NASA NTRS1968

Determination of Flaw Growth Characteristics of Ti-6Al-4V Sheet in the Solution-Treated and Aged Condition

The specific experimental investigation undertaken was designed to answer these questions on Ti-6Al-4V in the solution treated and aged condition. The defect growth and fracture characteristics were studied in parent (unwelded) and welded sheet material. The results of the study indicate that cryogenic proof testing will screen smaller size defects than proof testing at ambient conditions. However some unusual crack growth behavior during the proof test simulation suggests that some further study be made of stress and time duration effects.

Hoeppner, David W.↗
NASA NTRS1971

The influence of temperature on fatigue-crack growth in a mill-annealed Ti-6Al-4V alloy

To understand the influence of temperature on the rate of fatigue crack growth in high strength metal alloys, constant load amplitude fatigue crack growth experiments were carried out using a 1/4 inch thick (6.35 mm) mill-annealed Ti-6Al-4V alloy plate as a model material. The rates of fatigue crack growth were determined as a function of temperature, ranging from room temperature to about 290 C and as a function of the crack tip, stress intensity factor K, in dehumidified high purity argon environment. The dependence of the rate of fatigue crack growth on K appears to be separable into two regions. The transition correlates with changes in both the microscopic and macroscopic appearances of the fracture surfaces, and suggests a change in the mechanism and the influence of microstructure on fatigue crack growth.

Wei, R. P.↗
NASA NTRS1970

Low-temperature embrittlement of Ti-6Al-4V and Inconel-718 by high pressure hydrogen

Notched specimens of titanium alloy and Inconel-718 exhibit little reduction of notch strength at certain low temperatures under 2000 lb/sq in. hydrogen, unnotched specimens are not embrittled at these temperatures. The degree of Inconel-718 embrittlement is lower than earlier observations under 1000 lb/sq in. hydrogen.

Chandler, W. T.↗