Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

6 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2025

Through-thickness fracture behavior of neutron-irradiated nuclear graphite NBG-17 Using X-ray micro-CT

Achieving precise control over crack propagation in nuclear graphite and conducting quantitative analysis remain challenging. In this study, the through-thickness fracture behavior of pristine and neutron-irradiated (700 °C, ∼7 dpa) NBG-17 nuclear graphite was investigated using split-disc testing coupled with micro-computed tomography (micro-CT). A notably lower number of micropores was observed in the neutron-irradiated specimen. The fracture toughness of neutron-irradiated NBG-17 was measured to be 1.45 MPa√m, compared to 1.17 ± 0.05 MPa√m for the pristine specimen. In both materials, cracks were found to initiate at the filler–binder interface, and often correlated with microstructural features such as pores and thermal cracks. Crack bridging and deflections emerged as the primary toughening mechanisms in both unirradiated and irradiated NBG-17. However, compared with the pristine specimen, the cracks in the neutron-irradiated specimen were more likely to grow trans granularly, resulting in less deflected crack paths. The reduced micro-porosity and strengthened filler–binder boundaries were considered to be the cause of the observed differences in crack morphologies. In conclusion, this study provides a qualitative analysis of the fracture behavior of neutron-irradiated nuclear graphite in the absence of radiolytic oxidation.

36 - MATERIALS SCIENCE↗
DOE OSTI2025

HDG-1 Graphite Preirradiation Data Package Report

This report documents all pre-irradiation examination material-property measurement data for graphite specimens that are going to be used within the first high dose graphite (HDG) -1 irradiation capsule. The two new HDG capsules signify a major change to the AGC Experiment. HDG-1 and HDG-2 will replace the last two Advanced Graphite Creep (AGC) capsules (AGC-5 and AGC-6) which were designed to irradiate graphite at the extreme upper operational temperatures for a very-high-temperature reactor (VHTR) design, 1100°C. These very high temperature AGC-5 and AGC-6 capsules have been repurposed to re-irradiated specimens (from AGC-2, AGC-3, and AGC-4) at the lower temperatures of 600°C and 800°C. HDG-1 will be irradiated at 600°C and HDG-2 will be irradiated at 800°C. By re-irradiating the previous AGC specimens a total maximum neutron dose of around 15 dpa (displacements per atom) can be achieved for all major graphite grades at irradiation temperatures of 600°C and 800°C. Specimens in the HDG-1 capsule are made up of previously irradiated specimens from the AGC-2 capsule and unirradiated specimens prepared for the now discontinued AGC-5 capsule. Utilizing the irradiated specimens, a maximum neutron dose of around 15 dpa is anticipated. These new maximum dose levels will provide irradiated material property data over a total neutron dose range of 1-15 dpa at a temperature of 600°C when combined with the previous AGC-1 and AGC-2 irradiation data. This will provide quantitative data necessary for predicting the irradiation behavior and operating performance of new nuclear graphite grades for use within high temperature reactor designs. Similar to previous AGC test trains, HDG-1 includes the major graphite grades (IG-110, NBG-17, NBG-18, PCEA, and 2114) as well as adding the very fine-grain grade IG-430 which is of interest to the Molten Salt Reactor (MSR) designs. Also new to the HDG-1 capsule are 90 smaller geometry specimens designated as pencil specimens. These specimens take up only one third the space of a standard creep size specimen. This increased number of specimens will enhance property measurement statistics because they will provide 3 times the control specimen data at a position that would otherwise only have a single measurement.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2025

