DOE OSTI2021

Synthesis of End-Functionalized Poly(norbornenes) and Poly(ethylidene norbornenes) Using a Pd(II) Catalyst in Combination with Chain Transfer Agents

Synthesis of end-functionalized poly(norbornene)s (PNBs) and poly(ethylidenenorbornene)s (PENBs) were prepared using the palladium catalyst t Bu 3 PPdMeCl/NaBAr f in combination with chain transfer agents (CTAs) 4-penten-1-ol and 10-undecenal. These CTAs produce polymers end-capped with -OH and -CHO groups, respectively, in high yields with M n values in the range of 6K to 17K, depending on the molar ratio of the CTA: monomer. End-functionalized PNBs and PENBs with precisely controlled Mn values and very narrow molecular weight distributions were accessed by using 4-penten-1-ol and 10-undecenal as chain-terminating agents following living polymerizations in which monomer is completely consumed. The utility of the aldehyde-functionalized polymers is illustrated via coupling to a dye molecule and by synthesis of ambiphilic diblock copolymers, PNB-b-PEG and PENB-b-PEG.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2026

The Synthesis and Ring-Opening Metathesis Polymerization of Energetic Norbornene Materials

Energetic norbornenes are promising candidates toward the development of new energetic polymers due to the synthetic versatility of norbornene ring-opening metathesis polymerizations used in commercial applications. We report the synthesis of two energetic norbornene materials that can be made in two steps with modest yields, containing either trinitroethanol or fluorodinitroethanol substituents. The norbornene monomers were then polymerized, and the polymers were characterized by Fourier transform infrared spectroscopy (FT-IR), differential scanning calorimetry (DSC), contact angle measurements, and proton and carbon nuclear magnetic resonance spectroscopies ( 1 H and 13 C{ 1 H} NMR). Additionally, small-scale safety data consisting of electrostatic discharge (ESD), friction (FS), and impact (IS) sensitivities were measured for the norbornene monomers and their resulting polymers. These analyses revealed that energetic norbornene materials are relatively insensitive and have densities comparable to that of TNT (1.47–1.81 g·cm –3 ).

36 MATERIALS SCIENCE↗
DOE OSTI2021

Recent Progress of High Performance Thermosets Based on Norbornene Functional Benzoxazine Resins

With the growing demand for high performance polymeric materials in industry, several types of thermosets such as bismaleimides, advanced epoxy resins, cyanate esters, and phenolic resins have been widely investigated to improve the performance of thermosetting products. Among them, benzoxazine resins have received wide attention due to their extraordinarily rich molecular design flexibility, which can customize our needs and adapt increasing requirements. To further improve the properties of polybenzoxiazines, researchers have found that the introduction of a norbornene functional group into the benzoxazine moiety can effectively improve the comprehensive performance of polybenzoxazine thermosets. This article focused on reviewing the recent development of high-performance thermosets based on norbornene functional benzoxazine thermosetting resins.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Effects of a Small Fraction of Norbornene Comonomers on the Frontal Ring Opening Metathesis Polymerization of Dicyclopentadiene and Dihydrofuran

Frontal ring-opening metathesis polymerization (FROMP) is an energy-efficient process for the construction of high performance polydicyclopentadiene (pDCPD) thermosets. A small fraction of norbornene (NBE) comonomer is often added to DCPD to liquify the resin, but their effects on the resin chemistry and frontal curing characteristics are not quantitatively understood, especially for recently developed deconstructable DCPD resins containing cleavable comonomers. 2,3-Dihydrofuran (DHF) is a commercially available, effective cleavable comonomer for ROMP of norbornenes, and it has been recently demonstrated to enable full deconstruction of pDCPD thermosets at 5% loading. Herein, we investigated deconstructable DCPD resins containing 5% of different (oxa)NBE derivatives and 5% DHF. We report the effects of such a small fraction of (oxa)NBE comonomers on the resin pot life (room temperature resin reactivity), front curing characteristics, degree of cure, crosslinking density, comonomer distribution, and deconstruction kinetics of the resulting pDCPD thermosets. These effects can be correlated to the metathesis reactivity of these comonomers. As a result, this study provides quantitative understanding that will guide the future development of new deconstructable FROMP resins with desired construction and deconstruction characteristics.

