NASA NTRS1991

Compression behavior of TiB2-particulate-reinforced composites of Al22Fe3Ti8

The compression behavior of both the monolithic L1(2) compound Al22Fe3Ti8 and discontinuous composites obtained by incorporating about 1 micron TiB2 particles was studied for various volume percent reinforcements as a function of temperature and at high temepratures as a function of strain rate. In this study, by varying the Fe and Ti contents, the nature and volume fraction of the minor phases coexisting with the dominant L1(2) phase were changed and were examined with and without TiB2 reinforcement. At high strain rates, the TiB2 reinforcements significantly enhance ambiant and warm-temperature strength, although a crossover is observed at about 1000 K, above which the monolithic material is stronger than the composite. At slow strain rates representative of creep conditions, however, the TiB2-containing composites retain their superiority at least up to 1200 K.

Dipietro, M. S.↗
NASA NTRS1986

Elevated temperature strengthening of a melt spun austenitic steel by TiB2

Mechanical properties of an iron-based alloy containing (by wt pct) 33Ni, 2Al, 6Ti, and 2B (resulting in an alloy containing 10 vol pct TiB2) were evaluated by hardness and tensile testing. The alloy was cast as a ribbon using a dual 'free-jet' variation of Jech et al. (1984) method of chill-block melt-spinning against a copper wheel; to simulate thermal cycles the alloy ribbon would experience during compaction into shapes, various segments of the ribbon were annealed under a vacuum at temperatures ranging from 500 to 1150 C. The results show that maximum strengths at 650 and 760 C were developed in ribbons annealed at 1100 C; in these ribbons an optimal combination of grain coarsening with minimum TiB2 particle growth was observed. However, the elevated-temperature strength of the TiB2-strengthened alloy under optimal annealing conditions was poorer than that of conventional iron-based superalloys strengthened by gamma-prime precipitates.

Michal, G. M.↗
NASA NTRS1990

Elevated temperature slow plastic deformation of NiAl-TiB2 particulate composites at 1200 and 1300 K

Elevated temperature compression testing has been conducted in air at 1200 and 1300 K with strain rates varying from about 10 to the -4th to about 10 to the -7th/sec on NiAl-TiB2 particulate composites. These materials, which consisted of a B2 crystal structure intermetallic Ni-50 at. pct Al matrix and from 0 to 30 vol pct of approximately 1- micron diameter TiB2 particles, were fabricated by XD synthesis and hot pressed to full density. Flow strength of the composites increased with volume fraction of the strengthening phase with NiAl-30TiB2 being approximately three times stronger than NiAl. Comparison of the light optical and TEM microstructures of as-received and tested samples revealed that reactions did not occur between the two phases, and NiAl-TiB2 interfaces were not cracked during deformation. Additional TEM indicated that the particles stabilize a vastly different microstructure in the NiAl matrix of the composites than that formed in unreinforced NiAl.

Whittenberger, J. Daniel↗
NASA NTRS1991

The effect of TiB2 reinforcement on the mechanical properties of an Al-Cu-Li alloy-based metal-matrix composite

The addition of ceramic particles to aluminum based alloys can substantially improve mechanical properties, especially Young's modulus and room and elevated temperature strengths. However, these improvements typically occur at the expense of tensile ductility. The mechanical properties are evaluated to a metal matrix composite (MMC) consisting of an ultrahigh strength aluminum lithium alloy, Weldalite (tm) 049, reinforced with TiB2 particles produced by an in situ precipitation technique called the XD (tm) process. The results are compared to the behavior of a nonreinforced Weldalite 049 variant. It is shown that both 049 and 049-TiB2 show very attractive warm temperature properties e.g., 625 MPa yield strength at 150 C after 100 h at temperature. Weldalite 049 reinforced with a nominal 4 v pct. TiB2 shows an approx. 8 pct. increase in modulus and a good combination of strength (529 MPa UTS) and ductility (6.5 pct.) in the T3 temper. And the high ductility of Weldalite 049 in the naturally aged and underaged tempers makes the alloy a good, high strength matrix for ceramic reinforcement.

