NASA NTRS1990

A study of void effects on the interlaminar shear strength of unidirectional graphite fiber reinforced composites

A study was conducted to evaluate the effect of voids on the interlaminar shear strength (ILSS) of a polyimide matrix composite system. The graphite/PRM-15 composite was chosen for study because of the extensive amount of experience that has been amassed in the processing of this material. Composite densities and fiber contents of more than thirty different laminates were measured along with ILSS. Void contents were calculated and the void geometry and distribution were noted using microscopic techniques such as those used in metallography. It was found that there was a good empirical correlation between ILSS and composite density. The most acceptable relationship between the ILSS and density was found to be a power equation which closely resembles theoretically derived expressions. An increase in scatter in the strength data was observed as the void content increased. In laminates with low void content, the void appears to be more segregated in one area of the laminate. It was found that void free composites could be processed in matched metal die molds at pressures greater than 1.4 and less than 6.9 MPa.

Bowles, Kenneth J.↗

DOE OSTI2022

Particulate Fuel Modeling of MC 2 -3 using Iterative Local Spatial Self-shielding Method

We report a new spatial self-shielding method for particulate fuels has been developed based on disadvantage factors and implemented in the MC 2 -3 code. This method named the iterative local spatial self-shielding (ILSS) method considers the shadowing effect of randomly distributed particles on spatial self-shielding in particles through a homogenized composition region added outside the particle of interest at the center. The self-shielded cross sections of the central particle are determined iteratively since they are used in determining the cross sections of the homogenized composition region. The ILSS method was verified for infinite stochastic medium problems of single and multiple types of particles, VHTR unit cell problems, and HTTR assembly problems. The verification test results show that the ILSS method accurately predicts the stochastic particle shadowing effect and reaction rates in particles, whereas the regular array model and the stochastic collision probability method underpredict the particle shadowing effect and overestimate reaction rates in particles.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

NASA NTRS1985

The 371 deg C mechanical properties of graphite/polyimide composites

A series of condensation polyimides based on pyromellitic dianhydride is synthesized and evaluated for potential application at 371 C. Several three-and four-ring benzenoid diamine systems containing oxygen bridging groups are investigated. Thermomechanical analysis of neat resin specimens indicate that the polyimide prepared from the dimethyl ester of pyrometallitic acid (PMDE) and 2,2-bis4-(4'-aminophenoxy) phenyl]-1,1,1,3,3,3- hexafluoropropane (BDAF) is the only resin system which has a glass transition temperature (Tg) above 371 C. The Tg of the PMDE/BDAF polyimide is found to be 390 C after a postcure air at 371 C for 24 hr. Unidirectional composites are fabricated from the PMDE/BDAF system and unsized Celion 6000 graphite fibers. Final cure temperatures in the range of 371 to 427 C with an applied pressure of 10.34 to 13.78 MPa are investigated. The void content of the composites ranges from 4.6 to 8.6 percent. Composites cured at 399 C under a pressure of 10.34 MPa and postcured in air at 371 C for 24 hr exhibit the highest 371 C interlaminar shear strength (ILSS, 40.7 MPa) and flexural strength (758 MPa). The thermo-oxidative stability of the composites is determined by subjecting specimens to isothermal exposure at 371 C in air at atmospheric pressure, as well as a pressure of 0.52 MPa. Specimens exposed at atmospheric pressure exhibit a weight loss of 12 percent after 200 hr of exposure and 88 percent retention of its original 371 C ILSS. In contrast, the specimens exposed at 0.52 MPa pressure exhibit a comparable weight loss after only 72 hr, and a 71 percent retention of its original 371 C ILSS.

Delvigs, P.↗

NASA NTRS1988

Halogenation Enhances Carbon-Fiber/Epoxy Composites

Interlaminar shear strength increased by inexpensive treatment. New surface treatment for carbon fibers enhances interlaminar shear strength, ILSS, without altering tensile strength significantly. Exposure of polyacrylonitrile-based T-300, or equivalent, fibers to bromine vapor at room temperature improves ILSS of epoxy composites made from these fibers by 30 percent. Enhanced ILSS obtained from halogenation of carbon fibers beneficial in many aerospace and terrestrial applications.

