Results for “fiber-reinforced plastic”

DOE OSTI2022

Laboratory Accelerated Cyclic Corrosion Testing and On-Road Corrosion Testing of AA6××× Coupled to Carbon Fiber-Reinforced Plastics

Structures made from a combination of aluminum alloy (AA) and carbon fiber-reinforced plastic (CFRP) are susceptible to galvanic corrosion of the AA in harsh atmospheric conditions, such as might exist for closure panels in automotive applications. It is important to understand the galvanic corrosion behavior of these materials under laboratory conditions as that might allow prediction of performance in real environments. This work tested specially designed AA6×××-CFRP coupons, including AA6111 and AA6022, connected to CFRP made from two different carbon fiber fabrics (twill and random) with the aim of understanding the corrosion behaviors in a laboratory cyclic exposure chamber and during on-road exposure. The extent of corrosion was assessed by galvanic current measurements, optical profilometry, cross-sectional area analysis, and microscopic analysis. Based on the results, it was determined that the corrosion susceptibilities and morphologies observed in CFRP/AA couples tested in an environmental chamber for 12 weeks were in correspondence with those of the coupons subjected to on-road testing for 1 y in Columbus, OH.

Materials Science↗

DOE OSTI2023

Low-velocity repeated impact behaviors of Polymer Fiber Reinforced Plastics (PFRPs)

Modern fiber-reinforced composites have become ubiquitous across multiple industries due to their excellent weight-to-strength ratio. Typically glass or carbon fibers are widely used. While Glass or Carbon Fiber-Reinforced Plastics (GFPRs or CFPRs) have good stiffness, strength, and fatigue life, they are expensive and difficult to recycle. Researchers are exploring Polymer Fiber-Reinforced Plastics (PFRPs) as an alternative solution. PFRPs utilize polymer fibers and a polymer matrix. A wide range of materials options is available, including low-cost thermoplastics such as polyethylene or polypropylene. These thermoplastics are easy to handle and recyclable without special methods. Manufacturing parts using thermoplastics are well-established as well. However, their mechanical performances have not been extensively studied compared to GFRPs or CFRPs. This study examines the low-velocity impact resistance of PFRPs made of different thermoplastics. The low-velocity impacts are applied through a drop-weight tower. The experiment is divided into two cases: a single perforation impact and low-energy repeated impacts. Energy absorption and the number of impacts to failure are measured. The results are compared to traditional CFRPs which have a thermoset matrix. The PFRPs demonstrate energy absorption capabilities comparable to or greater than those of CFRPs with respect to specimen thickness and density. Additionally, the PFRPs show significantly higher impacts-to-failure than the CFRPs in low-energy repeated impact tests. This is particularly noteworthy considering that the PFRPs are much simpler and more economical to manufacture than CFRPs. To further

Ko, Seunghyun↗

DOE OSTI2023

Low-Velocity Impact Performances of Healed Polymer Fiber Reinforced Plastics

Extending the lifecycle of traditional carbon or glass fiber-reinforced plastics is a complicated problem. The lack of sustainability limits the applications of the traditional composite materials in the vehicle industries where recycling and repurposing are critical issues. Alternatives for the low-stressed structural components are polymer fiber-reinforced plastics (PFRPs). In PFRPs, both the fibers and matrix are composed of thermoplastic polymers (e.g. polypropylene or polyethylene). They are lightweight, easy to manufacture, and cost-effective. Additionally, recycling and repurposing thermoplastic polymers are well understood. Therefore, the PFRPs have strong advantages compared to the traditional fiber-reinforced composites in low-stressed structural applications. In this study, we investigated the low-velocity impact (LVI) performances of the PFRPs and compared them with carbon fiber-reinforced plastics (CFRPs). A semi-spherical impactor was dropped to flat, square panels, and the absorbed impact energy was measured. The damage mechanisms were examined using a Xray µCT scan. The PFRPs outperformed the CFRPs in terms of perforation energy normalized by plate thickness and density. After the perforation, we healed the fractured plates by leveraging the recyclability of the thermoplastic polymers. The healing process of the panels was identical to the initial panel manufacturing process. No additional materials were added during the healing process. The healed PFRP panels were impacted again and substantially recovered energy absorption capability. We also conducted the repeated-impact test with several different impact energies. Unlike the CFRPs where the impact peak load decreased as the impacts repeated, the PFRPs showed an increasing trend. Such a unique mechanism was due to the strain-hardening behavior of the polymer fibers and matrix. As a result, the repeated-impact life of the PFRPs was significantly enhanced. These results are particularly interesting in the automotive or aerospace industries where repeated LVI is frequently observed.

