NASA NTRS1999

Wide Temperature Core Loss Characteristics of Transverse Magnetically Annealed Amorphous Tapes for High Frequency Aerospace Magnetics

100 kHz core loss properties of sample transverse magnetically annealed, cobalt-based amorphous and iron-based nanocrystalline tape wound magnetic cores are presented over the temperature range of -150 C to 150 C, at selected values of B(sub peak). For B-fields not close to saturation, the core loss is not sensitive to temperature in this range and is as low as seen in the best MnZn power ferrites at their optimum temperatures. Frequency resolved characteristics are given over the range of 50 kHz to 1 MHz, but at B(sub peak) = 0.1 T and 50 C only. For example, the 100 kHz specific core loss ranged from 50 - 70 mW/cubic cm for the 3 materials, when measured at 0.1 T and 50 C. This very low high frequency core loss, together with near zero saturation magnetostriction and insensitivity to rough handling, makes these amorphous ribbons strong candidates for power magnetics applications in wide temperature aerospace environments.

Niedra, Janis M.↗
NASA NTRS1999

Wide Temperature Characteristics of Transverse Magnetically Annealed Amorphous Tapes for High Frequency Aerospace Magnetics

100 kHz core loss and magnetization properties of sample transverse magnetically annealed, cobalt-based amorphous and iron-based nanocrystalline tape wound magnetic cores are presented over the temperature range of -150 to 150 C, at selected values of B(sub peak). For B-fields not close to saturation, the core loss is not sensitive to temperature in this range and is as low as seen in the best MnZn power ferrites at their optimum temperatures. Frequency resolved characteristics are given over the range of 50 kHz to 1 MHz, at B(sub peak) = 0.1 T and 50 C only. A linear permeability model is used to interpret and present the magnetization characteristics and several figures of merit applicable to inductor materials arc reviewed. This linear modeling shows that, due to their high permeabilities, these cores must he gapped in order to make up high Q or high current inductors. However, they should serve well, as is, for high frequency, anti ratcheting transformer applications.

Niedra, Janis M.↗
NASA NTRS1999

Comparative Wide Temperature Core Loss Characteristics of Two Candidate Ferrites for the NASA/TRW 1500 W PEBB Converter

High frequency core loss and magnetization properties of commercial type MN8CX and PC40, high resistivity, MnZn based, power ferrites are presented over the temperature range of -l50 C to 150 C, at selected values of peak flux density (B (sub p)). Most of the data is at 100 kHz, with some data extended to 200 and 300 kHz for the MN8CX. Plots of the specific Core loss against temperature exhibit the minimal characteristic of such ferrites. These plots show that the MN8CX is optimized for minimum loss at about 25 C, whereas the PC40 is optimized at about 80 C. At the points of minimum loss and for the same B (sub p), the MN8CX has roughly half the losses of the PC40 at the lower flux densities. This loss ratio continues down to cryogenic temperatures. However, above about 80 C the losses are practically equal. The lowest 100 kHz loss recorded, 50 mW/cm3 for the MNGCX at a B (sub p) of 0.1T, equals that of a very low loss, Co based, transverse magnetically annealed, amorphous ribbon material. Except possibly at lower B (sub p) or much higher frequencies, these ferrites are not competitive for low losses over a wide temperature range with certain specialty amorphous materials. Permeability is computed from a linear model, plots against temperature are presented and again compared to the specialty amorphous materials.

Niedra, Janis M.↗