Jaworske, Donald A.↗

NASA NTRS1992

Void effects on the interlaminar shear strength of unidirectional graphite-fiber-reinforced composites

A study was conducted to evaluate the effect of voids on the interlaminar shear strength (ILSS) of a polyimide matrix composite system. The graphite/PMR-15 composite was chosen for study because of the extensive amount of experience that has been amassed in the processing of this material. Void contents were calculated and the void geometry and distribution were noted using microscope techniques such as those used in metallography. A good empirical correlation between ILSS and composite density was found. The most acceptable relationship between the ILSS and density was found to be a power equation that closely resembles theoretically derived expressions. It was found that void-free composites could be processed in matched metal die molds at pressures greater than 1.4 MPa and less than 6.9 MPa.

Bowles, Kenneth J.↗

DOE OSTI2022

Interlaminar improvement of carbon fiber/epoxy composites via fluorine‐containing high‐epoxy‐value sizing agent

Abstract To improve the interfacial bonding effect of carbon fibers (CFs) and epoxy resins, we prepared a fluorine‐containing high‐epoxy‐value sizing agent (named TS) in this article. It is an emulsion with a more uniform particle size distribution and higher stability better than a commercial Takemoto sizing agent. In addition, sulfonic acid groups can improve the hydrophilicity of the TS, and the presence of epoxy groups enhances the wettability between CFs and the matrix. The properties of the sizing agents were examined by Fourier transform infrared spectroscopy, dynamic light scattering, and thermogravimetric analysis. The sized CFs were evaluated by scanning electron microscopy, x‐ray photoelectron spectroscopy, monofilament tensile test, and dynamic contact angle. Afterward, CF/epoxy composites were prepared, and their fracture morphology and interlaminar shear strength (ILSS) were examined. Results indicated that the TS sizing significantly increased the content of activated carbon on the surface of the CFs and improved the bonding effect between the fiber and the matrix. After TS was sized, the ILSS increased from 49.64 to 58.74 MPa, 18.34% higher than unsized CF/epoxy composites, showing the prominent interfacial reinforcement better than commercial Takemoto.

Qiu, Zhijie↗

DOE OSTI2025

Enhanced Interfacial Strength in Carbon Fiber Composites via Mussel‐Inspired Sizing Polymers

Composite materials possess a high strength-to-weight ratio. A key determinant of their mechanical performance is the interfacial strength between the fibers and the matrix. Sizing agents are commonly used to improve this interface by promoting better adhesion, though optimizing this interaction remains a significant challenge. Here, this study evaluates the use of poly(catechol-styrene) (PCS), a mussel-inspired sizing agent, to enhance fiber–matrix bonding in carbon fiber composites. Woven carbon fiber laminates were dip-coated with varying concentrations of PCS (0.05 and 0.1 wt%) and subsequently fabricated using vacuum-assisted resin transfer molding followed by compression molding. Interlaminar shear strength (ILSS) tests showed improvements of 4% and 8% for the 0.05% and 0.1% PCS treatments, respectively. These results indicate that PCS is effective in reinforcing interfacial adhesion, thereby improving the mechanical integrity of carbon fiber-reinforced composites.

Carbon fiber composites↗

DOE OSTI2025

Influence of sizing concentration on strength, stiffness, and porosity in textile grade carbon fiber (TCF)-Epoxy composites: Revealing inverse trends

The effect of fiber sizing (i.e., surface treatment) concentration (0 %, 1.36 %, 1.52 %, 1.94 %, and 2.13 %) on the mechanical properties (tensile, flexural, interlaminar shear strength (ILSS), and low velocity impact) of textile grade carbon fiber (TCF)-epoxy composite is examined. An inverse relationship between the strength and stiffness of the composite is observed with increased sizing concentration. The root mean square (RMS) roughness of the fiber surface increased from 17.8 nm (unsized) to 22.7 nm with 2.13 % sizing concentration. It was found that the tensile strength increased by 131 % from 221.4 ± 18.5 MPa (unsized) to 510.8 ± 28.05 MPa (for 1.36 % sizing) and further by 155 %–563.7 ± 14.95 MPa at 2.13 % sizing. On the contrary, the stiffness is initially increased by 126 % from 33.52 ± 7.80 GPa (unsized) to 75.9 ± 3.21 GPa (for 1.36 % sizing) but reduced with further increase in the sizing concentration. A single fiber pull-out test is simulated using the finite element method to validate the reverse trend in strength and stiffness. The varying sizing concentration is simulated by introducing an interface of varying thickness between fibers and matrix. Simulation results confirm that a thicker interface, corresponding to a higher sizing concentration, decreases interfacial shear stress, enhancing material strength while decreasing stiffness. The reverse trend in strength and stiffness with the sizing concentration aligns with experimental observations. In conclusion, the present study emphasizes the importance of sizing concentration for mechanical properties and provide a design criterion for customized high-strength and high-stiffness applications.

