Silicon carbide fiber composite receiver tubes manufactured by PIP process

The performance of SiC fiber composites made by a polymer infiltration and pyrolysis (PIP) process was investigated. Two types of tubular composites were manufactured using Hi-Nicalon and Nicalon-CG silicon carbide fibers infiltrated with SMP10 silicon carbide matrix. The fiber content in both composites was about 25 vol.% with an average density of 2.39 g/cc. The tubular SiC composites showed stable solar absorptance and emittance of 0.97 and 0.91, respectively, at 800 °C. The composites were thermally shocked at 900, 1000, and 1100 °C with a waterjet simulating raindrops. As a result, the hoop tensile strength of the composites revealed no loss of mechanical strength due to the thermal shock experiments up to 1100 °C.

14 SOLAR ENERGY↗

DOE OSTI2020

Processing and properties of SiC composites made via binder jet 3D printing and infiltration and pyrolysis of preceramic polymer

The effect of polymer infiltration and pyrolysis (PIP) cycles with polycarbosiloxane on the microstructure, air leak rate, and properties of SiC composites manufactured by a combination of binder jet 3D printing and PIP are reported. The density, Young’s modulus and flexural strength of disk-shaped components increased with the number of PIP cycles. In the case of density, it increased from 2.05 g/cm 3 in one PIP cycle to 2.33 g/cm 3 after three PIP cycles, while values of flexural strength and Young’s modulus at room temperature after three PIP cycles reached 66.8 ± 2.5 MPa and 69.5 ± 2.8 GPa, respectively. Conversely, the air leak rate was found to decrease with number of PIP cycles, and it reached a value of 4 mbar-liter/s after three cycles. The instantaneous coefficient of thermal expansion of the composite was found to change minimally with the number of PIP cycles and had a value of 4 ± 1.2 ppm/°C between 200°C and 1,000°C. Thermal conductivity was found to increase with number of PIP cycles and to decrease with temperature. For example, after 3 PIP cycles it was found to change from 6.72 ± 0.08 to 6.98 ± 0.08 W/mK at 25°C and 7.36 ± 0.08 to 7.96 ± 0.08 W/mK at 300°C. These values were lower than those of crystalline SiC because of the amorphous nature of the matrix and the presence of pores and cracks.

36 MATERIALS SCIENCE↗

DOE OSTI2022

SolarPACES 2022

Performance of Silicon Carbide Fiber Composite Receiver Tubes for Concentrating Solar Power

14 SOLAR ENERGY↗