DOE OSTI2024

Pressureless sintering of lithium hydride

Lithium Hydride is a material of growing importance for addressing technological challenges related to nuclear fusion, long-term human space travel, and thermal energy storage. Pressureless sintering provides a straightforward, scalable approach to produce dense LiH parts of all sizes and shapes. Pressed LiH green compacts were sintered at heating rates from 2.5 to 20 °C/min to 650 °C, yielding densities up to 96 ± 1.4 %, with densification initiating at 500 °C. Here, a validated master sintering curve was constructed with a sintering apparent activation energy of 135 kJ/mol. X-ray diffraction and simultaneous thermal analysis revealed Li 2 O formation from 300 – 550 °C and decomposition of LiH into Li metal at 550 °C, each reflected as deviations in the master sintering curve. Computed tomography after thermal treatment to 550 °C showed the formation of corrosion products, and after thermal treatment to 650 °C LiH reduction to Li most significantly at exposed surfaces.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Spark plasma sintering of fuel meats for U 3 O 8 based dispersion fuels

Research and test reactors often use dispersion-type fuel due to its increased thermal conductivity and burn-up capabilities compared to conventional fuel. Al-U 3 O 8 (aluminumtriuranium octaoxide) dispersion fuels have several advantages over their competitors, such as higher service temperature and better stability of oxygen stoichiometry. However, the two-step fabrication of dispersion fuel causes undesirable porosity in cold-pressed fuel meats that is preserved in co-extruded fuel plates. To combat this, spark plasma sintering (SPS) was used for the fabrication of Al-15, 20, and 30 vol% U 3 O 8 and 8 and 12 vol% Mo-U 3 O 8 fuel meats for the Al-U 3 O 8 time. The in situ SPS data was used to construct and validate Master Sintering Curves (MSCs) with accuracies in Al fuels at 0.02 g/cm 3 , and Mo fuels at 0.07 and 0.17 g/cm 3 . The as-sintered fuel meats were characterised using x-ray diffraction (XRD) and scanning electron microscopy (SEM) to understand chemical and physical changes following the SPS process. The pellets exhibited very high relative densities, the U 3 O 8 was observed to undergo reduction to UO 2 .

Aluminium↗
DOE OSTI2021

Controlled current-rate AC flash sintering of uranium dioxide

Uranium dioxide (UO2) pellets with controlled microstructures were densified up to 93.4% of their theoretical density in less than 25 minutes at a furnace temperature of 873 K, utilizing controlled current-rate alternating current (AC) flash sintering (FS). Using this AC-FS method it was possible to control the sintering rate and thermal gradients, resulting in dense pellets with no appreciable hourglassing and good mechanical integrity. Moreover, the apparent sintering activation energy for FS and for conventionally sintered samples was estimated to be 108 kJ mol -1 and 380 kJ mol -1 , respectively using the master sintering curve method. The apparent activation energy for FS was remarkably close to those reported in the literature for spark plasma sintering of UO 2 . Furthermore, both these field assisted sintering methods utilize fast heating rates and electrical effects that are likely enhancing the grain boundary diffusion mechanism. Finally controlled current-rate AC-FS has been demonstrated as a technological advancement, capable of producing ceramic nuclear fuels in a fraction of the conventional processing time.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2020

Ultra–fast, selective, non–melting, laser sintering of alumina with anisotropic and size–suppressed grains

In this paper, we report an ultra-fast sintering phenomenon of alumina achieved by the scanning laser irradiation method. Using CO 2 laser irradiation, we found that micrometer-sized alumina powder (d 50 = 1.2 µm) can be sintered close to full density within a few tens of seconds. The microstructure of laser-sintered alumina was different from that of the furnace-sintered alumina. The relative density and grain size of the laser-sintered alumina gradually decreased from the center of the laser beam to the edge. Anisotropy of the grain size was measured along and perpendicular to the scanning direction. This anisotropy decreased as the scanning speed decreased from 0.1 mm/s to 0.01 mm/s. The sintering master curve of grain size versus relative density, which reflects the sintering mechanism, was found to be affected by the laser scanning speed. When the laser scanning speed was 0.1 mm/s, grain size suppression was found for the almost fully dense alumina. However, at lower scanning speed (e.g., 0.01 mm/s), there was significant grain growth in the regions where the relative density was greater than 90%. Furthermore, these results clearly indicate that alumina can be sintered, in the solid-state, to a high density in a short time using scanning laser and the microstructure is different from the furnace-sintered alumina.

08 HYDROGEN↗