An oxidation resistant coating for titanium alloys and titanium alloy matrix composites comprises an MCrAlX material. M is a metal selected from nickel, cobalt, and iron. X is an active element selected from Y, Yb, Zr, and Hf.
Titanium alloys are processed to develop a wide range of microstructure configurations and therefore material properties. While these properties are typically measured experimentally, a framework for property prediction could greatly enhance alloy design and manufacturing. In this work, a microstructure-sensitive framework is presented for the prediction of strength and ductility as well as estimates of the bounds in variability for these properties. The framework explicitly considers distributions of microstructure via new approaches for instantiation of structure in synthetic samples. The parametric evaluation strategy, including the finite element simulation package FEpX, is used to create and test virtual polycrystalline samples to evaluate the variability bounds of mechanical properties in Ti-6Al-4V. Critical parameters for the property evaluation framework are provided by measurements of single crystal properties and advanced characterization of microstructure and slip system strengths in 2D and 3D. Property distributions for yield strength and ductility are presented, along with the validation and verification steps undertaken. Comparisons between strain localization and slip activity in virtual samples and in experimental grain-scale strain measurements are also discussed.
Titanium alloys stress corrosion cracking /SCC/ from metallurgical-mechanical viewpoint, discussing phase transformations, dislocation arrangements, crack propagation, etc
Titanium hydride deformation assisted nucleation in alpha-beta titanium alloy, showing low strain rate embrittlement and stress corrosion crack propagation in aqueous environments
Stress corrosion cracking of titanium alloys and aluminum alloys
This work was performed to determine the tensile properties of cast, hot isostatic pressed (HIP'ed), and annealed titanium alloys, Ti-6Al-4V ELI and Ti-5Al-2.5Sn ELI, that are candidate materials for the space transportation main engine (STME) liquid hydrogen turbopump impeller. Samples of the cast alloys were HIP'ed, annealed, and machined into tensile specimens. The specimens were tested in air at ambient temperature (70 F) and also at -423 F in liquid hydrogen. The Ti-6Al-4V alloy had an average ultimate strength of 129.1 ksi at 70 F and 212.2 ksi at -423 F. The Ti-5Al-2.5Sn alloy had an average ultimate strength of 108.4 ksi at 70 degrees F and 185.0 ksi at -423 F. The ductility, as measured by reduction of area, for the Ti-6Al-4V averaged 15.2 percent at 70 F and 8.7 percent at -423 F, whereas for the Ti-5Al-2.5Sn alloy average reduction of area was 24.6 percent at 70 F and 11.7 percent at -423 F.
Traditionally, titanium alloys with satisfactory mechanical properties can only be produced via energy-intensive and costly wrought processes, while titanium alloys produced using low-cost powder metallurgy methods consistently result in inferior mechanical properties, especially low fatigue strength. Herein, we demonstrate a new microstructural engineering approach for producing low-cost titanium alloys with exceptional fatigue strength via the hydrogen sintering and phase transformation (HSPT) process. The high fatigue strength presented in this work is achieved by creating wroughtlike microstructures without resorting to wrought processing. This is accomplished by generating an ultrafine-grained as-sintered microstructure through hydrogen-enabled phase transformations, facilitating the subsequent creation of fatigue-resistant microstructures via simple heat treatments. Finally, the exceptional strength, ductility, and fatigue performance reported in this paper are a breakthrough in the field of low-cost titanium processing.
A high-strength dual a+ß phase titanium alloy Ti–6Al–4V is utilized as a material for beam windows in several accelerator target facilities. However, relatively little is known about how material properties of this alloy are affected by high-intensity proton beam irradiation. With plans to upgrade neutrino facilities at J-PARC and Fermilab to over 1 MW beam power, the radiation damage in the window material will reach a few displacements per atom (dpa) per year, significantly above the ~0.3 dpa level of existing data. The international RaDIATE collaboration, Radiation Damage In Accelerator Target Environments, has conducted a high intensity proton beam irradiation of various target and window material specimens at Brookhaven Linac Isotope Producer (BLIP) facility, including a variety of titanium alloys. Post-Irradiation Examination (PIE) of the specimens in the 1st capsule, irradiated at up to 0.25 dpa, is in progress. Tensile tests in a hot cell at Pacific Northwest National Laboratory (PNNL) exhibited a clear signature of radiation hardening and loss of ductility for Ti–6Al–4V, while Ti–3Al–2.5V, with less ß phase, exhibited less severe hardening. Microstructural investigations will follow to study the cause of the difference in tensile behavior between these alloys. High-cycle fatigue (HCF) performance is critical to the lifetime estimation of beam windows exposed to a periodic thermal stress from a pulsed proton beam. The first HCF data on irradiated titanium alloys are to be obtained by a conventional bend fatigue test at Fermilab and by an ultrasonic mesoscale fatigue test at Culham Laboratory. Specimens in the 2nd capsule, irradiated at up to ~1 dpa, cover typical titanium alloy grades, including possible radiation-resistant candidates. These systematic studies on the effects of radiation damage of titanium alloy materials are intended to enable us not only to predict realistic lifetimes of current beam windows made of Ti–6Al–4V, but also to extend the lifetime by choosing a more radiation and thermal shock tolerant alloy with a preferable heat treatment, or even by developing new materials.