Ko, Seunghyun↗

DOE OSTI2024

Low-velocity impact resistance and failure characteristics of all thermoplastic woven polymer-fiber-reinforced plastic composites

This study addresses the impact performances of recyclable composites made of all thermoplastic polymer-fiber-reinforced plastics (PFRPs), where the reinforcing fibers and matrix are made of thermoplastic polymers. Three woven PFRPs systems were evaluated, including polypropylene fibers, polypropylene matrix, and high-density polyethylene matrix. In low-velocity impact scenario with an impactor speed of less than 6 m/s, our results demonstrate the energy absorption capabilities of the flat laminate PFRPs compared to woven carbon fiber-reinforced plastics (CFRPs) and aluminum alloy 5052. For the systems studied, the PFRPs can reach the specific energy absorption 89% to 115% of the CFRPs. Even compared with the aluminum alloy 5052, the PFRPs can reach up to 97%. We investigate the failure morphologies of the PFRPs using X-ray µCT scans. They reveal the PFRPs’ unique ductile failure morphologies compared to common CFRPs. In addition, we heal the perforated region in the PFRPs by applying the manufacturing process identical to the initial curing process. The healed panels are perforated again, and they recovered 30% to 38% of their original specific energy absorption, a recovery not achievable with CFRPs. This study provides valuable experimental results, and concrete insights into the potential applications of recyclable PFRPs in various engineering fields. It emphasizes their excellent energy-absorbing capability and repairability.

CFRPs↗

DOE OSTI2023

Towards a Circular Economy for PET Bottles in the US

The United States generates the most plastic waste of any country. Along with that GHG emissions from the global plastic economy are expected to increase to 15% of the global carbon budget by 2050. It is imperative that plastic recycling is made a reality to reduce both plastic pollution in the environment and GHG emissions. A portfolio of end-of-life strategies must be implemented to minimize environmental impacts and retain valuable plastic material, but it is challenging to compare options that generate products with different utility and lifetime. Plastic use reduction, reuse and recycling are thus increasingly important, but making informed policy and research decisions within this space can be challenging given the diverse range of available solutions. The novel analysis framework, Plastic Parallel Pathways Platform (4P) has been equipped with consequential life cycle assessment, techno-economic analysis, and a plastic circularity indicator to estimate the greenhouse gas (GHG) emissions, circularity, and cost of polyethylene terephthalate (PET) down-cycling to lower-quality resin, closed-loop recycling to food-grade PET bottles, up-cycling to fiber-reinforced plastic (FRP), and conversion to non-plastic products (electricity, oil) on a United States economy-wide basis. Integrating system dynamics into this robust plastics model that already incorporates techno-economics, circularity, and environmental impacts will enable identification of key bottlenecks between manufacturers, waste sorters, and reclaimers that currently prevent rapid decarbonization of the plastics economy. System dynamics (SD) explore the evolution of activities and technologies based on changed macro parameters such as plastic demand and supply, market shifts, and cross-sectoral interactions. This project particularly aims to explore the interplay between, waste collection, plastic waste sorting, recycling, and manufacturing, as well as the effect of plastic bale quality and plastic reuse initiatives on the surrounding process stages. This functionality will facilitate combinatory analysis in which a portfolio of end-of-life pathways are assessed simultaneously, with the exact makeup of that portfolio affected by parameters such as technology scales, resource constraints, and waste mitigation efforts. Integrating SD with the 4P framework enables analyzing the effect of increased revenue and reinvestment into improving process efficiencies, sorting and collection quantities. Through that, market effects of increased recycled resin availability can be studied for the plastics systems model for the US. The results will help identify technical or economic bottlenecks that currently limit efforts to decarbonize the U.S. plastics economy.