Porosity↗

DOE OSTI2025

Sizing comingled CF/PA 6 fibers with cellulose nanofibrils for enhanced performance properties

Compatibility between the reinforcing phase and the polymer matrix is critical to achieving the desired mechanical and thermal performance of composite materials. Several mechanisms can enhance this interfacial interaction, including surface treatments (e.g., oxidation, plasma, or irradiation), in-situ nanoparticle deposition, and fiber sizing. Here, in this study, cellulose nanofibrils (CNF) were employed as a sustainable sizing agent to modify the interface in commingled carbon fiber (CF)/polyamide 6 (PA 6) yarns, in which CF and PA6 filaments are intimately blended to enable simultaneous consolidation. A 0.25 wt% CNF aqueous suspension was applied under bath sonication to ensure uniform dispersion and minimize agglomeration. CNF-sized and unsized yarns were used to fabricate unidirectional composite plates via filament winding on a flat mandrel, followed by compression molding. Scanning electron microscopy confirmed CNF presence on both CF and PA6 filaments. CNF-sized composites exhibited increments in interlaminar shear strength (ILSS) by 50%, flexural strength by 11%, and tensile strength by 2.5% compared to unsized composites. Thermal analysis showed minimal changes in degradation temperature and crystallinity. These findings demonstrate that CNF sizing enhances interfacial bonding and mechanical performance, offering a scalable and environmentally friendly strategy for thermoplastic composite manufacturing along with yarn/tow handleability.

Cellulose nanofibrils (CNF)↗

DOE OSTI2021

Performance of hybridized bamboo-carbon fiber reinforced polypropylene composites processed using wet laid technique

The end-of-life vehicles (ELV) regulations motivate hybrid materials usage in automotive industries to optimize properties at reduced cost and increase eco-friendly designs. This research explores hybrid compositions of natural bamboo fiber and synthetic carbon fiber. The goal of hybridization was to synergistically benefit from each constituent– i.e., sustainability, energy absorption and superior damping from bamboo, and high strength and stiffness from carbon fiber. Carbon fibers (CF), bamboo fibers (BF) and polypropylene (PP) fibers were dispersed in water to produce wet-laid hybrid mats. The mats were compression molded into consolidated panels to obtain the hybrid composite(s) (BF-CF-PP). Four formulations with different fiber-resin weight percent were designed and produced including- BF-PP (30/70), BF-PP (50/50), BF-CF-PP (32/8/60), and BF-CF-PP (8/32/60). The effect of (a) fiber length, (b) surface treatment, (c) fiber content, and (d) consolidation pressure on the mechanical properties were examined. The improved mechanical (flexural strength 76.4 MPa, flexural modulus 4.1 GPa, ILSS 12.4 MPa and impact strength 49.9 KJ/m 2 ) and vibrational damping (1.05%) properties showed that the BF-CF-PP (8/32/60) provided higher properties compared to the other variants. The projected properties at various stoichiometric ratios of carbon and bamboo fiber revealed that the properties of hybrid composites could be tailored to produce desirable, cost-effective, and sustainable automotive components.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Improvement of interfacial adhesion of unidirectional textile grade carbon fiber (TCF) with unsized, epoxy and urethane sizing reinforced in thermoset urethane composites

This work considers a unique wide tow (450k filaments) form of low-cost carbon fiber intended for non-aerospace applications. TCF is currently produced in epoxy and urethane sizing, and there is a need to understand its resulting composite properties. In this work, the interfacial adhesion of sized TCF reinforced in thermoset urethane (TSU) composites are examined through the surface, thermal and mechanical characterization techniques. Atomic force microscopy (AFM) results showed an increase in surface roughness for urethane (276%) and epoxy sized (78%) versus unsized TCF. XPS results showed 531% increase in O in epoxy sized TCF and 250% N content in urethane sized TCF compared to unsized TCF. The surface energy of epoxy and urethane sized TCF is enhanced by 78% and 96%, respectively compared to unsized TCF. The storage modulus showed improvement for urethane (23%) and epoxy (21%) sized than unsized TCF-TSU composites. The flexural, interlaminar shear strength (ILSS), and impact properties of urethane sized TCF increase by 24%, 50%, and 273%, respectively, than unsized TCF. The results demonstrate that the surface and thermal properties correlate with the mechanical properties of TCF-TSU composites and sizing enhances the wettability of the composites.