Luo, Xuyi [Stanford University, CA (United States)↗
DOE OSTI2024

Supersoft Norbornene–Based Thermoplastic Elastomers with High Strength and Upper Service Temperature

With over 6 million tons produced annually, thermoplastic elastomers (TPEs) have become ubiquitous in modern society, due to their unique combination of elasticity, toughness, and reprocessability. Nevertheless, industrial TPEs display a tradeoff between softness and strength, along with low upper service temperatures, typically ≤100 °C. This limits their utility, such as in bio-interfacial applications where supersoft deformation is required in tandem with strength, in addition to applications that require thermal stability (e.g., encapsulation of electronics, seals/joints for aeronautics, protective clothing for firefighting, and biomedical devices that can be subjected to steam sterilization). Thus, combining softness, strength, and high thermal resistance into a single versatile TPE has remained an unmet opportunity. Through de novo design and synthesis of novel norbornene-based ABA triblock copolymers, this gap is filled. Ring-opening metathesis polymerization is employed to prepare TPEs with an unprecedented combination of properties, including skin-like moduli (<100 kPa), strength competitive with commercial TPEs (>5 MPa), and upper service temperatures akin to high-performance plastics (≈260 °C). Here, the materials are elastic, tough, reprocessable, and shelf stable (≥2 months) without incorporation of plasticizer. Structure–property relationships identified herein inform development of next-generation TPEs that are both biologically soft yet thermomechanically durable.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Side Chain Dynamics of Poly(norbornene)- g -Poly(propylene oxide) Bottlebrush Polymers

The segmental dynamics of the side chains of poly(norbornene)- g -poly(propylene oxide) (PNB- g -PPO) bottlebrush polymer in comparison to PPO is studied by quasi-elastic neutron scattering. Having experimental time and length scale information simultaneously allows to extract spatial information in addition to relaxation time. Tethering one end of the PPO side chain onto a stiff PNB backbone slows down the segmental relaxation, over the length and time scales investigated. The power law dependence of the relaxation time on the momentum transfer, Q , indicates a more heterogeneous relaxation pattern for the bottlebrush polymer, whereas the linear PPO has less deviations from a homogenous relaxation. Similar conclusions can be drawn from the time dependent mean square displacement, $\langle$ r 2 ( t )$\rangle$, and the non-Gaussian parameter, α 2 ( t ). Herein, the bottlebrush polymer shows a more restricted dynamics, whereas the linear PPO reaches $\langle$ r 2 ( t )$\rangle$∝ t 0.5 at the highest temperature. The deviations from Gaussian behavior are evident at the α 2 ( t ). Both samples show a decaying α 2 ( t ). Finally, the non-Gaussian parameter supports the results from the power law dependence of the relaxation times, with lower α 2 ( t ) values for PPO compared to those for PNB-g-PPO, pointing to less deviations from Gaussian behavior.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Poly(norbornene) anion conductive membranes: homopolymer, block copolymer and random copolymer properties and performance

It has previously been shown that phase-separated block copolymers with non-ion conducting (hydrophobic) blocks and ion conducting (hydrophilic) blocks can form efficient ion conducting channels with high ionic mobility and conductivity. Block copolymers can provide a means for phase segregation and ion channel formation while homopolymers and random copolymers have been shown to have lower ion mobility. In this study, the properties of poly(norbornene) based anion exchange membranes (AEMs) comprising homopolymers, block copolymers, and random copolymers with high ion-exchange capacity (IEC) (3.48–4.55 meq. g -1 ) have been investigated and compared. The polymers were cross-linked with N,N,N',N'-tetramethyl-1,6-hexanediamine before casting the membranes to avoid excessive water swelling due to high water uptake. It was shown that high ionic conductivity can be achieved in both random copolymers and homopolymers even in the absence of microphase-separated structures. For example, the conductivity of a random copolymer was 194 mS cm -1 at 80 °C, which was comparable to the block copolymer, 201 mS cm -1 at 80 °C. The H 2 /O 2 fuel cell performance of random copolymer composite membranes showed a peak power density of 3.05 W cm -2 and peak current density of 7.85 A cm -2 at 80 °C compared to block copolymer membranes (peak power density of 3.21 W cm -2 and peak current density of 8.27 A cm -2 at 80 °C). It is more critical that high water transport be achieved in AEMs than achieving a phase-segregated morphology. Finally, the homopolymer, block copolymer, and random copolymer membranes showed <1.35% degradation after aging in 1 M NaOH at 80 °C for 1000 h.