circular economy↗

DOE OSTI2024

Towards a Circular Economy for PET Bottles in the U.S. - 4P Model

The United States generates the most plastic waste of any country. Along with that GHG emissions from the global plastic economy are expected to increase to 15% of the global carbon budget by 2050. It is imperative that plastic recycling is made a reality to reduce both plastic pollution in the environment and GHG emissions. A portfolio of end-of-life strategies must be implemented to minimize environmental impacts and retain valuable plastic material, but it is challenging to compare options that generate products with different utility and lifetime. Plastic use reduction, reuse and recycling are thus increasingly important, but making informed policy and research decisions within this space can be challenging given the diverse range of available solutions. The novel analysis framework, Plastic Parallel Pathways Platform (4P) has been equipped with consequential life cycle assessment, techno-economic analysis, and a plastic circularity indicator to estimate the greenhouse gas (GHG) emissions, circularity, and cost of polyethylene terephthalate (PET) down-cycling to lower-quality resin, closed-loop recycling to food-grade PET bottles, up-cycling to fiber-reinforced plastic (FRP), and conversion to non-plastic products (electricity, oil) on a United States economy-wide basis. Integrating system dynamics into this robust plastics model that already incorporates techno-economics, circularity, and environmental impacts will enable identification of key bottlenecks between manufacturers, waste sorters, and reclaimers that currently prevent rapid decarbonization of the plastics economy. System dynamics (SD) explore the evolution of activities and technologies based on changed macro parameters such as plastic demand and supply, market shifts, and cross-sectoral interactions. This project particularly aims to explore the interplay between, waste collection, plastic waste sorting, recycling, and manufacturing, as well as the effect of plastic bale quality and plastic reuse initiatives on the surrounding process stages. This functionality will facilitate combinatory analysis in which a portfolio of end-of-life pathways are assessed simultaneously, with the exact makeup of that portfolio affected by parameters such as technology scales, resource constraints, and waste mitigation efforts. Integrating SD with the 4P framework enables analyzing the effect of increased revenue and reinvestment into improving process efficiencies, sorting and collection quantities. Through that, market effects of increased recycled resin availability can be studied for the plastics systems model for the US. The results will help identify technical or economic bottlenecks that currently limit efforts to decarbonize the U.S. plastics economy.

carbon↗

DOE OSTI2024

Towards a Circular Economy for PET Bottles in the U.S. - 4P Framework

The United States generates the most plastic waste of any country. Along with that GHG emissions from the global plastic economy are expected to increase to 15% of the global carbon budget by 2050. It is imperative that plastic recycling is made a reality to reduce both plastic pollution in the environment and GHG emissions. A portfolio of end-of-life strategies must be implemented to minimize environmental impacts and retain valuable plastic material, but it is challenging to compare options that generate products with different utility and lifetime. Plastic use reduction, reuse and recycling are thus increasingly important, but making informed policy and research decisions within this space can be challenging given the diverse range of available solutions. The novel analysis framework, Plastic Parallel Pathways Platform (4P) has been equipped with consequential life cycle assessment, techno-economic analysis, and a plastic circularity indicator to estimate the greenhouse gas (GHG) emissions, circularity, and cost of polyethylene terephthalate (PET) down-cycling to lower-quality resin, closed-loop recycling to food-grade PET bottles, up-cycling to fiber-reinforced plastic (FRP), and conversion to non-plastic products (electricity, oil) on a United States economy-wide basis. Integrating system dynamics into this robust plastics model that already incorporates techno-economics, circularity, and environmental impacts will enable identification of key bottlenecks between manufacturers, waste sorters, and reclaimers that currently prevent rapid decarbonization of the plastics economy. System dynamics (SD) explore the evolution of activities and technologies based on changed macro parameters such as plastic demand and supply, market shifts, and cross-sectoral interactions. This project particularly aims to explore the interplay between, waste collection, plastic waste sorting, recycling, and manufacturing, as well as the effect of plastic bale quality and plastic reuse initiatives on the surrounding process stages. This functionality will facilitate combinatory analysis in which a portfolio of end-of-life pathways are assessed simultaneously, with the exact makeup of that portfolio affected by parameters such as technology scales, resource constraints, and waste mitigation efforts. Integrating SD with the 4P framework enables analyzing the effect of increased revenue and reinvestment into improving process efficiencies, sorting and collection quantities. Through that, market effects of increased recycled resin availability can be studied for the plastics systems model for the US. The results will help identify technical or economic bottlenecks that currently limit efforts to decarbonize the U.S. plastics economy.

