Spatio-temporal mapping of species in a femtosecond laser induced Zircaloy-4 plasma identified conditions well-suited for the detection and analysis of deuterium across a wide range of concentrations.
This work evaluates deformation activity in textured zircaloy-4 cladding with the aim of elucidating the mechanisms that govern mechanical behavior across a temperature range anticipated in reactor service. In particular, the dependence of mechanical anisotropy on temperature and stress state (ratio of applied stresses) is examined via uniaxial and biaxial tensile experiments at room temperature and 400 °C. The mechanical behavior was interpreted based on micro-texture and dominant slip system activity. Thermal activation of basal systems is found as a key mechanism affecting mechanical behavior across the temperature range. The biaxial stress states produce resolved shear stresses contrasting to uniaxial stress states. As a result, mechanical testing and implications for reactor pellet-cladding mechanical interaction stress conditions are discussed.
Not provided.
Thermal diffusivity measurements on Zirconium-based cladding materials have historically been a challenge due to the difficulty to measure on specimens with curved geometries, including nuclear grade Zircaloy cladding materials. Here, in this work, we first used laser flash analysis method and four-probe configuration method to measure the thermal diffusivity and electrical resistivity of Zircaloy tubes respectively, which show good agreement with Zircaloy plates in this work, as well as previously published data. The consistent results proved the applicability of the laser flash analysis setup and four-probe configuration method for investigating thermal diffusivity and electrical resistivity of Zircaloy tubes. We further investigated the hydrogen effect on thermal diffusivity and electrical resistivity of Zircaloy. Hydrogen plays significant roles in the thermal diffusivity of Zircaloy, which depends on the hydrogen concentration. For higher hydrogen contents (1130 and 1820 wppm in this work), where phase transformation (α-Zr + δ-hydride → α-Zr + β-Zr) occurs at 567 °C, thermal diffusivity decreases as a function of temperature at the α-Zr + δ-hydride phase regime, while increase at higher temperature at the α-Zr + β-Zr phase regime. For low hydrogen concentration, where hydride dissolved into α-Zr matrix phase at higher temperature, the thermal diffusivity is lower than non-hydrided Zircaloy-4 with similar temperature-dependent trends. Such observation demonstrates the hydrogen effects on reducing thermal diffusivity of α-Zr phase. Hydrogen increases the electrical resistivity of Zircaloy. Similar to thermal diffusivity results, the phase transformation causes a reversal of temperature-dependent trends in electrical resistivity results in Zircaloy-4 with higher hydrogen contents.
Using an instrumented autoclave operating at 288°C and 1100 psi, electrical impedance spectroscopy (EIS) measurements were taken from three neutron irradiated fuel channel samples (Zircaloy-2 and Zircaloy-4). The three high priority fuel channel samples were tested at 288°C using a simulated PWR water with the AC frequency range extending down through 10 -4 Hz, with corresponding DC measurements to validate the resistance measurements. EIS measurements were also taken at room temperature using a simulated PWR water from four neutron irradiated fuel channel samples (Zircaloy-2 and Zircaloy-4). and four water rod samples (Zircaloy-2). EIS measurements were also performed on unirradiated Zircaloy-2 tubes that were previously oxidized in autoclaves at various temperatures for different time durations to obtain oxide layers of different thicknesses. These experiments proved to be more challenging than anticipated because of the small size of the samples, which required development of fixtures to allow valid testing of the materials, some of which are radioactive, under pressure and temperature. Equivalent circuits were used to model the data. Some samples resulted in Nyquist plots where the arcs were too close to each other resulting in the inability to separate the different oxide morphological thicknesses. Microstructural characterization in the form of optical microscopy, scanning electron microscopy and (scanning) transmission electron microscopy was performed to document the microstructural features of the oxidized Zr-2 and Zr-4 samples (oxide and metal/oxide interface) and to interpret the EIS results. At the start of this work, it was assumed that despite the laminar cracks and porosity visible in both optical and SEM, the oxide scale is dense near the metal, effectively preventing the water from contacting the metal directly. While it is generally accepted that the large laminar cracks pores allow the water to percolate into the oxide film, it is unknown just how deep it can go, and how interconnected is the porosity, which will dictate how much the porosity is connected electrically to the water within the oxide scale. The EIS results demonstrated that there is in fact a distribution of oxide thicknesses over the various samples, and within each material condition, that are communicating to the liquid. This is derived from the fact that Nyquist plots have an arc radius whose center point is often below the Z’ axis, implying that instead of a single oxide thickness, these oxides have a distribution of thicknesses. This distribution of thicknesses produces arcs that are not clearly separable in most of the samples.