36 MATERIALS SCIENCE↗

NASA NTRS1987

Improving the interlaminar shear strength of carbon fiber-epoxy composites through carbon fiber bromination

The use of bromine to improve the interlaminar shear strength of PAN-based carbon fibers was investigated. Composite test specimens fabicated from brominated T-300 fibers and a MY720 matrix exhibited on average a 30% improvement in ILSS over their pristine counterparts. Mass, electrical resistivity, density, contact angle, and scanning Auger microscopy results suggested a mechanism in which the bromine was covalently bonded to the surface of the fiber, and this resulted in an increased van der Waal's adhesion between fiber and matrix.

Jaworske, Donald A.↗

NASA NTRS1992

Transverse flexural tests as a tool for assessing damage to PMR-15 composites from isothermal aging in air at elevated temperatures

To date, the effect of thermo-oxidative aging on unidirectional composite mechanical properties has been monitored by the measurement of interlaminar shear strength (ILSS) and either three or four point longitudinal flexural strength (LFS) of the composites being tested. Both results are affected by the fiber-to-matrix bonding, the former being dependent on the shear resistance of the interface and the latter on the degree of load sharing by the fibers through the fiber/matrix interface. Recently, fiber/matrix interfacial bond strengths have been monitored using a transverse flexural strength (TFS) test method. This test method was used to evaluate the effect of fiber surface treatment on the fiber/matrix bond. The interface bonding was varied in these tests using Hercules A-fibers with three-types of surfaces that produce bonds of poor, better, and good quality. The TFS was found not only to be sensitive to the bonding, but also to the aging time of unidirectional A-fiber/PMR-15 composites. This relationship reflects the mechanism by which the PMR-15 degrades during thermal aging.

Bowles, Kenneth J.↗

NASA NTRS1993

Transverse flexural tests as a tool for assessing damage to PMR-15 composites from isothermal aging in air at elevated temperatures

Bowles, Kenneth J.↗

NASA NTRS1995

The Effects of Fiber Surface Modification and Thermal Aging on Composite Toughness and Its Measurement

A detailed experimental study was conducted to establish the structure-property relationships between elevated temperature aging and fiber-matrix bonding, Mode 2 interlaminar fracture toughness, and failure modes of carbon fiber/PMR-15 composites. The fiber-matrix adhesion was varied by using carbon fibers with different surface treatments. Short beam shear tests were used to quantify the interfacial shear strength afforded by the use of the different fiber surface treatments. The results of the short beam shear tests showed that, for times up to 1000 hr, the aging process caused no changes in the bulk of the three composite materials that would degrade the shear properties of the material. Comparisons between the interlaminar shear strengths (ILSS) measured by the short beam shear tests and the GIIC test results, as measured by the ENF test, indicated that the differences in the surface treatments significantly affected the fracture properties while the effect of the aging process was probably limited to changes at the starter crack tip. The fracture properties changed due to a shift in the fracture from an interfacial failure to a failure within the matrix when the fiber was changed from AU-4 to AS-4 or AS-4G. There appears to be an effect of the fiber/matrix bonding on the thermo-oxidative stability of the composites that were tested. The low bonding afforded by the AU 1 fiber resulted in weight losses about twice those experienced by the AS 1 reinforced composites, the ones with the best TOS.

