Lattice defects in semiconducting Hg/1-x/Cd/x/Te alloys. I - Defect structure of undoped and copper doped Hg/0.8/Cd/0.2/Te. II - Defect structure of indium-doped Hg/0.8/Cd/0.2/Te
Hall effect and mobility measurements were conducted on undoped Hg(0.8)Cd(0.2)Te crystals which were quenched to room temperature after being subjected to equilibration at temperatures ranging from 400 to 655 C in various Hg atmospheres. The variation of the hole concentration in the cooled crystals at 77 K as a function of Hg's partial pressure at the equilibration temperature, together with a comparison of the hole mobility in the undoped samples with that in copper-doped ones, yields a defect model for the undoped crystals according to which they are intrinsic at the equilibration temperatures and the native acceptor defects are doubly ionized. In the second part of this paper, the effects of indium doping are considered. The concentration of electrons obtained in the cooled crystals was found to be lower than the intrinsic carrier concentration at the equilibration temperatures. A defect model is proposed according to which most of the indium is incorporated as In2Te3(s) dissolved in the crystal, with only a small fraction of indium acting as single donors occupying Hg lattice sites.