Results for “Nanovesicles” | Engineering Papers

DOE OSTI2022

Stable nanovesicles formed by intrinsically planar bilayers

Quatsome nanovesicles, formed through the self-assembly of cholesterol (CHOL) and cetyltrimethylammonium bromide (CTAB) in water, have shown long-term stability in terms of size and morphology, while at the same time exhibiting high CHOL-CTAB intermolecular binding energies. We hypothesize that CHOL/CTAB quatsomes are indeed thermodynamically stable nanovesicles, and investigate the mechanism underlying their formation. A systematic study was performed to determine whether CHOL/CTAB quatsomes satisfy the experimental requisites of thermodynamically stable vesicles. Coarse-grain molecular dynamics simulations were used to investigate the molecular organization in the vesicle membrane, and the characteristics of the simulated vesicle were corroborated with experimental data obtained by cryo–electron microscopy, small- and wide-angle X-ray scattering, and multi-angle static light scattering. CHOL/CTAB quatsomes fulfill the requisites of thermodynamically stable nanovesicles, but they do not exhibit the classical membrane curvature induced by a composition asymmetry between the bilayer leaflets, like catanionic nanovesicles. Instead, CHOL/CTAB quatsomes are formed through the association of intrinsically planar bilayers in a faceted vesicle with defects, indicating that distortions in the organization and orientation of molecules can play a major role in the formation of thermodynamically stable nanovesicles.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2024

The effect of low temperature on poly(3-methyl- N -vinylcaprolactam)- b -poly( N -vinylpyrrolidone) diblock copolymer nanovesicles assembled from all-aqueous media

Nanosized polymeric vesicles (polymersomes) self-assembled from double hydrophilic copolymers of poly(3-methyl-N-vinylcaprolactam) n -b-poly(N-vinylpyrrolidone) m (PMVC n -b-PVPON m ) using all aqueous media are a promising platform for biomedical applications, because of their superior stability over liposomes in vivo and high loading capacity. Herein, we explored the temperature-sensitive behavior of PMVC 58 -b-PVPON 65 vesicles using transmission electron microscopy (TEM), dynamic light scattering (DLS), atomic force microscopy (AFM), and small-angle neutron scattering (SANS) in response to lowering the solution temperature from 37 to 25, 20, 14 and 4 °C. The copolymer vesicles with an average size of 350 nm at 37 °C were assembled from the diblock copolymer dissolved in aqueous solution at 4 °C. We show that while the polymersome's size gradually decreases upon the temperature decrease from 37 to 4 °C, the average shell thickness increases from 17 nm to 25 nm, respectively. SANS study revealed that the PMVC 58 -b-PVPON 65 vesicle undergoes a gradual structure evolution from a dense-shell vesicle at 37–25 °C to a highly-hydrated shell vesicle at 20–14 °C to molecular chain aggregates at 4 °C. From SANS contrast matching study, this vesicle behavior is found to be driven by the gradual rehydration of PMVC block at 37–14 °C. The shell hydration at 20–14 °C also correlated with the 4.4-fold decrease in the relative fluorescence intensity from vesicle-encapsulated fluorescent dye, indicating ~80% of the dye release within 12 hours after the vesicle exposure to 14 °C. No significant (<5%) dye release was observed for the vesicle solutions at 37–20 °C, indicating excellent cargo retention inside the vesicles. Our study provides new fundamental insights on temperature-sensitive polymer vesicles and demonstrates that the copolymer assembly into polymersomes can be achieved by decreasing a copolymer aqueous solution temperature below 14 °C followed by solution exposure to ≥20 °C. This type of all-aqueous assembly, instead of nanoprecipitation from organic solvents or solvent exchange, can be highly desirable for encapsulating a wide range of biological molecules, including proteins, peptides, and nucleic acids, into stable polymer vesicles without a need for organic solvents for dissolution of the copolymers that are amphiphilic at physiologically relevant temperatures of 20–37 °C.

36 MATERIALS SCIENCE↗