Deformation band corrosion as a result of applied stress and cold-work in 304 stainless steel in simulated pressurized water reactor primary water conditions

Stainless steels like 304SS are commonly used in pressurized water reactor primary water environments due to their excellent resistance to stress corrosion cracking (SCC). However, SCC susceptibility has been observed in cold-worked 304SS. Cold-rolling introduces a high density of defects, such as deformation bands or dislocations, into the microstructure; applied stress, even if macroscopically below the yield stress, can result in regions with high localized stresses. Cold-worked and non-cold-worked samples were exposed to 360 °C simulated PWR primary water for 1500 h with and without active loading. Corrosion susceptibility of dislocations and deformation bands induced by cold-rolling and/or applied stress was studied using high-resolution (analytical) transmission electron microscopy. Deformation bands were generated in all specimens examined in the study. Penetrative oxidation was observed in some deformation bands in each specimen. The depth of penetrative deformation band oxidation frequently exceeded the depth of grain boundary oxidation in all specimens. However, deformation band oxides generally were narrowly confined to the deformation band plane. Highly Ni-rich regions were observed beyond all oxidation fronts. Surface oxides were thicker in the specimens exposed under active loading. In conclusion, the implications of these findings at surfaces for deformation bands intersecting stress corrosion crack paths are discussed.

EFTEM↗

DOE OSTI2024

Electric field enhanced diffusion welding of alloy 617: Microstructural characteristics and mechanical properties

This study investigated the microstructural characteristics and mechanical behavior of diffusion welded nickel-based Alloy 617 obtained by electric field-assisted sintering (EFAS) using various parameters. The interfacial microstructure exhibited different characteristics including good grain boundary (GB) migration across the interface in the samples diffusion-welded at 1100 °C and a flat interface in the samples joined at 1000 °C and 1050 °C. The interface consisted of fine Al 2 O 3 oxides, while precipitation of interfacial M 23 C 6 carbides was not observed. Grain boundaries migrated across the Al 2 O 3 oxides, leaving these oxides within the grains. Graded grain size was observed, with grain coarsening being more significant near the sample surface due to the temperature gradient induced by EFAS. Tensile testing revealed that the specimens fractured in the matrix away from the interface, indicting strong diffusion-welded joints. Further, the peak tensile strength of 807 MPa was obtained in the samples welded at 1000 °C due to minimal grain growth. The materials obtained at 1100 °C exhibited reduced tensile strength but improved ductility. Strain maps revealed by digital image correlation showed alternating high and low strain segments in the samples produced at 1000 °C and 1050 °C, indicating that the flat interfaces with no GB migration were less ductile compared to the matrix. A greater strain uniformity was observed along the bond interfaces with improved GB migration. The hardness reduced near the sample surfaces due to enlarged grains induced by temperature gradient. This study demonstrates that GB migration and enhanced mechanical strength can be achieved in diffusion-welded Alloy 617.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Microstructural Characteristics, Mechanical Properties, and Corrosion Behavior of Field-Assisted Diffusion Welded Alloy 617

This study investigated the microstructural characteristics, mechanical response, and corrosion resistance of Alloy 617 diffusion welded by electric field-assisted sintering (EFAS). The microstructure exhibited good grain boundary (GB) migration across the interface and flat interface in the samples bonded at different conditions. Graded grain size was observed, with grain coarsening being more significant near sample surface due to EFAS-induced temperature gradient. Tensile testing revealed that the specimens fractured in the matrix away from the interface. The peak strength of 807 MPa was obtained in the samples welded at 1000°C. The materials obtained at 1100°C exhibited reduced tensile strength but improved ductility. Strain maps revealed by digital image correlation showed the flat interfaces were less ductile compared to the matrix. The hardness reduced near sample surfaces due to enlarged grains induced by temperature gradient. The interfaces with GB migration exhibited improved corrosion resistance in molten salt compared to the flat interfaces.

36 - MATERIALS SCIENCE↗

DOE OSTI2025

Effect of microstructure and neutron irradiation defects on deuterium retention in SiC

Retention of hydrogen isotopes is a critical concern for operating fusion reactors as retained tritium both activates components and removes scarce fuel from the fuel cycle. Radiation-induced displacement damage in SiC influences the retention of hydrogen isotopes compared to pristine SiC. Deuterium retention in neutron irradiated high purity SiC has been compared to different microstructures of non-irradiated high purity SiC using thermal desorption spectroscopy after gas charging and low energy ion implantation. Experimental results show lower deuterium retention in single crystal SiC than in polycrystal SiC indicating that grain boundaries are key trapping features in unirradiated SiC. Deuterium is released at lower temperatures in neutron irradiated polycrystal SiC compared to pristine polycrystal SiC, suggesting weaker trapping by radiation-induced defects compared to grain boundary trapping sites in the pristine materials. Low energy ion implantation caused a high deuterium release temperature, highlighting the sensitivity of deuterium release behaviour to radiation defect characteristics. First principles calculations have been conducted to identify energetically favourable trapping sites in SiC at the H ABc V Si and H TSi V C complexes, and migration barriers between interstitial sites. This helps interpret experimental results and derive effective diffusivity of hydrogen isotopes in SiC in the presence of vacancies.

36 MATERIALS SCIENCE↗

DOE OSTI2026

Understanding Fundamental Mechanisms Behind Anomalous Segregation Behavior at Grain Boundaries during Diffusional Creep

Recent experimental studies in a nickel (Ni)-rhenium (Re) alloy demonstrated anisotropic elemental segregation around grain boundaries (GBs) while under tensile strain. Some GBs showed Re enrichment, while others showed Re depletion. We hypothesize that differing vacancy fluxes to GBs, caused by the anisotropic elastic stresses generated within the polycrystal, results in anisotropic creep-induced segregation (CIS) and grain growth. Using molecular dynamics simulations, we developed a mechanistic understanding of CIS and determined the contribution of elastic stresses and grain growth in Ni-Re alloys. We find that the stress state of the GB significantly changes the segregation energy profile for Re atoms, leading to significant Re redistribution. Further, as the GB migrates, the segregation/desegregation tendency of Re leads to bands of Re enrichment/depletion. Our results have important consequences for the quantitative predictions of diffusion creep and for the design of high-temperature creep-resistant Ni alloys.