Spray-Coated Silver as Backside Metal for III–V Photovoltaic Devices on GaAs and Ge Substrates

The accelerated increase in demand for III-V space photovoltaics on GaAs and Ge substrates, as well as growing interests in terrestrial applications, motivate the development of cost-effective, high-throughput processing routes of these materials. Here, in this study, we assess spray-coated silver (Ag) back contact metallization as a substitute for electron-beam-evaporated metals currently used in industry. We find that the spray-coated Ag films are dense and continuous. By means of quantum efficiency, dark current-voltage, and illuminated current-voltage characterizations, we show that spray-coated GaAs and Ge solar cells perform similarly to baseline devices with electroplated Au, including under high current densities. We estimate that the thresholds for specific contact resistance below which back contacts do not significantly contribute to resistive loss are 2.1 x 10 -1 Ω•cm 2 for GaAs and 4.7 x 10 -2 Ω•cm 2 for Ge. We experimentally confirm that our spray-coated samples meet these requirements. Peel tests show that the adhesion of plain spray-coated Ag films to the back of p-type Ge substrates used in III-V solar cells is currently insufficient, whereas adhesion to p-type GaAs substrates is outstanding and requires no further optimization.

14 SOLAR ENERGY↗

DOE OSTI2025

Selenium Migration and Local Structures in Cu‐Doped CdSeTe Solar Cells after Aging

Selenium grading plays a critical role in state-of-the-art Cadmium Telluride photovoltaic cells by enhancing long-wavelength absorption and extending minority carrier lifetimes —key to enabling the current performance record of 23.08%. However, very little is understood about selenium motion. In this study, a comprehensive, multimodal, and multiscale approach is employed to investigate Se migration and local structural changes in copper (Cu)-doped CdSeTe solar cells subjected to accelerated stress. X-ray fluorescence (XRF) microscopy shows unexpected levels of Se diffusion after 500 h under heat (75°C) and light (0.8 suns, 80 mW/cm 2 ), suggesting the coexistence of fast and slow diffusion channels even at low temperatures, with unexpectedly low activation energies (<0.85 eV). X-ray Absorption Near Edge Structure (XANES) analysis indicates a preferential migration of Se atoms to anionic lattice sites and a reduction in Se-Cl co-passivation at Te-terminated dislocation cores. Furthermore, these findings point to a reconfiguration of Se local environments and highlight the potential role of extended structural defects in enabling Se transport at low temperatures. Additionally, XANES results suggest that the presence of metallic Cu across the absorber layer may contribute to back-contact degradation and reduced hole density in both fresh and aged devices.

14 SOLAR ENERGY↗

DOE OSTI2026

Front-Surface Potential of Platinized p -InP Photocathodes Probed by Dual-Working-Electrode Measurements

The front-surface potential (E fr ) of p-InP/Pt photocathodes performing the hydrogen-evolution reaction has been probed under operating conditions using a dual-workingelectrode (DWE) method. The DWE data are consistent with expectations for proposed stability mechanisms for p-InP photocathodes. Specifically, E fr for Pt-modified p-InP adopts a value near the reversible hydrogen electrode (RHE) potential, consistent with kinetic suppression of metallic In 0 formation. The data provide a rapid, operando metric of interfacial catalyst activity, and indicate that E fr for the p-InP/Pt junction is governed by surface catalytic kinetics rather than by the applied back-contact potential (E b ).

Catalysts↗

DOE OSTI2026

Gold-Induced Chemical Perturbations in CdTe-Based Photovoltaic Cells

Back-contacting p-type CdTe has been identified as one of the major areas of loss in CdTe photovoltaic (PV) power conversion efficiency (PCE). In research settings, Au is a common contact material due to its ease of use and decent performance. This work provides a detailed investigation into using gold for back contacting As-doped, CdCl 2 -treated, polycrystalline CdTe that has been exposed to air after absorber processing, another routine practice. First, X-ray photoemission spectroscopy (XPS) is used to determine the native oxide to be 1.6 nm of CdTeO 3 by using a combination of angle-resolved XPS and the cadmium-modified Auger parameter. During gold metallization of CdTe, oxygen and oxidized tellurium are eliminated from the thin CdTeO 3 native oxide. The fates of the released oxygen and possibly cadmium and tellurium are not known, but these reaction byproducts can enter the absorber bulk or grain boundaries, stay at the interface, or dissolve in the Au. Interfacial hole barriers between CdTe and Au are measured for samples with and without the native oxide present prior to metallization. Results show that the thin CdTeO 3 alleviates the downward band bending by 40 meV from 470 to 430 meV even though it is consumed during interface formation. The implications of these chemical reactions on the device are assessed through photoluminescence (PL) spectroscopy, which shows losses in internal open circuit voltage (iVoc) from 820 to 795 meV, carrier lifetime from 123 to 45 ns, and PL quantum yield from 2.9 × 10 −5 to 1.2 × 10 −5 . Modeling timeresolved PL lifetimes demonstrates the back surface recombination velocity due to metallization reduces minority carrier lifetimes. These results identify the native oxide and show that it plays an important role in mediating downward band bending along with how the back interface reaction can negatively impact device-scale parameters and reduce PV PCE.

14 SOLAR ENERGY↗