Stress corrosion cracking behavior in titanium, molybdenum, and aluminum alloys, and electrochemical kinetic studies
A series of constant displacement and constant extension rate stress corrosion cracking (SCC) tests was performed on an alpha-beta brass alloy in 1 N Na2SO4 solutions. The chosen mechanical and electrochemical conditions resulted in predominantly transgranular, cleavage-like failure at high (about 8 to 50 microns/s) average crack propagation rates. Crack arrest markings were observed on selected transgranular facets, which almost exclusively bordered regions of ductile overload failure. It is proposed that the observed crack velocities and the specific nature of the arrest mark appearance are most consistent with a cracking mechanism involving adsorption or some other interaction with a damaging environmental species.
Stress corrosion cracking of titanium alloys and aluminum alloys
Extended SPL assembly language for SCC 4700 computer
The susceptibility of Ti-6Al-4V foil to stress corrosion cracking (SCC) by methanol can be decreased by treatment of the foil with 2,4-pentanedione prior to its immersion in the corroding media. It is assumed that such treatments remove from the protective film formed on the foil by exposure to the atmosphere, certain metal ions whose oxides are more readily penetrated by the ions, Na + and Cl- or Fe(3+) and Cl-, present in the corroding media.
Stress corrosion cracking of titanium alloys
Stress corrosion cracking of titanium alloys and chloride absorption during formation of titanium oxide
Electrochemistry of freshly generated titanium surfaces and stress corrosion cracking in aqueous solutions and in molten salts
Stress corrosion cracking of titanium alloys, velocity of cracking in aqueous and methanol solutions and halogenated organic solvents, concentration of TiCl3 in cracks
The variables studied in the stress-corrosion cracking performance of high strength aluminum alloys were: (1) corrosiveness of the environment, (2) specimen size and stiffness of the stressing system, (3) interpretation of transgranular cracking, and (4) interaction of the state of stress and specimen orientation in a product with an anisotropic grain structure. It was shown that the probability of failure and time to fracture for a specimen loaded in direct tension are influenced by corrosion pattern, the stressing assembly stiffness, and the notch tensile strength of the alloy. Results demonstrate that the combination of a normal tension stress and a shear stress acting on the plane of maximum susceptibility in a product with a highly directional grain cause the greatest tendency for stress-corrosion cracking.
The increasing amount of telemetry parameters and the increasing complexity of procedures used for the in-orbit satellite follow-up has led to the development of new tools for telemetry monitoring and procedures performing. The name of the system presented here is Graphic Server. It provides an advanced graphic representation of the satellite subsystems, including real-time telemetry and alarm displaying, and a powerful help for decision making with on line contingency procedures. Used for 2.5 years at the TELECOM S.C.C. for procedure performing, it has become an essential part of the S.C.C.
In April 2009, NASA Glenn Research Center (GRC) formed an integrated product team (IPT) to develop a Small Radioisotope Power System (SRPS) utilizing a single Advanced Stirling Convertor (ASC) with passive balancer. A single ASC produces approximately 80 We making this system advantageous for small distributed lunar science stations. The IPT consists of Sunpower, Inc., to provide the single ASC with a passive balancer, The Johns Hopkins University Applied Physics Laboratory (JHUAPL) to design an engineering model Single Convertor Controller (SCC) for an ASC with a passive balancer, and NASA GRC to provide technical support to these tasks and to develop a simulated lunar lander test stand. The single ASC with a passive balancer, simulated lunar lander test stand, and SCC were delivered to GRC and were tested as a system. The testing sequence at GRC included SCC fault tolerance, integration, electromagnetic interference (EMI), vibration, and extended operation testing. The SCC fault tolerance test characterized the SCCs ability to handle various fault conditions, including high or low bus power consumption, total open load or short circuit, and replacing a failed SCC card while the backup maintains control of the ASC. The integrated test characterized the behavior of the system across a range of operating conditions, including variations in cold-end temperature and piston amplitude, including the emitted vibration to both the sensors on the lunar lander and the lunar surface. The EMI test characterized the AC and DC magnetic and electric fields emitted by the SCC and single ASC. The vibration test confirms the SCCs ability to control the single ASC during launch. The extended operation test allows data to be collected over a period of thousands of hours to obtain long term performance data of the ASC with a passive balancer and the SCC. This paper will discuss the results of each of these tests.
Summary information is included for electrochemical aspects of stress corrosion cracking in alloy 2090 and an introduction to the work to be initiated on the new X2095 (Weldalite) alloy system. Stress corrosion cracking (SCC) was studied in both S-T and L-T orientations in alloy 2090. A constant load TTF test was performed in several environments with a potentiostatically applied potential. In the same environments the electrochemical behavior of phases found along subgrain boundaries was assessed. It was found that rapid failure due to SCC occurred when the following criteria was met: E(sub BR,T1) is less than E(sub applied) is less than E(sub Br, matrix phase). Although the L-T orientation is usually considered more resistant to SCC, failures in this orientation occurred when the stated criteria was met. This may be due to the relatively isotropic geometry of the subgrains which measure approximately 12 to 25 microns in diameters. Initial studies of alloy X2095 includes electrochemical characterization of three compositional variations each at three temperatures. The role of T(sub 1) dissolution in SCC behavior is addressed using techniques similar to those used in the research of 2090 described. SCC susceptibility is also studied using alternate immersion facilities at Reynolds Metals Corporation. Pitting is investigated in terms of stability, role of precipitate phases and constituent particles, and as initiation sites for SCC. In all research endeavors, attempts are made to link electrochemistry to microstructure. Previous work on 2090 provides a convenient basis for comparison since both alloys contain T(sub 1) precipitates but with different distributions. In 2090 T(sub 1) forms preferentially on subgrain boundaries whereas in X2095 the microstructure appears to be more homogeneous with finer T(sub 1) particles. Another point for comparison is the delta prime strengthening phase found in 2090 but absent in X2095.
