There is increasing interest in the degradation mechanism studies of thermal and environmental barrier coatings (TEBCs) of gas turbines by molten CaO-MgO-Al(exp. 2)O(exp. 3)-SiO(exp. 2) CMAS). CMAS minerals are usually referred as silicon-containing sand dust and volcano ash materials that are carried by the intake air into gas turbines, e.g. in aircraft engines, and their deposits often react at high temperatures (greater than 1200 degrees C) with the engine turbine coating systems and components. The high temperature reactions causes degradation and accelerated failure of the static and rotating components of the turbine engines. We discuss some results of the reactions between the CMAS and Rare-Earth (RE = Y, Yb, Dy, Gd, Nd and Sm) - oxide stabilized ZrO(exp. 2) or HfO(exp. 2) systems, and the stability of the resulting oxides and silicates. Plasma sprayed hollow tube samples (outside diameter = 4.7 mm, wall thickness = 0.76 mm and = 26 mm height) were half filled with CMAS powder, wrapped and sealed with platinum foil, and heat treated at 1310 degrees C for 5h. Samples were characterized by differential scanning calorimetry (DSC), X-ray diffraction, and cross-section electron microscopy analysis and energy dispersive X-ray spectroscopy. It was found that CMAS penetrated the samples at the grain boundaries and dissolved the TEBC materials to form silicate phases containing the rare-earth elements. Furthermore, it was found that apatite crystalline phases were formed in the samples with total rare-earth content higher than 12 mol% in the reaction zone for the ZrO(exp. 2) system. In general, samples with the nominal compositions (30YSZ), HfO(exp. 2)-7Dy(exp. 2)O(exp. 2) and ZrO(exp. 2)-9.5Y(exp. 2)O(exp. 3)-2.25Gd(exp. 2)O(exp. 3)-2.25Yb(exp. 2)O(exp. 3) exhibited lower reactivity or more resistance to CMAS than the other coating compositions of this work.