The effects of interfacial contact between 316 stainless steel (316 SS) waste canister and spent fuel cladding material (Zircaloy-4) in case of water intrusion into a deep geological repository are investigated. Hydrothermal corrosion experiments of 316 SS and Zircaloy-4 in direct contact were performed at elevated temperatures in MilliQ water and simulated Mont Terri groundwater. Hematite, magnetite, chromite, and baddeleyite form as secondary phases. pH of the Mont Terri solution increases with corrosion duration and magnetite forms preferentially instead of hematite. Thermodynamic modeling shows that iron oxidation in 316 SS controls the pH and redox potential of the aqueous environment and is in good agreement with experimental Mont Terri results, showing that experimental Mont Terri results trend to equilibrium. All oxides except hematite are predicted to exist at thermodynamic equilibrium based on calculations, implying that experimentally formed hematite will be reduced or transformed to magnetite at equilibrium. The thermodynamically predicted chromite was observed to form only at the interface where 316 SS was in contact with Zircaloy-4 at 250°C, showing that contact with Zircaloy-4 seems to accelerate the 316 SS corrosion to thermodynamic equilibrium. Finally, Mont Terri groundwater readily trends towards thermodynamic equilibrium, leading to a pH and redox buffered system that is dominated by iron in solution coming from the accelerated corrosion of 316 SS caused by Zircaloy-4 contact.
In this paper, accident-tolerant fuel (ATF) cladding materials aim to improve fuel reliability and safety during accident scenarios in water-cooled reactors. These ATF cladding should also perform comparable or better than the current zirconium alloy cladding under reactor normal operating conditions. Surface-modified Zircaloy-4 was produced by depositing a protective coating of chromium by two different coating techniques, Physical Vapor Deposition (PVD) and Cold Spray (CS). The coating thickness, structure, composition, and mechanical properties of the coated Zircaloy were assessed with advanced materials characterization techniques. Results showed a strengthening effect of the Cr-coating, along with ~83% higher hardness compared to that of the Zircaloy-4 substrate. Surface topography and surface chemistry of the Cr-coated Zircaloy-4 were assessed with contact profilometry, atomic force microscopy, contact angle goniometry, and X-ray photoelectron spectroscopy. Deposited Cr-coating significantly improved surface wettability compared to the substrate Zircaloy-4. The formation of surface oxides on the coatings by prolonged exposure to ambient air showed a further increase in the hydrophobic behavior. Surface parameters and surface chemistry after flow boiling critical heat flux tests, conducted at atmospheric pressure, evidenced a slight increase in surface roughness with notable changes in wettability associated with the formation of surface oxides.
The deposition of protective coatings on nuclear fuel cladding has been considered as a near-term Accident Tolerant Fuel (ATF) concept that will reduce the high-temperature oxidation rate and enhance accident tolerance of the cladding while providing additional benefits during normal and transient. In this study, the performance of the proposed ATF concept of Cr-coated-Zircaloy is assessed using a generic Boiling Water Reactor MELCOR plant model considering a Short-term Station Blackout (STSBO) scenario. Simulation results indicate that the use of Cr-coated-Zircaloy as cladding and canister material mitigates the core degradation process as compared to the traditional Zircaloy cladding and canister design. The onset of fuel degradation and collapse is delayed by over thirty minutes, and the extent of fuel degradation is reduced. Specifically, the gross in-vessel hydrogen generation decreased by almost a factor of three. Although the eutectic reaction between Cr-coating and Zircaloy could cause an early failure of the coating, the improvement in the delay of fuel degradation is still notable. In addition, a thicker coating is found helpful to obtain additional coping time and to decrease hydrogen generation. In addition to the eutectic formation that may compromise Cr-coated Zr, a different failure mode is identified for the Cr-coated-Zr when compared to Zircaloy; i.e., a complete melt of base material leads to component collapse before the coating is oxidized and consumed. These findings can help the industry focus on productive areas of research and development for accident-tolerant fuel concepts and enhancement of core safety margins.
