NASA NTRS1976

High modulus rare earth and beryllium containing silicate glass compositions

Glass compositions having a Young's modulus of at least 16 million psi and a specific modulus of at least 110 million inches consisting essentially of approximately, by weight, 20 to 43% SiO2, 8 to 21% Al2O3, 4 to 10% BeO, 27 to 58% of at least one oxide selected from a first group consisting of Y2O3, La2O3, Nd2O3, Ce2O3, Ce2O3, and the mixed rare earth oxides, and 3 to 12% of at least one oxide selected from a second group consisting of MgO, ZrO2, ZnO and CaO are described. The molar ratio of BeO to the total content of the first group oxides is from 1.0 to 3.0.

Bacon, J. F.↗

NASA NTRS1993

High efficiency direct thermal to electric energy conversion from radioisotope decay using selective emitters and spectrally tuned solar cells

Thermophotovoltaic (TPV) systems are attractive possibilities for direct thermal-to-electric energy conversion, but have typically required the use of black body radiators operating at high temperatures. Recent advances in both the understanding and performance of solid rare-earth oxide selective emitters make possible the use of TPV at temperatures as low as 1200K. Both selective emitter and filter system TPV systems are feasible. However, requirements on the filter system are severe in order to attain high efficiency. A thin-film of a rare-earth oxide is one method for producing an efficient, rugged selective emitter. An efficiency of 0.14 and power density of 9.2 W/KG at 1200K is calculated for a hypothetical thin-film neodymia (Nd2O3) selective emitter TPV system that uses radioisotope decay as the thermal energy source.

Chubb, Donald L.↗

NASA NTRS2002

Failure Morphologies of Cyclically Oxidized ZrO2-Based Thermal Barrier Coatings

Advanced and baseline thermal barrier coatings (TBCs) were thermal cycle tested in air at 1163 C until delamination or spallation of the ceramic top coat. The top coat of the advanced TBC s consisted of ZrO2 with various amounts of Y2O3, Yb2O3, Gd2O3, or Nd2O3 dopants. The composition of the top coat of the baseline TBC was ZrO2-8wt.%Y2O3. All top coats were deposited by air plasma spraying. A NiCrAlY or NiCoCrAlY bond coat was deposited by low pressure plasma spraying onto a single-crystal, Ni-base superalloy. The TBC lifetime for the baseline coatings was approximately 190 cycles (45 minutes at 1163 C per cycle) while the lifetime for the advanced coatings was as high as 425 cycles. The fracture surfaces and sample cross sections were examined after TBC failure by SEM and optical microscopy, and the top coats were further examined by X-ray diffraction. These post-test studies revealed that the fracture path largely followed splat boundaries with some trans-splat fracture. However, there were no obvious distinguishing features which explained the difference in TBC lifetimes between some of the advanced and baseline coatings.

Nesbitt, James A.↗

NASA NTRS1990

Failure Morphologies of Cyclically Oxidized ZrO2-Based Thermal Barrier Coatings

Plasma-sprayed thermal barrier coatings (TBC s) were thermal cycle tested in air at 1163 C until spallation of the top coat. Each thermal cycle consisted of a 45 minute exposure at the elevated temperature followed by a 15 minute cool to ambient temperature. The TBC s consisted of a ZrO2-based top coat containing various amounts of Y2O3, and/or Yb2O3, Gd2O3, and Nd2O3 applied by air plasma spraying and an MCrAlY bond coat applied by low pressure plasma spraying. The substrate was a single-crystal, Ni-based superalloy. The time to failure of the top coat varied from tens to hundreds of thermal cycles based on composition and spray parameters. The bond coat/top coat interface morphology and sample cross sections were examined by SEM and optical microscopy. The failure morphology following the cyclic oxidation testing will be discussed in relationship to the properties of the ceramic top coats.

Nesbit, James A.↗