On High-Fluence Irradiation Hardening of Nine RPV Surveillance Steels in the UCSB ATR-2 Experiment: Implications for Extended-Life Embrittlement Predictions
Nine archival reactor pressure vessel (RPV) surveillance steels from commercial nuclear power plants were irradiated in the University of California, Santa Barbara Advanced Test Reactor 2 (ATR-2) experiment to evaluate irradiation embrittlement under low-flux surveillance capsule versus higher flux test reactor (ATR-2) conditions. The postirradiation measurements of irradiation hardening, measured as increases in yield stress (Δσy), and corresponding conversions of Δσy to Charpy V-notch 41-J transition temperature shifts (ΔTc) are compared with various embrittlement trend curve (ETC) model predictions for the nine steels. Tensile and converted shear punch and microhardness measurements of Δσy generally show a continuing increase between intermediate and high ATR-2 fluences. The Eason-Odette-Nanstad-Yamamoto and ASTM E900 ETC models underpredict embrittlement at the ATR-2 irradiation condition: irradiation temperature (Ti) of 292°C, neutron fluence (ϕt) of 1.4 × 1020 n/cm2 (E > 1 MeV), and neutron flux (ϕ) of 3.68 × 1012 n/cm2-s. On average, the French FIS and Japanese JAEC ETCs slightly overpredict the ATR-2 data. The increase in Δσy with higher fluence is primarily due to Ni-Mn-Si precipitates, which slowly evolve in both nearly copper-free and copper-bearing steels. Finally, a new Odette-Wells-Almirall-Yamamoto embrittlement model is shown that yields good predictions for the nine steels at high fluences (ϕt > 5.5 × 1019 n/cm2).
Nanstad, Randy↗
On High-Fluence Irradiation Hardening of Nine RPV Surveillance Steels in the UCSB ATR-2 Experiment: Implications for Extended-Life Embrittlement Predictions
Nine archival reactor pressure vessel (RPV) surveillance steels from commercial nuclear power plants were irradiated in the University of California, Santa Barbara Advanced Test Reactor 2 (ATR-2) experiment to evaluate irradiation embrittlement under low-flux surveillance capsule versus higher flux test reactor (ATR-2) conditions. The postirradiation measurements of irradiation hardening, measured as increases in yield stress (Δσy), and corresponding conversions of Δσy to Charpy V-notch 41-J transition temperature shifts (ΔTc) are compared with various embrittlement trend curve (ETC) model predictions for the nine steels. Tensile and converted shear punch and microhardness measurements of Δσy generally show a continuing increase between intermediate and high ATR-2 fluences. The Eason-Odette-Nanstad-Yamamoto and ASTM E900 ETC models underpredict embrittlement at the ATR-2 irradiation condition: irradiation temperature (Ti) of 292°C, neutron fluence (ϕt) of 1.4 × 1020 n/cm2 (E > 1 MeV), and neutron flux (ϕ) of 3.68 × 1012 n/cm2-s. On average, the French FIS and Japanese JAEC ETCs slightly overpredict the ATR-2 data. The increase in Δσy with higher fluence is primarily due to Ni-Mn-Si precipitates, which slowly evolve in both nearly copper-free and copper-bearing steels. Finally, a new Odette-Wells-Almirall-Yamamoto embrittlement model is shown that yields good predictions for the nine steels at high fluences (ϕt > 5.5 × 1019 n/cm2).
Nanstad, Randy K.↗