity from 2.9 × 10 –3 to 1.5 × 10 –3 S cm –1 . The compatibility of Li 6 PS 5 Cl-CL electrolyte to single-crystalline NMC811 (S-NMC811) is further enhanced by adding a small amount (0.02 wt%) of AlF 3 into Li 6 PS 5 Cl-CL forming Li 6 PS 5 Cl-CuF 2- LiNO 3 -AlF 3 (Li 6 >PS 5 Cl-CLA) as a cathode electrolyte and by doing Cl – on S-NMC811 (Cl@S-NMC811) surface. The Cl@S-NMC811-Li 6 PS 5 Cl-CLA|Li 6 PS 5 Cl-CL|Li cells with areal capacity of 2.55 mAh cm -2 achieve a capacity retention of 69.4% after 100 cycles at 1C (1C = 200 mAh g -1 ). Adding a small amount of SEI and cathode/electrolyte interphase (CEI) former into the sulfide electrolytes with minimal reduction (48.3%) of ionic conductivity is an effective method to enhance the performance of ASSLB.

36 MATERIALS SCIENCE↗

Investigation and Suppression of Oxygen Release by LiNi 0.8 Co 0.1 Mn 0.1 O 2 Cathode under Overcharge Conditions

The safety issue of lithium-ion batteries is a crucial factor limiting their large-scale application. Therefore, it is of practical significance to evaluate the impact of their overcharge behavior because of the severe levels of oxygen release of cathode materials during this process. Here, by combining a variety of in situ techniques of spectroscopy and electron microscopy, this work studies the structural degradation of LiNi 0.8 Co 0.1 Mn 0.1 O 2 (NCM811) accompanying the oxygen release in the overcharge process. It is observed that a small amount of O 2 evolves from the initial surface at ≈4.7V. When charging to a higher voltage (≈5.5V), a large amount of O 2 evolves on the newly formed surface due to the occurrence of microcracks. Based on experimental results and theoretical calculations, it is determined that the oxygen release mainly occurs in the near-surface regions, where the remaining oxygen vacancies accumulate to create voids. To suppress the oxygen release, single-crystalline NCM811 with integrated structure is introduced and serves as a cathode, which can effectively inhibit morphology destruction and reduce the activation of lattice oxygen in the surface region. These findings provide a theoretical basis and effective strategy for improving the safety performance of Ni-rich cathode materials in practical applications.

25 ENERGY STORAGE↗