circular economy↗

DOE OSTI2023

Effect of printing parameters on 3D-printed carbon fiber-reinforced polymer composites under magnetic field control

Magnetic field controlled (MFC) 3D printing is a promising method for realizing the intelligent control of the structural performance of carbon fiber-reinforced plastic (CFRP) composites by adjusting the fiber orientation during the printing process. However, few studies have focused on the influence of the printing parameters on the magnetic control of the fiber direction. Therefore, in this study, the mechanical properties and internal fiber distributions of MFC 3D-printed samples of CFRP composites with 10 wt% fiber content, which were printed at different speeds and layer thicknesses, were investigated. Subsequently, the effects of the fiber content on the mechanical properties and fiber distribution of the MFC 3D-printed samples were studied. Furthermore, the origin of fiber fracture was evaluated through observation and analysis of the fracture section using scanning electron microscopy. The fiber orientation could be well adjusted under the action of a magnetic field and adjustment of printing parameters, thereby improving the tensile strength, young's modulus significantly with slightly decrease of fracture elongation. The recommended parameter combinations (printing speed and layer thickness) were 40 mm/s and 0.2 mm for 10 wt% fiber content CFRP composites.

36 MATERIALS SCIENCE↗

DOE OSTI2022

A new woven composite constitutive model validated by shock wave experiments

In this paper, we present results of plate impact simulations of shock compressed woven glass fiber-reinforced plastic (GRP) performed using the Arbitrary Lagrangian–Eulerian three-dimensional finite element code. A hyperelastic large-strain-based empirical Continuum Damage Mechanics (CDM) formulation is employed to describe damage initiation and growth in the shock-compressed GRP. The model parameters calibration scheme utilizes the Velocity Interferometer System for Any Reflector normal particle velocity measurements at the free surface of the GRP target plates. The impact velocity in the experiments ranged from 8.5 to 418 m/s. The finite element model considered planar 0°/90° bidirectional plies with an individual ply thickness of 0.68 mm, stacked to reach a total laminate thickness of 6.8 mm. The anisotropic elastic strains were estimated from the experimentally determined tetragonal symmetry stiffness matrix for the GRP. The strain-based damage model captures several salient features observed in the measured free surface particle wave profiles, including the shock rise time, onset of Elastic—Elastic Cracking, and the shape of the nonlinear portion of the experimental particle velocity profiles. Furthermore, the CDM model predicts the dominant damage mode to be matrix microcracking due to shear and the associated bulk expansion (bulking) under the global compressive loading in the plate impact configuration.

42 ENGINEERING↗

DOE OSTI2022

Understanding the Elastic, Plastic, and Damage Features in Fracturing of Self-reinforced Thermoplastic Composites via Non-destructive Digital Imaging Correlation

This work demonstrated the utilization of non-destructive Digital Imaging Correlation (DIC) method to characterize the elastic, plastic, and damage features during the Mode I intra-laminar fracturing process of self-reinforced thermoplastic composites by using a self-reinforced polypropylene (PP) composite as an example. The DIC results clearly showed the development of huge plastic zone (PZ) and non-negligible Fracture Process Zone (FPZ) in front of the notch tip during the fracturing process, and the geometries and sizes of the foregoing zones at the peak load were further quantified. Such an interesting fracturing behavior of self-reinforced thermoplastic composites is way different from brittle materials (e.g., glass, acrylic, etc.), ductile materials (e.g., aluminum, steel, etc.), and even quasi-brittle materials (e.g., concrete, nanoparticle-reinforced composites, tough ceramics, wood, cement, carbon/glass fiber-reinforced polymers, etc.). Thus, understanding the elastic, plastic, and damage features is the first step before better characterizing the material fracture properties of self-reinforced thermoplastic composites through new analytical methods and computational modeling. These efforts are of utmost importance for wide applications of self-reinforced thermoplastic composites in various engineering fields in the future.

