Li2O-Based Cathode Additives Enabling Prelithiation of Si Anodes
Low first-cycle Coulombic efficiency is especially poor for silicon (Si)-based anodes due to the high surface area of the Si-active material and extensive electrolyte decomposition during the initial cycles forming the solid electrolyte interphase (SEI). Therefore, developing successful prelithiation methods will greatly benefit the development of lithium-ion batteries (LiBs) utilizing Si anodes. In pursuit of this goal, in this study, lithium oxide (Li2O) was added to a LiNi0.6Mn0.2Co0.2O2 (NMC622) cathode using a scalable ball-milling approach to compensate for the initial Li loss at the anode. Different milling conditions were tested to evaluate the impact of particle morphology on the additive performance. In addition, Co3O4, a well-known oxygen evolution reaction catalyst, was introduced to facilitate the activation of Li2O. The Li2O + Co3O4 additives successfully delivered an additional capacity of 1116 mAh/gLi2O when charged up to 4.3 V in half cells and 1035 mAh/gLi2O when charged up to 4.1 V in full cells using Si anodes.
Electrolytic Reduction of Titanium Dioxide in Molten LiCl–Li2O
The electrolytic reduction of TiO2 in LiCl–Li2O (1 wt.%) at 650 °C was investigated under a series of cathodic reduction potentials and applied charges to provide a mechanistic understanding of the electrochemical characteristics of the system. The optimal cathodic reduction potential was determined as being −0.3 V vs. Li/Li+. Li2TiO3 and LiTiO2 were structurally identified as intermediate and partial reduction products of the TiO2 electrolytic reduction. The reduction of LiTiO2 was extremely slow and reversible due to its high stability and the detrimental effect of Li2O accumulation within the solid particles. The most reduced product obtained in this study was LiTiO2, which was achieved when using 150% of the theoretical charge under the optimal reduction potential. The highest reduction extent obtained in this study was 25%. Based on theoretical DFT modeling, a detailed multistep reduction mechanism and scheme were proposed for TiO2 electrolytic reduction in LiCl–Li2O (1 wt.%) at 650 °C.
Materials Data on Li2O by Materials Project
Li2O is Fluorite structured and crystallizes in the cubic Fm-3m space group. The structure is three-dimensional. Li1+ is bonded to four equivalent O2- atoms to form a mixture of corner and edge-sharing LiO4 tetrahedra. All Li–O bond lengths are 2.02 Å. O2- is bonded in a body-centered cubic geometry to eight equivalent Li1+ atoms.
Materials Data on Li2O by Materials Project
Li2O is Cotunnite structured and crystallizes in the orthorhombic Pnma space group. The structure is three-dimensional. there are two inequivalent Li1+ sites. In the first Li1+ site, Li1+ is bonded in a 3-coordinate geometry to five equivalent O2- atoms. There are a spread of Li–O bond distances ranging from 1.98–2.44 Å. In the second Li1+ site, Li1+ is bonded to four equivalent O2- atoms to form a mixture of edge and corner-sharing LiO4 tetrahedra. There is three shorter (1.98 Å) and one longer (2.00 Å) Li–O bond length. O2- is bonded in a 9-coordinate geometry to nine Li1+ atoms.
Evolution and interplay of lithium metal interphase components revealed by experimental and theoretical studies
ABSTRACT: Lithium metal batteries (LMB) have high energy densities and are crucial for clean energy solutions. The characterization of lithium metal interphase is fundamentally and practically important but technically challenging. Taking advantage of synchrotron x-ray which has the unique capability of analyzing crystalline/amorphous phases quantitative-ly with statistical significance, we study the composition and dynamics of LMB interphase for a newly developed im-portant LMB electrolyte that is based on fluorinated ether. Pair distribution function analysis revealed the sequential role of anion and solvent in interphase formation during cycling. The relative ratio between Li2O and LiF first increases and then decreases during cycling, suggesting suppressed Li2O formation in both initial and long extended cycles. Theoretical studies revealed that in initial cycles, this is due to the energy barrier in many-electron transfer. In long extended cycles, the anion decomposition product Li2O encourages solvent decomposition by facilitating solvent adsorption on Li2O which is followed by concurrent depletion of both. This work highlights the important role of Li2O in transitioning from anion-derived interphase to a solvent-derived one.
