Transition metal oxides are promising materials as cathodes for divalent batteries with high capacity under high voltage. A major challenge is the sluggish kinetics of intercalation of divalent cations into the oxide host. Tailoring of the size, composition and crystal structure of oxides is a necessary strategy to alleviate these barriers, which challenges our control of their synthesis. In this work, we selectively synthesize spinel-type Mg x Mn 3-x O 4 nanocrystals with different Mg/Mn ratios and investigate their ability to electrochemically shuttle Mg 2+ ions. Crystal-chemical characterization of the reaction outcomes was conducted with X-ray diffraction, X-ray absorption spectroscopy, electron microscopy, and elemental analysis. Both 5 nm thick MgMn 2 O 4 nanosheets and 10 nm Mg 0.41 Mn 2.59 O 4 nanocubes underwent reversible Mg 2+ deintercalation, yet no obvious reaction was observed in 60 nm Mg 1.2 Mn 1.8 O 4 nanocubes. Our results suggest that both the size of the spinel nanocrystals and the Mg/Mn ratios play a role in the observed behaviour. The advances in the synthesis of spinel oxide nanocrystals achieved, and their correlation with Mg 2+ deintercalation, pave the way toward the precise synthesis of multivalent cathode materials that fundamentally overcome barriers to practical application.
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