Lightweight Composites, Self-reinforced Thermoplas↗

DOE OSTI2025

Upcycling of post-consumer mixed polyolefin feedstock: An economic and technical evaluation

Here, this study reports techno-economic and life cycle analyses to evaluate the economic and environmental impacts of mechanically recycled PE/PP blends in the presence of rheology modifiers. Additionally, fiber-reinforced composites derived from the compatibilized blends were prepared and evaluated for their performance compared with virgin plastics. Results suggest that compatibilized PE/PP blends exhibit a 70% lower selling price compared to virgin PE. Furthermore, these blends achieved a 74% reduction in greenhouse gas emissions or climate change impact compared to the virgin counterpart. Fiber-reinforced composites from compatibilized PE/PP blends demonstrated improved or comparable mechanical properties relative to composites made from virgin PE/PP blends. Based on their favorable cost and environmental impact, along with performance comparable to virgin composites, compatibilized PP/PE composites made from post-consumer plastics can find applications in large-scale composite manufacturing.

Fiber reinforced plastics (FRP)↗

DOE OSTI2022

Long fiber injection molding

An improved method for obtaining high fiber volume fraction, long fiber injection molded articles is provided. According to one embodiment, the method includes forming an injection molding feedstock by cutting pre-impregnated fiber-reinforced tape into platelets. The platelets can be coated with a thin layer of polymer to allow sliding of the platelets with respect to each other at the early stages of plastication, rather than forcing relative motion of fibers with respect to each other. The method can further include the dispersion of material only in the final stages of the injection molding screw to promote gentle motion of the feedstock at the earlier stages of the plastication process. The method allows improvement of mechanical properties of articles manufactured with equipment and techniques that are prevalent in high volume automotive and consumer industries.

Kunc, Vlastimil↗

DOE OSTI2021

Closing the Loop on Automotive Carbon Fiber Prepreg Manufacturing Scrap

The project demonstrated how to “close the loop” on carbon fiber by integrating industrial carbon fiber scrap into new functional components in an automotive lightweighting application. The project serves as a validation of discontinuous recycled carbon fiber in a commercial context, while generating comprehensive material data throughout the production chain. To this end, the project exhibited increasing complexity as material evaluation progressed from benchtop to commercial scale through full-scale part production, with key material properties thoroughly characterized throughout the process. Of particular focus was the form of the fiber that was fed into compounding, as recycled fiber has historically been problematic to feed at commercial-scale. Carbon fiber is energy-intensive to manufacture, so reuse of existing fiber material can reduce costs and increase sustainability. Additionally, by integrating recovered short fiber into a thermoplastic, regrind processes can be used to provide feedstock for later generations of product. While regrind plastics are not “infinitely recyclable”, reusing the manufacturing scrap over several generations of products can greatly increase material sustainability and lower the fractional embodied energy of each successive product. As such, this project supports the IACMI technical goals of (1) 25% lower carbon fiber-reinforced polymer (CFRP) cost, (2) 50% reduction in CFRP embodied energy, and (3) 80% composite recyclability into useful products. The initial stage of the project involved down selecting surface treatment (sizing) chemistries. Sizing evaluations were performed on Vartega’s chemically recycled intermediate modulus fiber along with standard modulus dry scrap which was oversized with sizing provided by Michelman. More dramatic improvements from sizing were found on the standard rather than the intermediate modulus fibers. The strength of the chemically recycled individual fibers were evaluated by Michelman and ORNL through single fiber testing and found to be comparable to similarly evaluated virgin fibers. UDRI’s mechanical testing on injection molded test specimens identified similar mechanical properties and fiber distribution relative to benchmark specimens. Additional surface chemistry tests and visualizations were performed by the Colorado School of Mines to confirm close conformance between the benchmark and recycled-fiber specimens. As the mechanical test results exceeded the 80% threshold established as the go/no-go(GNG), the project scale was increased to use commercial-scale equipment that would both better characterize the manufacturing utility of the target product format and allow qualitative assessment of a complex commercial part. An upscaled compounding evaluation was performed with a 27 mm twin-screw compounding extruding using oversized standard modulus fibers that were formatted to improve bulk solids transfer. The project team anticipated that milestone mechanical benchmarks could be achieved given the favorable performance of the sized standard modulus material identified in the initial micro-compounding trials. While the mechanical performance did meet the milestone target for that phase of the project, mechanical properties for this standard modulus-based compound were still less than those of the Ford specification. To compare the performance, the project team oversized intermediate modulus dry fibers and compounded them with the project resin at BASF using a 40 mm compounder. Test specimen mechanical performance exceeded the targets laid out in both the project milestone and the Ford specification. A series of prototype parts were successfully molded, albeit with instances of short shot components due to the high thermal conductivity of the carbon fiber compared to glass fiber for which the prototype tool was designed for. The project demonstrated that recycled carbon fiber is a viable option in fiber reinforced compound, providing greatly increased strength and modulus for applications that require them. The “agglomerated” format that facilitated effective bulk solids transfer of recovered fiber showed promise for industrial application.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Hygrothermal Aging and Thermomechanical Characterization of As-Manufactured Tidal Turbine Blade Composites