Synthesis, Characterization, and Testing of High-Lithium-Density Composite Breeders
Solid tritium breeder materials must first and foremost have sufficiently high concentrations of lithium to enable a plant-scale tritium breeding ratio greater than 1:1. However, in addition to lithium content, such breeder materials must also meet other performance metrics including high tritium release rates, thermal conductivities, and irradiation damage tolerance. Perhaps most importantly, tritium breeders must maintain their mechanical integrity during reactor operation so as to avoid degradation which can jeopardize the functionality of the tritium breeder blanket module, which in most designs takes the form of a pebble bed geometry. Unfortunately, the mechanical robustness of most lithium-bearing ceramics under investigation for fusion applications is often inversely related to the lithium atom density. For example, a material such as lithium oxide (Li2O), which has one of the highest lithium atom densities, has a much lower mechanical splitting strength than lithium metatitanate (Li2TiO3), though Li2TiO3 has less than half the lithium atom density of Li2O. This work seeks to provide an alternative to monolithic ceramic tritium breeders, in the form of metal-reinforced composite tritium breeders. Specifically, composite tritium breeders have been synthesized combining Li2O with various ferrous metal reinforcements via electric field assisted sintering (EFAS), also known as spark plasma sintering (SPS). As the metal reinforcement content is increased, metallic networks are observed, via electron microscopy and X-ray computed tomography, to form throughout the composite material. Through destructive mechanical testing, even dilute metal reinforcement loading enables drastic mechanical strength improvements over pure Li2O while higher loadings give rise to quasi-ductile behavior and higher ultimate strengths than Li2TiO3 – while still maintaining a higher density of lithium atoms than Li2TiO3 and many other breeder candidates. In addition to microstructural characterization and mechanical testing, thermal property measurements and hydrogen permeability testing are underway to further assess the suitability of such composites for fusion reactor applications.
Molten Salt Synthesis of Increased (100)-Facet and Polycrystalline Nickel Oxide Nanoparticles for the Oxygen Evolution Reaction: Impact of Facet and Crystallinity on Electrocatalysis
Nickel oxide nanocubes with increased (100) surface facet presence (NiO(100)) were synthesized through a molten salt synthesis procedure to probe their oxygen evolution reaction (OER) activity in order to investigate the relationship between the surface facet and OER performance. While altering the synthesis parameters to decrease NiO(100) particle sizes and agglomeration, a polycrystalline NiO nanoparticle system formed from using Li2O as a Lux-Flood base (labelled Li2O-MSS NiO, where MSS stands for molten salt synthesis). This novel synthesis was further elaborated and the obtained materials were also tested for OER activity. After thorough structural characterization to determine crystallinity, lattice spacings, and elemental distribution, their OER activity was compared versus high surface area NiO(111) nanosheets in a three-electrode rotating disk electrode (RDE) system. The activity trend of (111) > Li2O-MSS > (100) was observed. This decrease in activity of the nanocube and polycrystalline samples was explained by differences between theoretical and experimental conditions, differences in ink rheology and resulting catalyst layer properties, and significant agglomeration seen in the imaging of the sample. Methods for improving the OER activity of these samples are discussed in the conclusion of this study.
Elucidating the Effects of LiF on Lithium Metal Anodes
LiF is widely recognized as a crucial component of a solid-electrolyte interphase (SEI) for Li metal anodes. However, the roles of LiF in the SEI remain elusive. Herein, we examined the evolution of SEI influenced by LiF and identified distinct features that elucidate functional characteristics of LiF for Li metal anodes. Through comprehensive empirical and theoretical analyses, we found that LiF enriches Li2O within the SEI, forms LiF/Li2O interfaces, exhibits non-negligible solubility with spontaneous dissolution-reprecipitation behavior in the electrolyte, and works synergistically with Li2O. These findings shed light on the effects of LiF on Li metal anodes and the arrangement characteristic of LiF within the SEI. By integrating key discoveries regarding LiF, a projected working mechanism for LiF is illustrated. Overall, our study on LiF provides valuable insights that advance the understanding of the SEI and interphase nanostructures, contributing to the development of more reliable and practical Li metal batteries.
Unraveling the convoluted and dynamic interphasial mechanisms on Li metal anode
Accurate understanding of the chemistry of solid-electrolyte interphase (SEI) is key to developing new electrolytes for high-energy batteries using lithium metal (Li-0) anodes(1). SEI is generally believed to be formed by the reactions between Li-0 and electrolyte(2,3). However, our new study shows this is not the whole story. Through synchrotron-based X-ray diffraction and pair distribution function analysis, we reveal a much more convoluted formation mechanism of SEI, which receives considerable contributions from electrolyte, cathode, moisture and native surface species on Li-0, with highly dynamic nature during cycling. Using isotope labelling, we traced the origin of LiH to electrolyte solvent, moisture and a new source: the native surface species (LiOH) on pristine Li-0. When lithium accessibility is very limited as in the case of anode-free cells, LiOH develops into plate-shaped large crystals during cycling. Alternatively, when the lithium source is abundant, as in the case of Li||NMC811 cells, LiOH reacts with Li-0 to form LiH and Li2O. While the desired anion-derived LiF-rich SEI is typically found in the concentrated electrolytes or their derivatives, we found it can also be formed in low-concentration electrolyte via the crosstalk effect, emphasizing the importance of formation cycle protocol and opening up opportunities for low-cost electrolyte development.
