Time at Temperature Experiments on Neutron Irradiated Zircaloy-2 using Conventional & Flash DSC
Dryout events in Boiling Water Reactors (BWRs) are currently treated by NRC regulations as automatic disqualification for continued fuel rod operation, even though this criterion does not account for the rate or duration of power increases, associated changes in material behavior, or the possibility of rewetting. Operational history from Anticipated Operational Occurrences (AOOs) shows that short, transient power excursions often demand only modest heat removal, and industry experience suggests that fuel can briefly enter dryout yet return to safe, stable operation. The lack of detailed understanding of the material response during such events motivates the present series of experiments. This study uses unique and innovative methods to investigate microstructural evolution in irradiated Zircaloy-2 exposed to high temperatures in inert environments. Differential Scanning Calorimetry (DSC) and FlashDSC are combined to build a comprehensive experimental framework capable of identifying the a–ß phase transformation in zirconium and examining defect annealing under steep thermal gradients. FlashDSC enables rapid heating and cooling of Focused Ion Beam (FIB)–prepared large-area lift-outs (LALOs) of irradiated Zircaloy-2 at rates of 1,000 K/s to peak temperatures of 600°C, 750°C, and 900°C. The goal is to determine whether these conditions produce measurable microstructural changes that could influence cladding performance in typical BWR environments. Microstructural characterization includes quantifying dislocation density and assessing secondary phase particle (SPP) size and distribution using Transmission Electron Microscopy (TEM). Ongoing analysis, such as diffraction pattern indexing and 4D STEM processing, will further refine these observations.