This study investigates the hygrothermal aging behavior and thermomechanical properties of as-manufactured glass fiber-reinforced epoxy and thermoplastic composite tidal turbine blades. The blades were previously deployed in a marine environment and subsequently analyzed through a comprehensive suite of material characterization techniques, including hygrothermal aging, dynamic mechanical analysis (DMA), tensile testing and X-ray computed tomography (XCT). Hygrothermal aging experiments revealed that while thermoplastic composites exhibited lower overall water absorption (0.78% vs. 0.47%), they had significantly higher diffusion coefficients than epoxy (2.1 vs. 12.1 × 10 −13 m 2 s −1 ), suggesting faster saturation in operational environments. DMA results demonstrated that water ingress caused plasticization in epoxy matrices, reducing the glass transition temperature and increasing damping (112 °C to 104 °C), while thermoplastic composites showed more stable thermal behavior (87 °C glass transition temperature). Tensile testing revealed substantial reductions in ultimate strength (>40%) for both materials after prolonged water exposure, with minimal change in elastic modulus, highlighting the role of matrix degradation over fiber reinforcement. XCT image analysis showed that both composites were manufactured with high quality: no large voids or cracks were present, and the degree of misalignment was low. These findings inform future marine renewable energy composite designs by emphasizing the critical influence of moisture on long-term structural integrity and the need for optimized material systems in harsh marine environments. This work provides a rare real-world comparison of epoxy and recyclable thermoplastic tidal turbine blades, showing how laboratory aging tests and advanced imaging reveal the influence of material and manufacturing choices on long-term marine durability.

16 TIDAL AND WAVE POWER↗

DOE OSTI2022

Microstructural and nanomechanical studies of PVD Cr coatings on SiC for LWR fuel cladding applications

The microstructure and nanomechanical properties of pure Cr coatings deposited on SiC with various physical vapor deposition (PVD) methods have been investigated for the mitigation of hydrothermal corrosion of SiC-SiC f (SiC fiber-reinforced SiC matrix) composite fuel cladding in light water reactors (LWR). Cr coatings (4–7 μm thick) were deposited on unbiased SiC substrates using six variants of magnetron sputtering processes: (i) standard (S-DCMS), (ii) pulsed (P-DCMS), (iii) ion-assisted (I-DCMS), and (iv) pulsed ion-assisted direct current magnetron sputtering (PI-DCMS), (v) high-power impulse magnetron sputtering (HiPIMS), and (vi) bipolar HiPIMS (B-HiPIMS). Microstructural characterization and nanoindentation testing were used to evaluate effects of deposition technique on coating microstructure and nanomechanical properties. The application of positive reverse pulses to the sputter target induced coarsening of the columnar grain structure, while ion bombardment of substrates during deposition promoted densification of the coating microstructure. Both effects are exemplified in B-HiPIMS deposition, resulting in a high-density microstructure with compressive residual stress. Material pile-up around nano-indents and plastic work during nanoindentation were analyzed to understand deformation behavior of the coatings. Finally, the results suggest the B-HiPIMS process to be among the promising methods for the deposition of Cr coatings on SiC-SiC f for LWR cladding application.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Recyclable CFRPs with extremely high T g : hydrothermal recyclability in pure water and upcycling of the recyclates for new composite preparation