This work assesses the potential of proton irradiation to simulate the neutron damage to the matrix and laves phase Zr(Fe,Cr) 2 precipitates in Zircaloy-4. Isothermal proton irradiation has been performed on Zircaloy-4 samples at irradiation temperatures ranging from 250 to 350 °C. Two-step proton irradiation was also performed to enhance the amorphization of and iron loss from the laves phase Zr(Fe,Cr) 2 precipitates. The irradiated microstructures, including dislocation loops and rafts near SPPs, were observed in proton irradiated Zircaloy-4, which are consistent with neutron irradiated material at a similar damage level. The amount of irradiation-induced hardening after proton irradiation was similar to post neutron irradiated data. The significant amorphization of the SPPs and concurrent Fe redistribution observed on neutron irradiated materials can be effectively emulated using a two-step proton irradiation on Zircaloy-4. Hence, the neutron irradiation effect on Zircaloy-4 can be mostly captured using the two-step proton irradiation described in this study.
This work developed a microstructure-based finite element model to predict the stress state of alloys with second phase inclusions. Quantitative microstructural details extracted from scanning electron microscopy (SEM) images were used to generate heterogeneous microstructures including the morphology and spatial distribution of hydrides. Generation of digital microstructure was achieved through two steps of tessellations using software Neper and Matlab. The process is demonstrated using an example of Zircaloy material with secondary phases of hydrides dispersed within and stress-strain response of Zircaloy containing hydrides was predicted. The constitutive material model for Zircaloy in this study was based on crystal plasticity theory which considers the hexagonal close-packed (HCP) atomic structure of Zircaloy material. The hydrides were modeled as isotropic elasto-plastic material. A parametric study had been conducted to understand the effect of volume fraction, and lamellae thickness of the hydride phase on the mechanical properties of the overall material. Results can help designers to alter the manufacturing process to obtain the enhanced mechanical properties for components used in nuclear applications made by Zircaloy material.
The popularity of crystal plasticity finite element method (CPFEM) models is increasing due to their ability to predict the mechanical response of crystalline materials such as metals and metal alloys more accurately than traditional continuum mechanics models. This is since the crystal plasticity models consider the effect of atomic structure, microstructural morphology, and properties of individual grains. These CPFEM models use a large number of material parameters in order to capture the mesoscale physics which comes with the downside of the tedious calibration process. In this paper, a CPFEM code was developed to include the twinning induced grain reorientation and subsequent crystallographic slip for HPC material. The developed code is incorporated in a large-scale, parallelized nonlinear solver WARP3D. Further, a sensitivity analysis with respect to 22 material parameters was then conducted using single crystal and polycrystal representative volume element (RVE) of Zircaloy material. Loading was applied along five different crystallographic orientations for single crystal RVE and along three directions namely, rolling (RD), transverse (TD), and normal (ND) direction for polycrystal RVE. Results obtained from the sensitivity analysis were used for the calibration of material parameters for Zircaloy. Finally, developed code along with calibrated material parameters was used to investigate the effect of the hydride phase formation in Zircaloy which is a typical case observed for nuclear applications. It was found that the volume fraction of the hydride phase has a significant impact on the mechanical properties of Zircaloy.
Coating the surface of Zircaloy-4 light water reactor fuel cladding tube is of considerable interest for enhancing its accident tolerance. In this study, thermal annealing of FeCrAl-coated Zircaloy-4 at 725 °C for 500 h, was used to induce interfacial reactions between Zircaloy-4 and FeCrAl. The interface zones were then irradiated by 3.5 MeV Zr ions at 400 °C, up to 50, 100, 150 peak dpa values. Transmission electron microscopy (TEM) and scanning TEM were used to characterize microstructural and composition changes before and after ion irradiation. Three interfacial phases were identified: FeZr 3 , (Fe,Cr) 2 Zr, and ZrC. The widest intermetallic layer, FeZr3, had large grains. The narrower phases, (Fe,Cr)2Zr and ZrC, contained small grains and were often mixed. The unexpected observation of the ZrC phase was attributed to the presence of very small impurity level concentrations of carbon in the powder material. No void swelling was observed in any of the phases, including the FeCrAl coating and Zircaloy-4 substrate. (Fe,Cr) 2 Zr, however, fully amorphized after irradiation, even at the lowest dpa.