Source record↗
NASA NTRS1991

The effect of TiB2 reinforcement on the mechanical properties of an Al-Cu-Li alloy-based metal-matrix composite

Weldalite 049, an Al-base Cu-Li-Mg-Ag-Zr alloy, achieves 700 MPa tensile strengths in the near-peak-aged temper in virtue of the nucleation of a T(1)-type platelike strengthening precipitate. Attention is presently given to the possibility that the alloy's modulus could be further increased through the addition of high-modulus TiB2 particles, using the 'XD' process, due to TiB2's good wettability with liquid Al. An 8-percent modulus increase is obtained with 4 vol pct TiB2.

Langan, T. J.↗
NASA NTRS1990

High-temperature slow-strain-rate compression studies on CoAl-TiB2 composites

Results are presented of compressive deformation tests performed on particulate-reinforced CoAl-TiB2 composites in the temperature range 1100-1300 K. Hot-pressed and postdeformation microstructures were characterized by TEM and by optical microscopy. It was found that the addition of TiB2 particles improves the deformation resistance of the matrix, due to dislocation-particle interactions.

Mannan, S. K.↗
NASA NTRS1991

Effect of Li level, artificial aging, and TiB2 reinforcement on the modulus of Weldalite (tm) 049

The dynamic Young's Modulus (E) was determined for (1) alloys 049(1.3)(heat 072), (2) 049(1.9), and (3) 049(1.3) TiB2 in the T3 temper and after aging at 160 C were made on a single 0.953 cm (0.375 in) cube to reduce scatter from microstructural inhomogeneities. Both shear and transverse wave velocities were measured for the L, LT, and ST directions by a pulse echo technique. These velocities were then used to calculate modulus. The change is shown in E with aging time at 160 C (320 F) for the three alloys. It is clear from the plots that aging has a minor, but measurable, influence on the E of alloys 049(1.3) and 049(1.9): E decreases by -2.5 pct. for 2 and 3 during the initial stages of artificial aging. This decrease in E generally follows the strength reversion. On further aging beyond the reversion well, E increases and then decreases again as the alloy overage. The slightly higher modulus in the T8 than in the T3 temper is consistent with the presence of the high modulus T sub 1 phase in the T8 temper. A similar change in E was observed on aging for the TiB2 reinforced variant that also follows the aging curve.

Source record↗
NASA NTRS1995

The effect of gravity on the combustion synthesis of Ni-Al and Ni3Al-TiB2 composites from elements

Previous studies on the combustion synthesis of advanced materials indicate that combustion and structure formation mechanisms involve several stages including melting of reactants and products, spreading of the melt, droplet coalescence, diffusion and convection, buoyancy of solid particles, and densification of the liquid product. Most of these processes are affected by gravity. Conducting the combustion synthesis under microgravity conditions is expected to help elucidate the reaction mechanisms. Two systems were examined. The first involves Ni/AI cladded particles, which is an ideal system to examine the individual particle and liquid flow before combustion occurs. For comparison, elemental Ni and Al powders with the same stoichiometry as that of the cladded particles were also used in some experiments. The second system was the Ni3AITiB2 composite in which the Ni3AI (-delta H(sub f) = 153.1 kJ/mol) phase melts during reaction enabling us to examine settling of the liquid phase. The amount of liquid phase was controlled by varying the TiB2 (-delta H(sub f) = 323.8 kJ/mol) content which generates the additional heat. The overall reactions for the two systems can be expressed as follows. System 1: 4Ni + 2AI yields Ni3AI + NiA and System 2: 3Ni + Al + x (Ti + 2B) yields Ni3Al + x(TiB2). For the first system, pellets were pressed directly from the cladded particles, at green densities about 77 +/- 3% of theoretical value. For the second, the pellets were prepared by mixing the elemental reactant powders in the required stoichiometry by ball-milling and then pressing uniaxially at green densities about 70 +/- 3 percent of theoretical. The pellets were cylindrical in shape, 10 mm in diameter and length typically 20-30 mm. The pellet samples were reacted in UHP Argon (1 atm) using the experimental setup and procedure described previously. After reaction, the samples were sectioned axially in order to conduct the microstructural analysis in the longitudinal direction. The phase composition of the reacted product was determined by X-ray diffraction (XRD) and the microstructure was analyzed using scanning electron microscopy (SEM) along with energy dispersive X-ray spectrometry (EDX).