In recent years researchers have introduced different malleable and/or degradable thermosetting polymers to address the recyclability of traditional thermoset materials. Nonetheless, the mechanical properties and glass transition temperature (T g ) of these polymers are often compromised to achieve the desired depolymerization rate. In this work, a hydrothermally recyclable epoxy/anhydride thermosetting system with superior mechanical performance and high T g (>200 °C) was developed for carbon fiber reinforced plastic (CFRP) applications, using triethanolamine as the co-curing agent and tetraglycidyl methylenedianiline (TGDDM) as the epoxy matrix. The hydrothermal recycling of such cured systems is achieved at relatively low temperature (200 °C) without the addition of a catalyst. This mild recycling process decomposes the recyclable polymer matrix into an oligomer and imparts little damage to the valuable carbon fiber. The recycled carbon fiber and the decomposed polymer resin are reused to prepare a new CFRP. Here, this study has introduced a simple and practical approach for the preparation of recyclable CFRPs with high T g and a pathway for highly efficient closed-loop recycling, which sets up a framework for the future design of sustainable polymer composites.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2025

Upcycling of CFRP Waste: Viable Eco-friendly Chemical Recycling and Manufacturing of Novel Repairable and Recyclable Composites

The rapid growth of the carbon fiber-reinforced polymer (CFRP) composite market has driven researchers to find value-added applications for outdated prepregs, manufacturing scraps, and end-of-life components. Currently, most CFRP waste is incinerated or landfilled, which squanders its residual value and burdens the environment. Various mechanical, thermal, and chemical approaches have been attempted to recover the carbon fiber, polymer matrix, or both. However, these current practices are often costly, energy-intensive, and generate secondary waste and pollution. To address these shortcomings, this project aims to develop a viable and sustainable chemical recycling technology for CFRP waste that can efficiently and cost-effectively decompose the polymer matrix and manufacture new recyclable composites from both the recovered carbon fiber (rCF) and decomposed matrix polymer (DMP).

36 MATERIALS SCIENCE↗

DOE OSTI2022

Mechanical Properties of High-Temperature Fiber-Reinforced Thermoset Composites with Plain Weave and Unidirectional Carbon Fiber Fillers

Fiber-reinforced thermoset composites are a class of materials that address the arising needs from the aerospace and hypersonic industries for high specific strength, temperature-resistant structural materials. Among the high-temperature resistant thermoset categories, phenolic triazine (PT) cyanate esters stand out thanks to their inherent high degradation temperature, glass transition temperature, and mechanical strength. Despite the outstanding properties of these thermosets, the performance of carbon fiber composites using PT cyanate esters as matrices has not been thoroughly characterized. This work evaluated PT and carbon fiber composites’ compressive properties and failure mechanisms with different fiber arrangements. A PT resin with both plain weave (PW) and non-crimped unidirectional (UD) carbon fiber mats was analyzed in this research. Highly loaded thermoset composites were obtained using process temperatures not exceeding 260 °C, and the composites proved to retain compressive strength at temperatures beyond 300 °C. Compressive testing revealed that PT composites retained compressive strength values of 50.4% of room temperature for UD composites and 61.4% for PW composites. Post-compressive failure observations of the gage section revealed that the mechanisms for failure evolved with temperature from brittle, delamination-dominant failure to shear-like failure promoted by the plastic failure of the matrix. This study demonstrated that PT composites are a good candidate for structural applications in harsh environments.

Hall, Samuel Ernesto↗