Bowles, Kenneth J.↗

NASA NTRS1997

The Effects of Fiber Surface Modification and Thermal Aging on Composite Toughness And its Measurement

A detailed experimental study was conducted to establish the structure-property relationships between elevated temperature aging and (I) fiber-matrix bonding, (2) Mode II interlaminar fracture toughness, and (3) failure modes of carbon fiber/PMR-15 composites. The fiber-matrix adhesion was varied by using carbon fibers with different surface treatments. Short beam shear tests were used to quantify the interfacial shear strength afforded by the use of the different fiber surface treatments. The results of the short beam shear tests definitely showed that, for aging times up to 1000 hr, the aging process caused no observable changes in the bulk of the three composite materials that---would degrade the shear properties of the material. Comparisons between the interlaminar shear strength (ILSS) measured by the short beam shear tests and the GII c test results, as measured by the ENF test, indicated that the differences in the surface treatments significantly affected the fracture properties while the effect of the aging process was probably limited to changes at the starter crack tip. The fracture properties changed due to a shift in the fracture from an interfacial failure to a failure within the matrix when the fiber was changed from AU-4 to AS-4 or AS-4G. There appears to be an effect of the fiber/matrix bonding on the thermo-oxidative stability of the composites that were tested. The low bonding afforded by the AU-4 fiber resulted in weight losses about twice those experienced by the AS-4 reinforced composites, the ones with the best TOS.

Bowles, Kenneth J.↗

NASA NTRS2015

Improving Interlaminar Shear Strength

To achieve NASA's mission of space exploration, innovative manufacturing processes are being applied to the fabrication of complex propulsion elements.1 Use of fiber-reinforced, polymeric composite tanks are known to reduce weight while increasing performance of propulsion vehicles. Maximizing the performance of these materials is needed to reduce the hardware weight to result in increased performance in support of NASA's missions. NASA has partnered with the Mississippi State University (MSU) to utilize a unique scalable approach of locally improving the critical properties needed for composite structures. MSU is responsible for the primary development of the concept with material and engineering support provided by NASA. The all-composite tank shown in figure 1 is fabricated using a prepreg system of IM7 carbon fiber/CYCOM 5320-1 epoxy resin. This is a resin system developed for out-of-autoclave applications. This new technology is needed to support the fabrication of large, all composite structures and is currently being evaluated on a joint project with Boeing for the Space Launch System (SLS) program. In initial efforts to form an all composite pressure vessel using this prepreg system, a 60% decrease in properties was observed in scarf joint regions. Inspection of these areas identified interlaminar failure in the adjacent laminated structure as the main failure mechanism. This project seeks to improve the interlaminar shear strength (ILSS) within the prepreg layup by locally modifying the interply region shown in figure 2.2

Jackson, Justin↗

DOE OSTI2021

Cross Section Generation Capability in Griffin

The Griffin code is a Multiphysics Object-Oriented Simulation Environment (MOOSE) based reactor multiphysics analysis application jointly developed by Idaho National Laboratory and Argonne National Laboratory. The code includes a variety of steady-state solvers for fixed-source, k-eigenvalue, adjoint, and subcritical multiplication, as well as transient solvers for point-kinetics, improved quasi-static, and spatial dynamics. The code reads multigroup cross sections in the ISOXML format generated from external deterministic or Monte Carlo cross section generation codes. The implementation of the cross section generation capability in Griffin was initiated last year by plugging in the cross section application programming interface (CSAPI) and reviewing the methodologies for treating particulate fuels. The focus this year was on improving the CSAPI integration and implementing advanced self-shielding methods for applications to advanced reactor problems with TRISO fuels. First, the process for cross section library generation was updated to accurately and rigorously produce isotopic cross section data. Second, the on-the-fly slowing down method for the resonance treatment was implemented in CSAPI to improve the accuracy of effective multigroup cross sections in the resonance energy range. Among various on-the-fly slowing down methods, the equivalent Dancoff factor cell method was employed. Third, the iterative local spatial self-shielding method was implemented under the calculation framework of the equivalent Dancoff factor cell method to accurately deal with the double heterogeneity effect of particulate fuel. The updated CSAPI with the advanced self-shielding methods, together with the cross section libraries generated based on the improved process, were tested for the very high temperature reactor (VHTR), high temperature test reactor (HTTR), and Empire benchmark problems with various resonance self-shielding conditions, indicating that the updated CSAPI in Griffin is able to produce multigroup cross sections accurately and efficiently. We also show that the methodology works well for pebble bed fuel from HTR-10, but the capability still needs to be fully integrated into CSAPI. In the future, further benchmark tests will be performed for various thermal reactor core problems, including particulate fuel-based pebble bed reactors.

22 - GENERAL STUDIES OF NUCLEAR REACTORS↗