In the light of research material published up to May 1970, the current understanding of the experimental variables involved in the stress-corrosion cracking (SCC) behavior of titanium and its alloys is reviewed. Following a brief summary of the metallurgy and electrochemistry of titanium alloys, the mechanical, electrochemical, and metallurgical parameters influencing SCC behavior are explored with emphasis on crack growth kinetics. Macro- and microfeatures of fractures are examined, and it is shown that many transgranular SCC failures exhibit morphological and crystallographic features similar to mechanical cleavage failures. Current SCC models are reviewed with respect to their ability to explain the observed SCC behavior of titanium and its alloys. Possible methods for eliminating or minimizing stress corrosion hazards in titanium or titanium alloy components are described.
The stress corrosion cracking (SCC) resistance of 18Ni maraging steel (grades 200, 250, 300, and 350) was determined in 3.5 percent salt (NaCl) solution, synthetic sea water, high humidity, and outside MSFC atmosphere. All grades of the maraging steel were found to be susceptible to SCC in varying degrees according to their strengths, with the lowest strength steel (grade 200) being the least susceptible and the highest strength steel (grade 350), the most susceptible to SCC. The SCC resistance of 250 grade maraging steel was also evaluated in salt and salt-chromate solutions using fracture mechanics techniques. The threshold value, K sub SCC, was found to be approximately 44 MN/sq m square root m, (40 ksi square root in.) or 40 percent of the K sub Q value.
The sustained load stress corrosion cracking (SCC) threshold for aluminum alloy 214 was determined using smooth (sigma sub TH) and precracked (K sub ISCC) specimens, and cyclic load growth behavior in 3.5% NaCl salt solution was studied. The relationship between K sub ISCC and sigma sub TH was also studied. The work showed that 2124-T851 aluminum alloy in plate gage has a moderately high resistance to stress corrosion attack. Experimental results showed that no SCC occurred in the longitudinal and long transverse directions in any of the tests. Some SCC was found by smooth tests in the short transverse direction, and the data were confirmed by two test methods-sigma sub TH = 275 MN/sq m (40 ksi). No SCC was found from compact specimen tests in any direction: surface flaw and center notch specimens evaluated in the short transverse direction exhibited SCC. The data indicate that stress corrosion behavior is defect, size, and stress dependent, but not entirely in accordance with a stress intensity controlled mechanism.
Examinations of the inside surface of irradiated fuel cladding from two reactors show the Zircaloy cladding is exposed to a number of aggressive substances, among them iodine, cadmium, and iron-contaminated cesium. Iodine-induced stress corrosion cracking (SCC) of well characterized samples of Zircaloy sheet and tubing was studied. Results indicate that a threshold stress must be exceeded for iodine SCC to occur. The existence of a threshold stress indicates that crack formation probably is the key step in iodine SCC. Investigation of the crack formation process showed that the cracks responsible for SCC failure nucleated at locations in the metal surface that contained higher than average concentrations of alloying elements and impurities. A four-stage model of iodine SCC is proposed based on the experimental results and the relevance of the observations to pellet cladding interaction failures is discussed.
Detailed destructive examinations were conducted to characterize the integrity and material properties of two aluminum alloy (7075-T6) horizontal stabilizer tie box forgings removed.from US. Air Force C5A and C5B transport aircraft. The C5B tie box forging was,found to contain no evidence of cracking. Thirteen cracks were found in the CSA,forging. All but one of the cracks observed in the C5A component were located along the top cap region (one crack was located in the bottom cap region). The cracks in the C5A component initiated at fastener holes and propagated along a highly tunneled intergranular crack path. The tunneled crack growth configuration is a likelv result of surface compressive stress produced during peening of the .forging suijace. The tie box forging ,fatigue crack growth, fracture and stress corrosion cracking (SCC) properties were characterized. Reported herein are the results of laboratory air ,fatigue crack growth tests and 95% relative humidity SCC tests conducted using specimens machined from the C5A ,forging. SCC test results revealed that the C5A ,forging material was susceptible to intergranular environmental assisted cracking: the C5A forging material exhibited a SCC crack-tip stress-intensity factor threshold of less than 6 MPadn. Fracture toughness tests revealed that the C5A forging material exhibited a fracture toughness that was 25% less than the C5B forging. The C5A forging exhibited rapid laboratory air fatigue crack growth rates having a threshold crack-tip stress-intensity factor range of less than 0.8 MPa sup m. Detailed fractographic examinations revealed that the ,fatigue crack intergranular growth crack path was similar to the cracking observed in the C5A tie box forging. Because both fatigue crack propagation and SCC exhibit similar intergranular crack path behavior, the damage mechanism resulting in multi-site cracking of tie box forgings cannot be determined unless local cyclic stresses can be quantified.