Crystallographic and TEM Features of a TBC/Ti2AlC MAX Phase Interface after 1300°C Burner Rig Oxidation
A FIB/STEM interfacial study was performed on a TBC/Ti 2 AlC MAX phase system, oxidized in an aggressive burner rig test (Mach 0.3 at 1300 °C for 500 h). The 7YSZ TBC, α-Al 2 O 3 TGO, and MAXthal 211 TM Ti 2 AlC base were variously characterized by TEM/STEM, EDS, SADP, and HRTEM. The YSZ was a mix of “clean” featureless and “faulted” high contrast grains. The latter exhibited ferro-elastic domains of high Y content tetragonal t″ variants. No martensite was observed. The TGO was essentially a duplex α-Al 2 O 3 structure of inner columnar plus outer equiaxed grains. It maintained a perfectly intact, clean interface with the Ti 2 AlC substrate. The Ti 2 AlC substrate exhibited no interfacial Al-depletion zone but, rather, numerous faults along the basal plane of the hexagonal structure. These are believed to offer a means of depleting Al by forming crystallographic, low-Al planar defects, proposed as Ti 2.5 AlC 1.5 . These characterizations support and augment prior optical, SEM, and XRD findings that demonstrated remarkable durability for the YSZ/Ti 2 AlC MAX phase system in aggressive burner tests.