Implanting Transition Metal into Li 2 O-Based Cathode Prelithiation Agent for High-Energy-Density and Long-Life Li-Ion Batteries
Compensating the irreversible loss of limited active lithium (Li) is essentially important for improving the energy-density and cycle-life of practical Li-ion battery full-cell, especially after employing high-capacity but low initial coulombic efficiency anode candidates. Introducing prelithiation agent can provide additional Li source for such compensation. Herein, we precisely implant trace Co (extracted from transition metal oxide) into the Li site of Li 2 O, obtaining (Li 0.66 Co 0.11$\square$0.23 ) 2 O (CLO) cathode prelithiation agent. Further, the synergistic formation of Li vacancies and Co-derived catalysis efficiently enhance the inherent conductivity and weaken the Li-O interaction of Li 2 O, which facilitates its anionic oxidation to peroxo/superoxo species and gaseous O 2 , achieving 1642.7 mAh/g ~Li2O prelithiation capacity (≈980 mAh/g for prelithiation agent). Coupled 6.5 wt % CLO-based prelithiation agent with LiCoO 2 cathode, substantial additional Li source stored within CLO is efficiently released to compensate the Li consumption on the SiO/C anode, achieving 270 Wh/kg pouch-type full-cell with 92 % capacity retention after 1000 cycles.
Understanding a novel form of intergranular corrosion of stainless steel 316L exposed to molten LiCl-Li 2 O-Li
We report stainless steel 316 L exposed to LiCl-Li2O molten salt containing Li metal for 500 and 1000 h experiences deep intergranular attack and bulk void formation. This degradation is due to a synergistic corrosion mechanism, different than other forms of molten salt corrosion, where Cr and Mn oxides and carbides form along grain boundaries and are dissolved by Li metal. Synchrotron transmission X-ray microscopy 3D imaging is used to show corrosion morphology and Cr enrichment and depletion in a novel format that has not previously been used for bulk corrosion samples.
Long cycle and calendar life of Si-based Li-ion batteries enabled by localized high-concentration electrolytes and their surprising water tolerance
Silicon-based anodes promise an increase in energy density for Li-ion batteries, yet they suffer from a poor calendar life. Researchers have posited that fluorinated lithium salt forms reactive side products that destroy the solid electrolyte interphase (SEI), even without cycling. HF is one such reactive side product formed from trace water contamination in the electrolyte. Some electrolytes, such as localized high concentration electrolytes (LHCEs) may improve cell stability in highly reactive systems, such as Li metal and Si. In the present study, LHCEs containing 200-300 ppm of water retained up to 8% greater capacity (1200-1300 mAh/g Si) in calendar life tests over 200 days compared to dried electrolytes (< 20 ppm water). Calendar aging took place at 100% state of charge. Cells with 200-300 ppm water performed comparably to cells with 20 ppm water in cycle life tests (900-1000 mAh/g Si) . Even adding 1000 ppm water did not lead to rapid capacity fade in cells undergoing cycle life tests. Nano-FTIR spectroscopy revealed chemical and structural differences in the SEI for cells with 1000 ppm water compared to 200-300 ppm water. The SEI differences, including increased Li2O concentration, may have contributed to improved calendar life. This research reveals the capabilities of LHCEs to improve the calendar and cycle life of Si-based Li-ion batteries, despite the presence of a highly reactive contaminant.
A multiscale model to understand the interface chemistry, contacts, and dynamics during lithium stripping
A reversible Li-metal electrode, paired with a solid electrolyte, is critical for attaining higher energy density and safer batteries beyond the current lithium-ion cells. A stable stripping process may be even harder to attain as the stripping process will remove Li-atoms from the surface, and naturally reduce surface contact area, if not self-corrected by other mechanisms, such as diffusion and plastic deformation under an applied external stack pressure. Here, we capture these mechanisms occurring at multiple length- and time- scales, i.e., interface interactions, vacancy hopping, and plastic deformation, by integrating density functional theory (DFT) simulations, kinetic Monte Carlo (KMC), and continuum finite element method (FEM). By assuming the self-affine nature of multiscale contacts, we predict the steady-state contact area as a function of stripping current density, interface wettability, and stack pressure. We further estimate the exponential increase of overpotential due to contact area loss to maintain the same stripping current density. We demonstrate that a lithiophilic interface requires less stack pressure to reach the same steady-state contact area fraction than a lithiophobic interface. A “tolerable steady-state” contact area loss for maintaining stable stripping is estimated at 20 %, corresponding to a 10 % increase in overpotential. To constrain contact loss within the tolerance, the required stack pressure is 0.1, 0.5, and 2 times the yield strength of lithium metal for three distinct interfaces, lithiophilic Li/lithium oxide(Li2O), Li/lithium lanthanum zirconium oxide(LLZO), and lithiophoblic Li/lithium fluoride(LiF), respectively. The modeling results agree with experiments on the impact of the stack pressure quantitatively, while the discrepancy in stripping rate sensitivity is attributed to the simplifying interface interaction in our simulations. Overall, this multiscale simulation framework demonstrates the importance of electrochemical-mechanical coupling in understanding the dynamics of the Li/SE interface during stripping.
