DOE OSTI2025

Study of hydride reorientation and ductility of SRA ZIRLO and PRXA ZIRLO using ring compression testing (RCT)

Before dry storage, spent nuclear fuel is dried at high temperatures, which induces hydride dissolution. Radial hydride particles precipitate when cooled under a stress above a threshold stress. This process can severely degrade the ductility of cladding tubes. Zirconium alloys with different microstructures, such as grain boundary density, were quantified and studied to examine their effect on hydride reorientation. The ring compression loading mode creates a range of stress states depending on the location within the ring with respect to the applied load, producing various hydride morphologies that can be used to study the effects of microstructures on hydride reorientation. Finite element modeling was performed to calculate the hoop stress, which is the dominant stress, during hydride reorientation. These results were coupled with hydride morphology to determine the threshold stress for hydride reorientation, depending on the microstructure. In conclusion, the samples were then mechanically tested using ring compression to evaluate the ductility of zirconium alloys as a function of different hydride morphologies.

Hydride embrittlement↗

DOE OSTI2025

Dislocation nano-hydrides in nickel: Nucleation, evolution and effects on dislocation behaviors

Nano-hydrides have been predicted to precipitate at the core of edge dislocations in the Ni-H system, a mechanism that may promote hydrogen embrittlement. However, nano-hydride nucleation, growth, and effects on dislocation behavior have seldom been explored. This work combines molecular dynamics grand canonical Monte Carlo (MD-GCMC) simulations and continuum modeling to uncover a wide range of phenomena linked to dislocation nano-hydrides. Simulations reveal that nano-hydrides can be stabilized at dislocation cores with all character angles, including screw segments, due to the hydrostatic stresses around the cores of the Shockley partials. Nano-hydride nucleation takes place in these regions, and growth is dictated by the character angle θ of the perfect dislocation. The equilibrium stacking fault width d eq varies dynamically to increase the local hydrostatic stress field and facilitate the formation of the nano-hydride, forming a constriction-like feature and leading to three distinct behaviors: d eq decreases for θ > 30°, d eq remains unchanged for θ = 30°, and d eq increases for θ < 30°. Remote hydrostatic and Escaig stresses are also shown to influence the nucleation stage, implying stress concentrations such as those ahead of crack tips may facilitate nano-hydride precipitation. Moreover, we identify a new hydrogen-induced 60° dislocation reaction that emits a Shockley partial on a conjugate plane, with potential implications for twin nucleation. Testable predictions from this study are then used to reinterpret previous results from the literature. In conclusion, these findings provide a comprehensive framework to assess nano-hydride formation and evolution at dislocations in nickel and other face-centered cubic metals, with important implications to hydrogen embrittlement.

Dislocations↗

DOE OSTI2024

Hydrogen embrittlement of Zircaloy-4 fabricated by ultrasonic additive manufacturing

Ultrasonic additive manufacturing (UAM) was successfully applied to the zirconium material system to create a planar geometry. Following fabrication, SS-J3 type tensile specimens of the UAM and wrought Zircaloy-4 with a nominal gage section of 5×1.2×0.75 mm were machined for hydriding studies and mechanical testing. The SS-J3 type tensile specimens were gas-charged with hydrogen using a custom system that precisely controls hydrogen gas flow rate, hydrogen partial pressure, and temperature. To avoid altering the UAM material, the maximum process temperature was limited to 550°C. Using different initial hydrogen gas pressures and flow rates, various hydrogen contents (70–1755 wppm) were achieved for Zircaloy-4 specimens. Tensile testing shows that, regardless of hydrogen content, all UAM specimens measured yield strengths in the range of 557±16 MPa and ultimate tensile strengths of 660±4MPa. However, total elongation clearly decreased as a function of increasing hydrogen content. Further, at the lowest hydrogen content, the total plastic elongation measured 21.5%, and this value decreased to less than 2% when the hydrogen content was increased to 1000 wppm. Cross-sectional optical microscopy images revealed that the hydride distributions are randomly oriented. For the low hydrogen content specimen, these randomly distributed hydrides are isolated from each other. A sandwiched structure, consisting of high-density and low-density layers, was also observed for the specimens with hydrogen content between 200 and 400 wppm. As the hydrogen content increases, the hydrides diffuse into the low-density hydride layers to form a network across the whole specimen. Although the tensile properties of UAM and wrought Zircaloy-4 exhibit the same behavior with increasing hydrogen content, the distinctions in grain orientations led to differences in the hydride orientations at low and intermediate hydrogen concentrations.