Varma, Arvind↗
NASA NTRS1989

Fracture resistance of a TiB2 particle/SiC matrix composite at elevated temperature

The fracture resistance of a commercial TiB2 particle/SiC matrix composite was evaluated at temperatures ranging from 20 to 1400 C. A laser interferometric strain gauge (LiSG) was used to continuously monitor the crack mouth opening displacement (CMOD) of the chevron-notched and straight-notched, three-point bend specimens used. Crack growth resistance curves (R-curves) were determined from the load versus displacement curves and displacement calibrations. Fracture toughness, work-of-fracture, and R-curve levels were found to decrease with increasing temperature. Microstructure, fracture surface, and oxidation coat were examined to explain the fracture behavior.

Jenkins, Michael G.↗
NASA NTRS1991

Weldability of Weldalite (tm) 049 with and without TiB2 reinforcement

The effects are assessed of TiB2 reinforcement and parent alloy Li content on the weldability of Weldalite (tm) 049 type alloys. Welding trials were performed using either AC or DC polarity gas tungsten arc (GTA) welding according to described procedures. The welding was performed under conditions of high restraint on 5 cm (2 in) wide x 25.4 cm (10 in) long plates machined from the 0.952 cm (0.375 in) extruded bar parallel to the extrusion direction. A 37.5 deg bevel was machined on the center edge of the extruded bar. Cut rod filler wire was machined from three alloys, and one commercially available 2319 filler wire was also used. The preliminary assessment of the weldability revealed no propensity for hot cracking under conditions of high restraint. This result is significant, because hot cracking has been reported for all other leading aluminum lithium alloys welded with certain conventional filler alloys. The strengths for Weldalite parent welded with parent filler obtained were higher than those for alloys used in launch systems, such as 2219 and 2014 welded with 2319 and 4043 fillers, respectively. Even higher values were obtained by variable polarity plasma arc welding (e.g., 54 ksi (372 MPa) mean tensile strength).

Source record↗
NASA NTRS1991

Effect of Li level, artificial aging, and TiB2 reinforcement on the fracture toughness of Weldalite (tm) 049-type alloys

Plane strain fracture toughness (K sub IC) was evaluated for Weldalite (tm) 049 with and without TiB2 reinforcement. For the nonreinforced variant, changes in toughness were measured for various aging conditions and lithium levels. Toughness testing was carried out on fatigue precracked compact tension (CT) specimens at 24 C, as per ASTM standard E-399. Toughness was measured as a function of aging time at 160 C for the two Weldalite 049(1.3) heats. The composition of these heats differed only in that 0.03 wt pct. Ti was added to one as an additional grain refiner. Both heats showed a decrease in toughness with increasing aging time, although toughness values for one were significantly higher than for the other. This greater toughness may be due to a subtle change in the grain size resulting for the presence of Ti or, alternatively, to differences in texture or substructure formed during extrusion.

Source record↗
NASA NTRS1988

Fracture resistance of a TiB2 particle/SiC matrix composite at elevated temperature

The fracture resistance of a commercial TiB 2 particle/SiC matrix composite was evaluated at temperatures ranging from 20 to 1400 °C. A laser interferometric strain gauge (LISG) was used to continuously monitor the crack mouth opening displacement (CMOD) of the chevron-notched and straight-notched, three-point bend specimens used. Crack growth resistance curves (R-curves) were determined from the load versus displacement curves and displacement calibrations. Fracture toughness, work-of-fracture, and R-curve levels were found to decrease with increasing temperature. Microstructure, fracture surface, and oxidation coat were examined to explain the fracture behavior.