Here, this study evaluated the embrittlement of Zircaloy-4 cladding by dry air and dry nitrogen environments as a function of process temperature and duration of exposure. A Netzsch thermogravimetric analyzer was used to measure the mass gain of cladding sections over time with specified temperature and gas flow programs. Oxidation of Zircaloy in dry air produced a brittle ZrO 2 layer with ductile unreacted metal. In contrast, nitridation of Zircaloy had a slower reaction rate but produced a brittle cladding that was more easily breached during ring compression tests. The ring compression tests demonstrated that ductility of Zircaloy cladding decreases as nitrogen pickup increases; a ductile-to-brittle transition occurs near a mass gain of 2.1 wt %. Nitridation showed minimal temperature dependency in ductility degradation, whereas oxidation showed significant temperature dependency in ductility degradation, with severe embrittlement occurring at 1200 °C. Optical micrographs confirmed the formation of uniform ZrN layers (approximately 12 µm thick) on the cladding surface, indicating that cladding embrittlement is primarily the result of nitrogen diffusion rather than metal layer thinning.
A tritium producing assembly, also known as tritium producing burnable absorber rods (TPBARs), consists of a metal getter tube located between the cladding and γ-LiAlO2 pellets. The metal getter tube is composed of a nickel (Ni) layer coated on Zircaloy-4. The getter assembly is used to capture tritium (3H) species (mainly 3H2 and 3H2O) generated from γ-LiAlO2 pellets during irradiation. Exploring 3H species (3H2, 3H2O) dissociation on the Ni surface and diffusion in the Ni layer and across the interface of Ni-plated Zircaloy-4 getters can provide insights on tritium transport and retention in the pellets and the getter materials. . In FY25, based on the ideal interface model of Ni-Zircaloy-4 generated in FY24, we will further explore the diffusion pathways of 3H across such Ni-ZrNi-alloy layer-Zircalory-4 interfaces under different conditions, including with oxide/hydroxide clusters on the Ni layer, and impurities located in ZrNi-alloy and Zircalory-4 layers. Due to the size limitation of DFT simulation, we will separate the 3-layer system into 3 sub-systems: Ni-ZrNi interface, ZrNi alloy layer, ZrNi-alloy-Zircaloy-4 interface, and simulate the diffusion barriers for tritium.
The ATR I-positions' isolation from the flux trap region provides an opportunity for a test facility that could create conditions representative of commercial light water reactors. Such a facility requires piping couplings and joints that withstand extreme thermal and pressure cycling. Also, transitioning from steel to zircaloy piping inside the reactor vessel allows the neutronic properties of zircaloy to be leveraged while using cost-effective stainless steel outside of the core. Grayloc-style hub couplings will act as transition points between stainless steel piping and zircaloy piping inside the reactor vessel. These couplings have not been sufficiently tested for leakage where there is a transition between materials. This transition is a concern because the thermal expansion coefficients of the materials differ. Seal integrity between the two components may be greatly affected by thermal expansion at the connection. Thus, the effect of thermal cycling must be assessed. Thermal and pressure cycling and hydrodynamic testing will be conducted to verify seal integrity of the steel to zircaloy hub coupling when subjected to ATR conditions.
In this work, a constitutive model for zircaloy-4 embedded with δ-phase hydride rim/blister structures (δ-phase zircaloy hydride) is presented. Nanoindentation and nano-scale impact experiments were performed on the δ-hydride blisters as a function of temperature in order to obtain strain rate dependent location specific constitutive response. A power law viscoplastic constitutive model was chosen to represent the strain rate dependent behavior. The strength coefficient and the strain hardening exponent in the power law relation were found to decrease with increase in temperature indicating softening behavior at higher temperatures. The strain rate exponent remained constant with increase in temperature indicating that the rate dependent ductility does not change significantly at higher temperatures. A finite element method based model was created to analyze the failure behavior and the ductile to brittle transition in zircaloy hydride. The model predicted that fracture strength of δ-phase zircaloy hydride decreases linearly with increase in temperature.