Electrospun Ti–Zr Oxide Heterostructures Enable Strongly Anchored Ultralow-Ir Anodes for Durable Acidic Oxygen Evolution
Proton-exchange-membrane water electrolysis (PEMWE) requires acidic oxygen-evolution-reaction (OER) anodes that combine high activity, high durability, and low Ir loading. Here, we report a Ti-Zr composite electrospun oxide (ESO) nanorod support that enables ultralow-Ir anodes for high-performance PEMWE. Zr-containing Ti oxide heterostructures stabilize anatase-rich TiO2, tune the local oxygen-coordination environment, and strengthen interfacial anchoring of IrOx under acidic anodic conditions. The electrospun nanorod network further creates an open, mechanically coherent catalyst layer that improves Ir utilization, ionomer penetration, and mass transport. At an anode loading of 0.2 mgIr cm-2, the optimized Ir/TiZr20-ESO anode delivers a PEMWE mass activity of 0.99 A mgIr-1 at 1.45 V, 28.3 and 43.0 times higher than commercial Ir black and commercial IrO2/TiO2, respectively. The same anode reaches 3.0 and 4.0 A cm-2 at 1.75 and 1.83 V, respectively, and sustains 2000 h operation at 2.0 A cm-2. Also, accelerated stress tests up to 525 hours over 31,500 cycles confirm promising long-term durability, with an insignificant performance decay of 0.4 μV per cycle. Density functional theory indicates that the Ti-Zr oxide heterostructure suppresses Ti demetallation and strengthens IrO2 interfacial binding, rationalizing the improved high-current-density stability.