Fracture↗
NASA NTRS1991

Combustion synthesis of TiB2-Al2O3-Al composite materials

The oxide-aluminum exothermic reduction reaction is presently used in the combustion-synthesis of ceramic/metal composites. An excess of Al is used in the reacting materials, which rapidly generate enough heat to exceed Al's melting point. The molten Al thus evolved is allowed to infiltrate the porous ceramic matrix as the exothermic reaction proceeds; this feature of the process turns the disadvantage of high porosity levels in combustion-synthesized materials into an advantage. Attention is given to the system obtained with 3TiO2 + 3B2O3 + (10-x)Al starting materials.

Feng, H. J.↗
NASA NTRS2007

Ground-Based Testing of TiB2 and Al2O3/TiB2 Response to Space Environment

Two materials, titanium diboride and an alumina/titanium diboride composite, exhibit characteristics favorable for use in multiple space applications. These characteristics include low mass (4.52 gm/cc), high strain rate impact resistance, high temperature use (3000oC M.P.), thermal and electrical conductivity, thermal shock resistance, and high visible-range reflectivity. Additionally, the presence of boron in these materials gives them the potential to shield against neutron radiation as well as charged radiation. These materials are flying on MISSE 6 to assess material changes resulting from exposure to the space environment. This study provides a preliminary, ground-based examination of these materials' interactions with individual components of the space environment, in particular atomic oxygen (AO) and neutron radiation, in order to better predict and understand post-flight results. Individual specimens are exposed to ground state AO and surface oxidation is measured. Equivalent exposures of up to 13 months show no rapid oxidation, however evidence indicates some surface oxidation occurring. Other samples are placed near a polyethylene moderated, one Ci Am/Be neutron source to determine their shielding capability. Comparisons between exposed and shielded indium foil, which is activated by transmitted neutrons, measure each material's ability to shield neutrons. Preliminary results indicate a significant shielding benefit provided by both materials.

Jefferies, Sharon A.↗
NASA NTRS1990

The Mechanisms of Dispersion Strengthening and Fracture in Al-based XD (TM) Alloys

The influence of reinforcement size, volume fraction, and matrix deformation behavior on room and elevated temperature strength, and the fracture toughness of metal matrix composites of both pure aluminum and Al(4 percent)Cu(1.5 percent)Mg with 0 to 15 vol percent TiB2 were examined. Higher TiB2 volume fractions increased the tensile yield strength both at room and elevated temperatures, and reduced the elongation to fracture. Tensile tests also indicate that small particles provided a greater increase in strength for a given volume fraction than larger particles, whereas elongation to fracture appeared to be insensitive to reinforcement size. The fracture toughness of the Al(4 percent)Cu(1.5 percent)Mg alloys decreased rapidly with TiB2 additions of 0 to 5 vol percent and more slowly with TiB2 additions of 5 to 15 vol percent. Fracture toughness appears to be independent of TiB2 particle size. The isothermal-aging response of the precipitation strengthened Al(4 percent)Cu(1.5 percent)Mg alloys was not altered by the presence of TiB2.

Aiken, R. M., Jr.↗
NASA NTRSDate not supplied

Macro-scale Testing and Micromechanics Modeling of Fracture Behaviors for Boron Carbide Composites with Hierarchical Microstructures

