SEARCH · Engineering Papers
Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.
Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.
U2Mo crystallizes in the tetragonal I4/mmm space group. The structure is three-dimensional. U is bonded in a 9-coordinate geometry to four equivalent U and five equivalent Mo atoms. All U–U bond lengths are 2.79 Å. There are four shorter (2.99 Å) and one longer (3.11 Å) U–Mo bond lengths. Mo is bonded in a 10-coordinate geometry to ten equivalent U atoms.
Understanding the microstructural and phase changes occurring during irradiation and their impact on metallic fuel behavior is integral to research and development of nuclear fuel programs. This paper reports systematic analysis of as-fabricated and irradiated low-enriched U-Mo (uranium-molybdenum metal alloy) fuel using atom probe tomography (APT). This study is carried out on U-7 wt.% Mo fuel particles coated with a ZrN layer contained within an Al matrix during irradiation. The dispersion fuel plates from which the fuel samples were extracted are irradiated at Belgian Nuclear Research Centre (SCK CEN) with burn-up of 52% and 66% in the framework of the SELENIUM (Surface Engineering of Low ENrIched Uranium-Molybdenum) project. The APT studies on U-Mo particles from as-fabricated fuel plates enriched to 19.8% revealed predominantly γ-phase U-Mo, along with a network of the cell boundary decorated with α-U, γ’-U2Mo, and UC precipitates along the grain boundaries. The corresponding APT characterization of irradiated fuel samples showed formation of fission gas bubbles enriched with solid fission products. The intermediate burnup sample showed a uniform distribution of the typical bubble superlattice with a radius of 2 nm arranged in a regular lattice, while the high burnup sample showed a non-uniform distribution of bubbles in grain-refined regions. There was no evidence of remnant α-U, γ’-U2Mo, and UC phases in the irradiated U-7 wt.% Mo samples.
In this study we compared the microstructure evolution of U-Mo fuel foils produced with and without heat treatment at low burn-up via advanced post-irradiation examination. The aim of this study is to observe after irradiation the ways in which the fabrication processes have influenced fuel behavior at early-stage irradiation, as for very low burn up microstructural studies are lacking. In this work it was observed that the larger grain size detected in the heat-treated samples before irradiation led to decreased grain refinement after irradiation. Grain refinement was associated with the presence of small nano-size bubbles and precipitates. This phenomenon is hypothesized to influence early fuel swelling during reactor irradiation. Grain refinement was also observed to increase in regions where γ-U decomposition was present. Thus, it was enhanced in the samples fabricated without heat treatment. The heat treatment also increased the thickness of the U-Mo/Zr interface, namely of the UZr 2 layer. However, the influence of this layer on fuel performance needs further investigation. On one side, it may contribute to better mechanical bonding; on the other, it may influence swelling and blistering in the interaction layer as porosity increases when this layer is increased. This was observed especially in the presence of increased area containing low Mo concentration, and thus containing a higher fraction of the α-U phase, which is highly susceptible to irradiation induced swelling. Strong evidence of reverse transformation under irradiation (α-U + γ'-U2Mo → bcc γ-U) was observed in these samples. While the precipitates (carbides and oxide) seem to be unaffected by the irradiation at these low burnups. However, further analyses are necessary at higher burn-up to assess the exact impact different heat treatments have on fuel performance.