Micromechanical and fatigue in situ synchrotron characterization of an additively manufactured superalloy with porosity
Additive manufacturing (AM) has the potential to transform component production, but its widespread adoption is constrained by defects, such as pores, that compromise structural integrity. Here, this study investigates the influence of porosity on the micromechanical and fatigue response of AM Inconel 718 (IN718), a widely used aerospace superalloy. One baseline specimen with minimal stochastic porosity and another intentionally seeded with lack of fusion (LOF) pores were examined using high-energy X-ray diffraction microscopy (HEDM) and micro-computed tomography during cyclic loading. Fatigue cracks in the LOF specimen initiated more frequently and at lower cycle counts than in the baseline specimen. The number fraction of fatigue cracks that grew was comparatively higher in the LOF specimen. Grain-level metrics, including stress and diffraction spot widths, were quantified using far-field HEDM. Across the thousands of grains detected in both specimens, the pores in the LOF specimen increased the variability of stress and spot width evolution in the azimuthal direction, the latter serving as a surrogate measure of plastic deformation. However, no correlations emerged between these metrics and grain proximity to fatigue crack initiation sites or pores, underscoring the limitations of grain-averaged metrics for predicting fatigue. Nonetheless, the rich dataset reported here provides a foundation for future modeling efforts.