Experiments were conducted to determine the friction and wear characteristics of aluminum bronzes and copper-tin, titanium-tin, and copper-silver alloys sliding against a titanium-6% aluminum-4% vanadium alloy (Ti-6Al-4V). Hemispherically tipped riders of aluminum bronze and the titanium and copper alloys were run against Ti-6Al-4V disks in air at 430 C. The sliding velocity was 13 cm/sec, and the load was 250 g. Results revealed that high tin content titanium and copper alloys underwent significantly less wear and galling than commonly used aluminum bronzes. Also friction force was less erratic than with the aluminum bronzes.
During high temperature exposure, an interfacial reaction occurs between SiC fiber reinforcement and titanium matrices which can be detrimental to the mechanical properties of the composite. The reaction kinetics between SCS-6 fibers and Ti-1100 were determined at 800 to 1000 C and found to be slower than those of other currently used titanium alloys (Ti-15-3, Ti-6-4). The experimentally determined reaction kinetics for Ti-1100 were extrapolated to 700 C and found to accurately predict reaction zone size after 1000 hours of exposure. Predictions of the time to consume the surface layer on the SCS-6 and SCS-9 fibers were made in an effort to estimate the time that the fiber will retain its strength in Ti-1100 during isothermal exposure at high temperatures. Using this approach, the strength of an SCS-6 fiber in Ti-1100 should be retained for over 20,000 hours at isothermal exposures less than 800 C. Strength predictions using the rule of mixtures for a unidirectional Ti-1100/SCS-6 composite are presented for short term exposures up to 700 C. Room temperature tests of an as-fabricated 20 volume percent fiber/Ti-1100 composite yielded a UTS of 226 ksi (1490 MPa) which is close to that predicted by the ROM.
A high-intensity proton beam exposure with 181 MeV energy has been conducted at Brookhaven Linac Isotope Producer facility on various material specimens for accelerator targetry applications, including titanium alloys as a beam window material. The radiation damage level of the analyzed capsule was 0.25 dpa at the beam center region with an irradiation temperature around 120 oC. Tensile tests showed increased hardness and a large decrease in ductility for the dual a+ß-phase Ti-6Al-4V Grade-5 and Grade-23 extra low interstitial alloys, with the near a-phase Ti-3Al-2.5V Grade-9 alloy still exhibiting uniform elongation of a few % after irradiation. Transmission Electron Microscope analyses on Ti-6Al-4V indicated clear evidence of a high-density of defect clusters with size less than 2 nm in each a-phase grain. The ß-phase grains did not contain any visible defects such as loops or black dots, while the diffraction patterns clearly indicated ?-phase precipitation in an advanced formation stage. The radiation-induced ?-phase transformation in the ß-phase could lead to greater loss of ductility in Ti-6Al-4V alloys in comparison with Ti-3Al-2.5V alloy with less ß-phase.google scho
Highlights: • First systematic error analyses for XDIC • First XDIC study of Ti-6Al-4V under dynamic tension • Deformation mode transition induces dynamic ductility decrease. • Dynamic shear localization due to rate-dependent microvoid coalescence process. - Abstract: Dynamic and quasi-static tension experiments are conducted on Ti-6Al-4V alloys, with in situ, synchrotron-based, high-speed, x-ray phase contrast imaging implemented to characterize the dynamic deformation and fracture process of Ti alloys at the Advanced Photon Source. X-ray digital imaging correlation (XDIC) is applied for strain field mapping. The size distribution of x-ray speckles are quantified via a morphological analysis, with a mean of ∼20 μm. Systematic error analyses of displacement and strain field measurements are firstly conducted for XDIC, and demonstrate that the displacement and strain errors can be controlled below 0.01 pixel and 0.1%, respectively. Mesoscale strain characteristics measured via XDIC are consistent with and reveal mechanisms for the bulk-scale stress–strain responses. Under dynamic tension, a sharp transition to strain softening occurs when the bulk strain exceeds about 0.04, which leads to a lower dynamic fracture strain (0.08) than the quasi-static one (0.1). The corresponding strain filed mapping demonstrates that shear deformation localizations grow and coalesce rapidly into a narrow shear deformation band under dynamic loading, while tensile deformation and necking progresses gradually under quasi-static loading. Scanning electron microscopy shows that void nucleation occurs mainly at the interface of α and β phases for both quasi-static and dynamic tension. However, microvoids coalesce preferentially along colony boundaries or the boundary α phase under quasi-static tension, but along the maximum shear stress direction (across colonies) under dynamic tension. Fractography of recovered samples also shows consistent features.
Abstract not provided
Ingot of titanium alloy containing three percent aluminum studied to develop production technology
Stress corrosion cracking behavior in titanium, molybdenum, and aluminum alloys, and electrochemical kinetic studies
Not Available
Not provided.