08 HYDROGEN↗
DOE OSTI2025

Videos and front speeds of frontal ring-opening metathesis polymerization (FROMP) of DCPD/ENB with norbornene-functionalized PDMS comonomers

This dataset contains videos and front speed measurements for 16 frontal ring-opening metastasis polymerization experiments of dicyclopentadiene (DCPD)/5-ethylidene-2-norbornene (ENB) resins and norbornene-functionalized polydimethylsiloxane (nor-PDMS) comonomers. Each run was carried out in a 10 mm diameter glass test tube and recorded to quantify front propagation behavior. Reported front speeds were extracted by video tracking and reported maximum front temperatures were measured with a thermocouple.

Clarke, Brandon R.↗
DOE OSTI2023

Polynorbornene-based polycations

A statistical, cationic-functionalized norbornene copolymer is formed by a process including performing a vinyl addition polymerization in the presence of a metal catalyst of a first norbornene monomer substituted with a first alkyl group and at least a second norbornene monomer substituted with a second alkyl group, to form an intermediate norbornene copolymer. The second alkyl group includes a substituent which undergoes a substitution reaction with a precursor of a cationic group. The process further includes adding the precursor for the cationic group to the intermediate norbornene copolymer to form the cationic functionalized norbornene copolymer. The cationic group has a volume of 0.25 cm 3 /mol or greater (for example, a phosphonium group or an imidazolium group).

Noonan, Kevin↗
DOE OSTI2022

Poly(ionic liquid)s with Dicationic Pendants as Gas Separation Membranes

Poly(norbornene)s and poly(ionic liquid)s are two different classes of attractive materials, which are known for their structural tunability and thermal stabilities, and have been extensively studied as gas separation membranes. The incorporation of ionic liquids (ILs) into the poly(norbornene) through post-polymerization has resulted in unique materials with synergistic properties. However, direct polymerization of norbornene-containing IL monomers as gas separation membranes are limited. To this end, a series of norbornene-containing imidazolium-based mono- and di-cationic ILs (NBM-mIm and NBM-DILs) with different connectivity and spacer lengths were synthesized and characterized spectroscopically. Subsequently, the poly(NBM-mIm) with bistriflimide [Tf2N−] and poly([NBM-DILs][Tf2N]2) comprising homo-, random-, and block- (co)polymers were synthesized via ring-opening metathesis polymerization using the air-stable Grubbs second-generation catalyst. Block copolymers (BCPs), specifically, [NBM-mIM][Tf2N] and [NBM-ImCnmIm] [Tf2N]2 (n = 4 and 6) were synthesized at two different compositions, which generated high molecular weight polymers with decent solubility relative to homo- and random (co)polymers of [NBM-DILs] [Tf2N]2. The prepared BCPs were efficiently analyzed by a host of analytical tools, including 1H-NMR, GPC, and WAXD. The successfully BCPs were cast into thin membranes ranging from 47 to 125 μm and their gas (CO2, N2, CH4, and H2) permeations were measured at 20 °C using a time-lag apparatus. These membranes displayed modest CO2 permeability in a non-linear fashion with respect to composition and a reverse trend in CO2/N2 permselectivity was observed, as a usual trade-off behavior between permeability and permselectivity.

59 BASIC BIOLOGICAL SCIENCES↗
DOE OSTI2024

Photo-Crosslinkable Naphthalene Diimide Polymer for Solution-Processed n – i – p Perovskite Solar Cells

We copolymerize a norbornene monomer bearing a pendant naphthalene diimide with a norbornene bearing a cinnamate pendant moiety to synthesize a crosslinkable electron-transporting polymer and study its use in solution-processed n–i–p perovskite solar cells. The crosslinked material exhibits over 90% transparency in the visible region and higher thermal stability (>300 °C) and lower surface energy than the corresponding homopolymer of the naphthalene diimide functionalized norbornene. Coating an ITO surface with the photo-crosslinked copolymer yields a slightly lower work function than homopolymer-coated ITO. We show that the morphologies of the perovskite films deposited on both polymers are similar (~300 nm features) based upon scanning electron microscopy. Our solar-cell device results show that the crosslinked naphthalene diimide polymer gives a higher open-circuit voltage (1.08 vs 1.05 V), fill factor (average 64.43 vs 58.77%), and stabilized power conversion efficiency (12.28 vs 10.33%) compared to its non-crosslinked homopolymer counterpart, as well as reduced hysteresis. As a result, we attribute the improved performance to decreased work function, reduced nonradiative recombination, and higher shunt resistance.

