SEARCH · Engineering Papers

Results for “Nd(SiOs)2”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

SourceResearch connectionFrom yearThrough year

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

3 records

All sources NASA NTRS DOE OSTI

NASA NTRS1992

Tests of shock chemistry in IC 443G

Eight molecular species, in the hot dense clump IC 443G, believed to be impacted by the shock wave from the SNR IC 443, are investigated. The clump consists of two distinct regions, one relatively cool, and one hotter and denser. Region 1 contains CO, HCO(+), HCN, and CN, whose abundances may be explained either by ion-molecule chemistry, or by a D shock of 60-90 km/s, passing through a clump of about 100,000/cu cm. Region 2 gives rise to SiO, CS, SO, and H2CO, and requires an ND shock of 5-15 km/s passing through a region of about 1,000,000/cu cm. Observed fractional abundances fit ND shock models if L is about 6.6 x 10 exp 15 cm. In general, observed line widths vary inversely with derived excitation density, while centroid velocities of all species are essentially identical.

Turner, B. E.↗

NASA NTRSDate not supplied

Exploring the Effect of EBC Composition on CMAS Wetting Behavior

Rare-earth disilicate (REDS) materials are existing materials used in environmental barrier coating (EBC) for the protection of structural materials in the hot-section of turbine engines. REDS interactions with molten calcium-magnesium-aluminosilicate (CMAS) debris are of interest to understand molten CMAS attack and improve CMAS mitigation strategies. This work assesses the effect of REDS composition on CMAS wetting by investigating wetting angle, spreading, and reactivity. Freestanding atmospheric plasma spray (APS) REDS coatings (for RE = Y, La, Nd, Gd, Yb, Lu) were exposed to 10 mg of CMAS (Ca33-Mg9-Al13-Si45 in single cation mol%) in stagnant lab air at 1250C. APS YbDS was compared to a dense spark plasma sintered (SPS) phase-pure Yb2Si2O7 and a nominal 20 vol% phase-mixture of Yb 2 SiO 5 in Yb 2 Si 2 O 7 (20YbMS/YbDS). CMAS mass was held constant but specimen surface areas varied, yielding a range of loading between ~6 and 10 mg/cm2. CMAS was loaded as a cylindrical rod atop the specimen surface, polished to 4000 grit, and heated to temperature in a Linseis L74/HS/1700 heating microscope. The heating microscope measured the evolution of molten CMAS diameter, height, and contact angle. Molten CMAS diameter at 1150C and contact angle measurements after two hours of exposure at 1250C yielded a positive trend with rare-earth cation size. There was no statistically significant difference in CMAS wetting behavior between SPS YbDS and 20YbMS/YbDS. Post-exposure specimens were examined in plan view and cross-section with XRD, SEM, and EDS. CMAS spreading was cross-examined using plan view SEM, while reactivity utilized plan view XRD and cross-sectional SEM/EDS.

Clark Luckhardt↗

NASA NTRS2017

Thermochemistry of Calcium-Magnesium-Aluminum-Silicate (CMAS) and Components of Advanced Thermal and Environmental Barrier Coating Systems

There is increasing interest in the degradation mechanism studies of thermal and environmental barrier coatings (TEBCs) of gas turbines by molten CaO-MgO-Al(exp. 2)O(exp. 3)-SiO(exp. 2) CMAS). CMAS minerals are usually referred as silicon-containing sand dust and volcano ash materials that are carried by the intake air into gas turbines, e.g. in aircraft engines, and their deposits often react at high temperatures (greater than 1200 degrees C) with the engine turbine coating systems and components. The high temperature reactions causes degradation and accelerated failure of the static and rotating components of the turbine engines. We discuss some results of the reactions between the CMAS and Rare-Earth (RE = Y, Yb, Dy, Gd, Nd and Sm) - oxide stabilized ZrO(exp. 2) or HfO(exp. 2) systems, and the stability of the resulting oxides and silicates. Plasma sprayed hollow tube samples (outside diameter = 4.7 mm, wall thickness = 0.76 mm and = 26 mm height) were half filled with CMAS powder, wrapped and sealed with platinum foil, and heat treated at 1310 degrees C for 5h. Samples were characterized by differential scanning calorimetry (DSC), X-ray diffraction, and cross-section electron microscopy analysis and energy dispersive X-ray spectroscopy. It was found that CMAS penetrated the samples at the grain boundaries and dissolved the TEBC materials to form silicate phases containing the rare-earth elements. Furthermore, it was found that apatite crystalline phases were formed in the samples with total rare-earth content higher than 12 mol% in the reaction zone for the ZrO(exp. 2) system. In general, samples with the nominal compositions (30YSZ), HfO(exp. 2)-7Dy(exp. 2)O(exp. 2) and ZrO(exp. 2)-9.5Y(exp. 2)O(exp. 3)-2.25Gd(exp. 2)O(exp. 3)-2.25Yb(exp. 2)O(exp. 3) exhibited lower reactivity or more resistance to CMAS than the other coating compositions of this work.

degradation↗