Thermal stability of oxidized ultrathin Li films on TZM for plasma facing components
For improved understanding of the behavior of Li plasma facing components (PFCs) in the presence of oxygen impurities, we report on the thermal stability of ultrathin (up to 1.0 nm) LiO x films on a titanium-zirconium-molybdenum (TZM) alloy substrate over the temperature range of 310–1400 K. LiO x films were prepared by either post-oxidation of Li films or Li films deposited on an oxygen-precovered TZM surface. Thermal stability of these films was studied using a combination of temperature programmed desorption (TPD), X-ray photoelectron spectroscopy (XPS), and low-energy ion scattering (LEIS). For post-oxidized Li films, TPD showed that no Li desorption occurred until temperatures above 620 K, and then Li desorbed from the surface via at least three desorption peaks. The O 1s XPS spectra on the post-oxidized films at 310 K indicate the formation of lithium oxide (Li2O) and peroxide/hydroxide (Li 2 O 2 /LiOH). The peroxide/hydroxide converts to oxide after heating to 680 K with no desorption of Li or O 2 , and then this film decomposes to liberate Li into the gas phase while leaving oxygen at the TZM surface. Heating the LiO x films to 1070 K led to a solid-state reaction with surface Mo atoms of the substrate to form a condensed binary lithium molybdenum oxide (LixMoOy) phase, which upon further heating decomposed to liberate gas phase binary lithium molybdenum oxide species. Li deposition on an oxygen-precovered TZM surface formed a complex, highly stable, oxygen rich, Li-O-Mo interfacial oxide. Li desorption from multilayer Li films on oxygen-precovered TZM surfaces occurred in a metallic Li multilayer peak and three other oxide-derived peaks. These results support the improved thermal stability of oxidized lithium as compared to metallic Li and have implications for Mo impurity transport into the plasma at high temperatures.
Investigation Into LiCl-LiF+Li 2 O as a Low Temperature Electrolyte in Direct Electrolytic Reduction of UO 2
Direct electrolytic reduction (DER) of UO 2 in a binary LiCl-Li2O (1–3 wt%) at 650 °C has been widely reported. The process temperature can be reduced to 550 °C in theory by using a near eutectic ternary LiCl-LiF+Li 2O (∼2 wt%) electrolyte, which will result in substantial reduction in rate of salt vaporization. The feasibility of using the ternary electrolyte for the process was tested via material compatibility testing, electrochemical polarization testing, and controlled potential or current DER experiments. MgO, Pt, and 625 nickel samples were each contacted with the ternary salt for 168 h. Negligible changes to dimensions and mass of the samples were measured, and concentrations of corrosion products in the salt were 102 ppm or less. O2−oxidation was observed to occur at a lower potential than Cl-or F-on a Pt anode. DER of UO2was performed in six trials. Process variables included type of reference electrode, electrochemical control method, type of cathode basket, and electrolyte composition. UO 2conversion ranged from 28.2 to 99.9 % , and current efficiency ranged from 38 to 52%. Overall, results indicate that the use of the ternary salt is feasible for DER.
Understanding Solid Electrolyte Interphase Nucleation and Growth on Lithium Metal Surfaces
Experiments and theory are needed to decode the exact structure and distribution of components of a passivation layer formed at the anode surface of Li metal batteries, known as the Solid Electrolyte Interphase (SEI). Due to the inherent dynamic behavior as well as the lithium reactivity, the SEI structure and its growth mechanisms are still unclear. This study uses molecular simulation and computational chemistry tools to investigate the initial nucleation and growth dynamics of LiOH and Li2O that provide us with thermodynamics and structural information about the nucleating clusters of each species. Following the most favorable pathways for the addition of each of the components to a given nascent SEI cluster reveals their preferential nucleation mechanisms and illustrates different degrees of crystallinity and electron density distribution that are useful to understand ionic transport through SEI blocks.