NASA NTRS2026

Fatigue Behavior of Laser Powder Bed Fused HAYNES 214: Effects of Different Surface Treatments

In this study, under NASA’s Rapid and Analysis Manufacturing Propulsion Technology (RAMPT) project, effects of different surface post-treatments on surface texture and fatigue behavior of L-PBF Alloy 214 were investigated. Various subtractive SPTs including abrasive flow machining (AFM), machining (M), shot peening (SP), vapormatt (VM), dry electropolishing (DE), chemical milling (CM), chemical-mechanical polishing (CMP), electro chemical (ECP) were applied to study the variations of the surface texture, microstructure and uniaxial fatigue behavior under fully reversed strain-controlled condition at four different strain amplitudes of 0.005, 0.004, 0.003, and 0.0025 mm/mm. The insights gained regarding the relationship between structural and mechanical properties for different SPTs can help establish guidelines for selecting the most effective process to enhance the performance of Laser Powder Bed Fusion (L-PBF) Alloy 214, especially for critical aerospace applications.

Post-Processing↗
NASA NTRS1962

Mercury Corrosion Loop Testing Program

The Mercury Corrosion Loop Testing Program continued through the second quarter. Materials to be tested in the 10 forced-convection test loops were selected; the materials are: Haynes 25, 9 Cr-1Mo alloy clad with Type 316 stainless steel, AM 350 stainless steel, and columbium (niobium) clad with Type 316 stainless steel. The eight-test-cell facility was completed and all utilities were installed. Pneumatic and electronic instrumentation for all test cells was installed and calibrated. Fabrication was initiated on the first four Haynes 25 loops. The first loop was 85% assembled at the end of the quarter. A centrifugal pump made from Type 316 stainless steel was tested; bearing modifications were made to improve operation.

Corrosion↗
NASA NTRS2016

NASA Alternative Orion Small Cell Battery Design Support

The NASA Orion Crew Module Reference Design was produced to address large scale thermal runaway (TR) hazard with specific safety controls for the Orion Spacecraft. The design presented provides the description of a full scale battery design reference for implementation as a drop in replacement to meet all spacecraft energy requirements with compatible 120 Vdc electrical and mechanical interface using small cell technology (18650) packaging. The 32V SuperBrick incorporates unique support features and an electrical bus bar arrangement that allows cells negative can insertion into heat sink that is compressively coupled to the battery enclosure to promote good thermal management. The housing design also provides an internal flame suppression "filter tray" and positive venting path internal to the enclosure to allow hot effluent ejecta to escape in the event of single cell TR. Virtual cells (14P Banks) that are supported to provide cell spacing with interstitial materials to prevent side can failures that can produce cell to cell TR propagation. These features were successfully test in four separate TR run with the full scale DTA1 test article in February 2016. Successfully Completed Test Objectives - Four separate TR test runs with Full-Scale DTA1 housing with Two SuperBricks, Two SuperBrick Emulators All Tests resulted in "clean" gas with less than 6 C rise at Battery vent All Tests resulted in less than 2 C temperature rise on cold-plate outlet All Tests resulted in less than 6 psi pressure rise in the battery housing Test Run 1 -One neighbor cell TR, highest remaining neighbor 139 C. Ejecta shorted to bus caused prolonged additional heating, One shorted cell did experience TR after 12 minutes, remaining cells had adequate thermal margin Test Run 2 - No cell to cell propagation, highest neighbor cell 112 C; Test Run 3 - No cell to cell propagation, highest neighbor cell 96 C; Test Run 4 - No cell to cell propagation, highest neighbor cell 101 C; Primary TR testing and analysis were completed and reviewed for endorsement by NASA Engineering and Safety Center team members. All Key Test Objectives were met and the small cell design alternative was demonstrated and selected to be a feasible drop in replacement for the MPCV Orion CM Battery for EM2 mission.

Haynes, Chuck↗
DOE OSTI2026

Influence of microstructure and temperature on impact toughness of H13 steel produced by binder jet additive manufacturing

Binder Jet Additive Manufacturing (BJAM) is a promising manufacturing pathway to produce H13 steel dies and tooling with complex geometries for applications in high pressure aluminum die casting, hot stamping, and injection molding. While fully dense H13 coupons produced using BJAM have been subjected to detailed microstructure characterization, properties which are critical and relevant to the aforementioned applications, such as impact toughness, have not been reported. Here, this work evaluated the influence of microstructural characteristics and test temperature on the impact toughness of H13 produced by BJAM. Coupons were produced from three different powder size distributions (PSDs), with nominal powder size ranges of −22 μm, 10-32 μm, and 15-53 μm. Coupons were printed, sintered, hot isostatically pressed (HIPed), and heat treated by quenching and tempering. After HIPing, the measured porosities of the different PSDs were all less than 0.015 vol%. The −22 μm PSD BJAM material exhibited the best impact toughness of all three PSDs across the entire test temperature range from 25 to 400 °C, and also exhibited an ambient temperature impact toughness of 10.9 J at a hardness of 46 HRC, equivalent to minimum threshold requirements for premium grade H13. However, all three BJAM PSDs exhibited moderately lower impact toughness than premium grade wrought H13 from RT to 400 °C. We attribute this in part due to the very large prior-austenite grain (PAG) sizes near 400 μm and segregation from former liquid channels leading to greater amounts of carbide precipitation on PAG boundaries. Technical pathways for optimizing processing and chemistry of BJAM H13 to further improve impact toughness are discussed.