Summary of Graphite Data Stored within NDMAS

The Graphite Technology Development Project provides data to support the design of graphite core components within specific reactor service conditions of the next generation of high-temperature, gas-cooled nuclear reactors. Physical, mechanical, and thermal properties of nuclear grade graphite were characterized for specimens that were unirradiated, irradiated, and irradiated under various stress conditions. The material properties include diameter, length, mass, density, compressive strength, tensile strength, flexural strength, modulus, resistivity, thermal diffusivity, and thermal expansion coefficient. Baseline graphite specimens are unirradiated from different grades (2114, IG-110, NBG-17, NBG-18, and PCEA) and different types used in different characterization tests (compressive, flexural, tensile, one-inch cylinder, and quarter-inch cylinder). The Advanced Graphite Creep (AGC) irradiation specimens are from a much larger number of grades and cylinder types (creep, piggyback, and pencil). For baseline graphite, characterization data for 7,756 specimens extracted from thirteen graphite billets were captured to the NDMAS database. For AGC experiments, four irradiation campaigns have been completed: AGC-1, AGC-2, AGC-3, and AGC-4. The ongoing HDG-1 (High-Dose Graphite) experiment, which began irradiation with Cycle 168B on August 26, 2020, includes specimens previously irradiated in AGC-2 in addition to the specimens originally destined for AGC-5.. Besides the characterization data, the AGC data includes irradiation monitoring and physics data representing the irradiation conditions of AGC specimens. Currently, all data for AGC-1, AGC-2, and AGC-3 have been captured to the NDMAS database. Only AGC-4 pre-irradiation and irradiation monitoring data have been captured, and HDG-1 pre-irradiation data are in process of being captured for unirradiated specimens. To date, a total of 38,149 material property records have been captured into NDMAS database for baseline and AGC specimens. All characterization data are qualified for use according to their perspective data verification reports. For the AGC irradiation campaigns, a total of 41,502 qualified physics calculation records were added for AGC-1, AGC-2, and AGC-3. Finally, a total of 173,698,505 AGC irradiation monitoring data records (thermocouple temperature, gas flow rate, gas pressure, gas moisture, applied load, and specimen displacement) have been captured to NDMAS; the majority of those records (~94%) are qualified data records.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2025

Analysis Of Fracture Location on Tensile Graphite Samples

The main standard for testing the ultimate tensile strength of graphite is ASTM C749. Commercial entities have raised concerns about samples breaking outside of the gauge section, particularly in the radius or head of the sample. When this occurs, the data gathered from the samples is unusable and increases the cost of testing as more samples will need to be machined. This study investigates the locations and frequency of sample breakage for four different grades of graphite using a custom-made measurement scale. The four grades include two fine-grain (2114 and IG-110) and two medium/coarse-grain (NBG-17 and PCEA). Our results show that fine-grain grades are more susceptible to breaking outside the gauge section, with almost 30% of the samples from grade 2114 breaking outside this region. Additionally, the radius being too small causes stress concentrations near the ends of the gauge section resulting in a bimodal distribution of the fracture locations.

36 - MATERIALS SCIENCE↗
DOE OSTI2025

Bayesian Calibration of Nuclear Graphite Property Models Accounting for Model Inadequacy and Impacts on Component Performance

Nuclear-grade structural graphite is extensively utilized in the core designs of various advanced nuclear reactors. In the reactor environment, graphite is subjected to prolonged exposure to extreme conditions, including high temperatures, radiation, and potentially molten salt and oxygen. Such exposure can induce several degradation mechanisms in graphite, including nonuniform volumetric strains caused by irradiation and thermal expansion, leading to stresses that may compromise the performance of graphite components. Assessing component integrity requires accurate models of graphite's thermomechanical response. This report documents the Bayesian calibration of thermomechanical properties for nuclear-grade graphite and their application to graphite component modeling and simulation using the Grizzly code. As part of this work, uncertainty-quantified models were developed for the elastic modulus, coefficient of thermal expansion, irradiation-induced dimensional change, and irradiation-induced creep for graphite grades IG-110, NBG-18, NBG-17, PCEA, and 2114. Using a hierarchical Bayesian approach, multiple experimental data sources were combined to develop Gaussian process models for the properties. Using the Kennedy O'Hagan framework, the uncertainties due to inadequacies in the model and the inherent spread in the experimental data were quantified for three different models. These uncertainty-quantified models, with a model-form correction, were subsequently applied to a coupled-physics simulation of representative graphite components, revealing that the uncertainties have a large impact on the components' deformation.

36 - MATERIALS SCIENCE↗
DOE OSTI2025

Bayesian calibration of irradiated graphite property models under high temperatures

Graphite under high temperatures and irradiation is central to advanced reactors. We develop a Bayesian calibration framework for graphite property models that explicitly represents model-data mismatch via a Gaussian-process discrepancy. The approach propagates uncertainty from parameters, experimental noise, and model form, with a hierarchical variance structure to capture group and cross-group noise. Using two predictive models across five grades (IG-110, NBG-18, PCEA, NBG-17, 2114) and four properties-irradiation-induced dimension change, creep, Young’s modulus change ratio, and coefficient of thermal expansion change ratio-we obtain average predictive-error reductions of 54%, 65%, 17%, and 17% when discrepancy is included. We illustrate engineering impact with a multiphysics model of a very-high-temperature reactor prismatic reflector brick, analyzing stresses under high fluence and temperature. Accounting for model discrepancy markedly improves predictive accuracy and provides a robust basis for reliable graphite component design in advanced reactors.

36 - MATERIALS SCIENCE↗