With a unique combination of properties including high hardness, low density, wear and corrosion resistance, thermal stability, high neutron absorption, and semi-conductivity, boron carbide (B4C) is a candidate material for various engineering applications that involve extreme environment. The current applications of boron carbide, however, are limited by its intrinsic brittleness due to its strong covalent bonding. To toughen boron carbide, in this work hierarchical microstructure designs was used to provide multiple toughening mechanisms including crack deflection/bridging, micro-crack toughening, etc. Using field assisted sintering, B4C composites with hierarchical microstructure features including graphite platelets, micron and sub-micron sized TiB2 reinforcements were fabricated. The fracture toughness of fabricated B4C composites were previously measured at micro-scale using micro-indentation followed by post-testing microstructure inspection. However, questions including whether the fracture toughness enhancement measured at micro-scale can translate to macro-scale mechanical properties, and what are the fundamental mechanisms behind observed fracture toughness enhancement, remain to be answered. In this study, the fabricated B4C composites were tested using standardized four-point bending method to obtain fracture toughness at macro-scale. In addition, micromechanics modeling was conducted using MAC/GMC code and crack-band model to study the effect of residual stress and weak interphases on fracture behaviors of B4C composites reinforced with TiB2 particles. Through standardized four-point bending tests, fracture toughness enhancements up to 2.85, 3.32, and 3.65 MPa∙m(exp 1/2) (from 2.38 MPa∙m(exp 1/2)) were achieved for B4C composites with graphite platelets addition (micro/nano B4C), with TiB2 formation (micro B4C-TiB2), and with both graphite and TiB2 addition (micro/nano B4C-TiB2) respectively. Micromechanics modeling indicated that introduction of thermal residual stress and weak interphases caused enhanced micro-cracking behavior and resulted in the observed fracture toughness enhancement. These results furthered understanding about the mechanical behaviors at macro-scale and the mechanisms behind observed fracture toughness enhancement for B4C composites with hierarchical microstructures and can provide reference data for the future design of B4C composites with optimized microstructures for further fracture toughness enhancement.

Boron Carbide↗
NASA NTRSDate not supplied

Toughening of Boron Carbide Composites by Hierarchical Microstructuring

Due to a unique combination of properties including high hardness, low density, chemical and thermal stability, semi-conductivity, and high neutron absorption, boron carbide (B4C) is a potential candidate for various applications involving extreme environment. However, B4C’s current application is limited because of its low fracture toughness. In this study, a hierarchical microstructure design with features including TiB2 grains and graphite platelets was used to toughen B4C by simultaneously utilizing multiple toughening mechanisms including crack deflection, bridging, and micro-crack toughening. Using field-assisted sintering technology (FAST), B4C composites with dense and hierarchical microstructure were fabricated. Previously, the fracture toughness of fabricated B4C composites was measured at micro-scale using micro-indentation to have up to 56% improvement. In this work, the B4C composites’ fracture toughness was characterized at macro-scale using four-point bending methods and compared with previous results obtained at micro-scale. Micromechanics modeling of fracture behaviors for B4C-TiB2 composites was also performed to evaluate the contributions from experimentally observed toughening mechanisms. From four-point bending tests, B4C composites reinforced with both TiB2 grains (~15 vol%) and graphite platelets (~8.7 vol%) exhibited the highest fracture toughness enhancement from 2.38 to 3.65 MPa∙m^(1/2). The measured values were lower than those obtained using micro-indentation but maintained the general trends. The discrepancy between the indentation and four-point bending test results originated from the complex deformation behaviors triggered by the high contact load during indentation tests. Through micromechanics modeling, introduced thermal residual stress due to thermal expansion mismatch between B4C and TiB2, and weak interphases at B4C-TiB2 boundaries were identified as the main causes for experimentally observed toughness enhancement. These results proved the effectiveness of hierarchical microstructure designs for B4C toughening and can provide reference for the future design of B4C composites with optimized microstructures for further fracture toughness enhancement.

composites↗
NASA NTRS1988

Elevated temperature slow plastic deformation of NiAl/TiB2 particulate composites

The 'XD' process for production of discontinuously-reinforced metal-matrix composites has been used to enhance the high-temperature strength of NiAl-TiB2 composites with particulate densities of up to 30 vol pct. SEM, TEM, and optical characterizations of the resulting microstructures showed the average TiB2 particle size to be about 1 micron, while the average grain of the NiAl matrix was of the order of 10 microns. Elevated temperature compression tests conducted at 1200 and 1300 K indicated flow strengths to increase with TiB2 content, so that the 20 vol pct TiB2-reinforced composite was three times stronger than the unreinforced NiAl; this is ascribed to the very high density of microstructural tangled dislocations, loops, and subgrain boundaries connecting the particles.

Whittenberger, J. Daniel↗