Binder jet additive manufacturing↗
NASA NTRSDate not supplied

Effect of Barely Visible Impact Damage on Thermoplastic Welded Structure

Spirit Aerosystems recently conducted screening tests on thermoplastic skin/stringer panels manufactured with Automated Fiber Placement (AFP) and stamp forming which were joined using Spirit’s Co-Fusion process. Skin and stringer gauge were both set to 0.168 cm. The resulting panel design is 48 cm tall, 49 cm wide, and has 3 stringers welded at a 21.5 cm pitch. Barely Visible Impact Damage (BVID) and Residual Compressive Strength were chosen to conduct a damage tolerance study. Zee stringers, made with IM8/PEKK-FC material, were Co-Fusion welded to a T1100/TC1225 skin. Out of these 5 panels, 1 was chosen to be a BVID survey panel, 1 for pristine compressive strength determination, and 3 to be impacted to create BVID followed by testing for residual compressive strength. On the survey panel, impacts ranged in energy from 40J – 65J and dent depth measurements were conducted at 24 hours, 48 hours, and two weeks after impacting. The residual compressive strength panel failed near the predicted load of 214 MPa. For the residual compressive strength panels, BVID was created at two different mid-bay locations: 1) striking the OML coincident with the stringer and 2) striking the skin IML 2.5 cm away from the stringer flange. Pulse Echo Ultrasonic Testing was used to inspect the panels before and after creating BVID.

HiCAM↗
NASA NTRSDate not supplied

Design, Build, and Testing of the Roman Space Telescope’s Wide Field Instrument Optical Stimulus System (SORC)

The Stimulus Of Ray Cones (SORC) is an optical stimulus system developed to verify, characterize, and calibrate the Roman Space Telescope’s (RST) Wide Field Instrument (WFI) under simulated operational conditions. SORC provides several critical test modes, the primary being point-source mode, which projects an image anywhere on the Focal Plane Assembly (FPA) detectors. This mode provides precise position knowledge of the FPA within WFI. Additional modes enable capturing WFI pupil alignment, evaluation of WFI’s selectable optical elements, and verification of focal plane fiber operation for higher-level system testing. The light source system incorporates a suite of narrowband and broadband fiber fed sources spanning the visible to near-infrared range, with options for pulsed or continuous wave illumination. SORC was designed and built at NASA’s Goddard Spaceflight Center (GSFC). Initial system-level testing occurred under ambient conditions in GSFC’s Spacecraft Systems Development and Integration Facility (SSDIF), followed by vacuum testing at operational temperatures (SORC at 214-222 K) in the Space Environment Simulator (SES). The system was then shipped to BAE Systems in Boulder, CO for post-shipment ambient and cryogenic testing before integration with WFI for two thermal vacuum test campaigns at cryogenic temperatures. This presentation will focus on design, development, and performance of SORC. Details of WFI verification and calibration using SORC, along with test results, have been published previously and will be referenced only as needed to describe SORC. The SORC ground test capability is critical to ensuring WFI meets stringent optical performance requirements, directly supporting the mission’s science objectives.

Stimulus of Ray Cones↗
DOE OSTI2026

A transport-based framework for solidification cracking in Ni-based superalloys processed by laser powder bed fusion

Solidification cracking remains a persistent barrier to laser powder bed fusion (LPBF) processing of solid-solution-strengthened (SSS) Ni-based superalloys and is commonly attributed to carbide formation, liquation-type failure, or elemental segregation. In this work, the cracking behavior of three SSS Ni-based superalloys—Inconel 625 (625), Inconel 617 (617), and Haynes 230 (230)—is examined under comparable LPBF conditions to evaluate the origins of their cracking susceptibility. Carbides were present in both 625 and 230, yet cracking behavior differed significantly. MC-type carbides in 625 remain discrete and preserve liquid connectivity, whereas Cr-rich M23C6 carbides in 230 form at cellular triple junctions that bottleneck the interdendritic liquid network, influencing cracking through liquid connectivity rather than as an independent cause. Alloy 617 exhibited anomalous segregation without resolvable secondary phases yet cracked mildly, indicating that extensive carbide formation is not a prerequisite for cracking. To rationalize these observations, a transport-limited framework is proposed in which cracking occurs when terminal-liquid feeding cannot accommodate solidification-induced strain; among the mechanisms evaluated, this framework is most consistent with the physical constraints imposed by LPBF solidification. Transport-based crack-susceptibility indexes incorporating permeability, viscosity, and solidification kinetics distinguish the alloy hierarchy; permeability ratios Krat increased from approximately 7 (625) to 11.5 (617) and 14.5 (230), with corresponding increases in the μ-weighted mushy zone risk index (CSIMZRM). These results are consistent with transport-limited liquid feeding as a rate-limiting contributor to solidification cracking in LPBF-processed SSS Ni-based superalloys, providing a physically grounded basis for alloy and process design.

Hyer, Holden [ORNL] (ORCID:0000000343915561)↗