14 SOLAR ENERGY↗
DOE OSTI2023

Quaternized Polynorbornene Random Copolymers for Fuel Cell Devices

Quaternized polymers are critical components for various energy devices. Vinyl-addition polynorbornenes provide high mechanical strength, high ion conductivity, and chemical stability in a wide range of pH environments due to the all-C–C bond backbone. In this paper, we present the synthesis of a series of quaternized polynorbornene random copolymers via vinyl addition polymerization and elucidate the impact of polymer composition on their properties. The quaternary ammonium alkyl tether length and the ratio of n-hexylnorbornene to unsubstituted norbornene are systemically tailored. A copolymer of 5-(3-bromopropyl)-2-norbornene and norbornene with pendant trimethylammonium groups achieved hydroxide conductivity of 109 mS/cm at 80 °C with a modest water uptake of 72%. The addition of n-hexylnorbornene to the copolymer, to make a terpolymer, allows for the polymer composition to be tailored for properties, including a decrease in water uptake and higher processability, despite a slightly decreased hydroxide conductivity. Moreover, the developed membranes are chemically robust and highly mechanically stable, enabling thin membranes to be easily fabricated. This study provides insight into important design parameters for quaternized polynorbornenes for a variety of energy storage and conversion devices, especially fuel cells.

25 ENERGY STORAGE↗
DOE OSTI2021

Mechanisms of the Cu(I)-Catalyzed Intermolecular Photocycloaddition Reaction Revealed by Optical and X-ray Transient Absorption Spectroscopies

The [2 + 2] photocycloaddition provides a simple, single-step route to cyclobutane moieties that would otherwise be disfavored or impossible due to ring strain and/or steric interactions. We have used a combination of optical and X-ray transient absorption spectroscopies to elucidate the mechanism of the Cu(I)-catalyzed intermolecular photocycloaddition reaction using norbornene and cyclohexene as model substrates. We find that for norbornene the reaction proceeds through an initial metal-to-ligand charge transfer (MLCT) state that persists for 18 ns before the metal returns to the monovalent oxidation state. The Cu K-edge spectrum continues to evolve until ~5 μs and then remains unchanged for the 50 μs duration of the measurement, reflecting product formation and ligand dissociation. We hypothesize that the MLCT transition and reverse electron transfer serve to sensitize the triplet excited state of one of the norbornene ligands, which then dimerizes with the other to give the product. For the case of cyclohexene, however, we do not observe a charge transfer state following photoexcitation and instead find evidence for an increase in the metal–ligand bond strength that persists for several ns before product formation occurs. This is consistent with a mechanism in which ligand photoisomerization is the initial step, which was first proposed by Salomon and Kochi in 1974 to explain the stereoselectivity of the reaction. Furthermore, our investigation reveals how this photocatalytic reaction may be directed along strikingly disparate trajectories by only very minor changes to the structure of the substrate.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

Ring-opening metathesis polymerization of cobaltocenium derivative to prepare anion exchange membrane with high ionic conductivity

Abstract An efficient method to incorporate a cobaltocenium cation into polymers for anion exchange membranes is described. A cobaltocenium-containing norbornene derivative has been synthesized. It can be homopolymerized, or copolymerized with norbornene, by ring-opening metathesis polymerization (ROMP) with quantitative yields. The composition of the random copolymers can be precisely controlled by adjusting the feed ratio of the monomers. Additionally, the resulting polymers can be cast into thin robust membranes. The morphology of the membranes is characterized by humidity controlled SAXS and TEM, showing disordered interconnected cobaltocenium domains. The high ionic conductivity suggests that such membranes are good candidates for anion exchange membranes.

42 ENGINEERING↗