NASA NTRS1979

Polyimide adhesive bonding

Adhesive systems which could be used to bond composite-to-composite, composite-to-titanium, and honeycomb sandwich structures with operational capability at 589K for a minimum of 125 hours were evaluated. Evaluations were based on mechanical property tests such as lap shear and flatwise tensile and on processability. Quasi-isotropic Celion 6000/PMR-15 composite adherend was used to construct lap shear and flatwise tensile specimens. Hexcel's HRH-327-3/16-6.0 glass polyimide honeycomb core was also utilized in the flatwise tensile specimens. Numerous processing variations were also studied that led to selected cure cycles for each adhesive. Shear specimens having either 12 mm or 75 mm overlaps were used to determine the effect of bond size on processability and lap shear properties. The data indicate that processing of FM-34, FM-34B-18, LARC-13 and NRO56X can be achieved using a cure compatible with the composite adherend. No significant differences in mechanical properties were observed among the three adhesive systems and all three are suitable candidates for 589K/125 hour service.

Progar, D.↗
NASA NTRS1979

The structural behavior of a graphite-polymide honeycomb sandwich panel with quasi-isotropic face sheets and an orthotropic core

The results of a series of tests of graphite-polyimide honeycomb sandwich panels are presented. The panels were 1.22 m long, 0.508 m wide, and approximately 13.3 m thick. The face sheets were a T-300/PMR-15 fabric in a quasi-isotropic layup and were 0.279 mm thick. The core was Hexcel HRH 327-3/16 - 4.0 glass reinforced polyimide honeycomb, 12.7 mm thick. Three panels were used in the test: one was cut into smaller pieces for testing as beam, compression, and shear specimens; a second panel was used for plate bending tests; the third panel was used for in-plane stability tests. Presented are the experimental results of four point bending tests, short block compression tests, core transverse shear modulus, three point bending tests, vibration tests, plate bending tests, and panel stability tests. The results of the first three tests are used to predict the results of some of the other tests. The predictions and experimental results are compared, and the agreement is quite good.

Hyer, M. W.↗
NASA NTRS1980

Experimental investigation of graphite/polyimide sandwich panels in edgewise compression

The local and general buckling of graphite/polyimide sandwich panels simply supported along all four edges and loaded in uniaxial edgewise compression is investigated. Material properties of sandwich panel constituents (adhesive and facings) were determined from flatwise tension and sandwich beam flexure tests. An adhesive bond study resulted in the selection of a suitable cure cycle for FM 34 polyimide film adhesive and, a bonding technique using a liquid cell edge version of that adhesive resulted in considerable mass savings. Tensile and compressive material properties of the facings, quasiisotropic, symmetric, laminates (0, +45,90,-45)s of Celion/PMR-15, were determined at 116, R.T., and 589 K (-250, R.T., and 600 F) usng the sandwich beam flexure test method. Results indicate the Gr/PI is a usable structural material for short term use at temperatures as high as 589 K (600 F). Buckling specimens were 1006.5 sq cm. 156 sq in., had quasiisotropic symmetric facings (0, + or - 45,90)s and a glass/polyimide honeycomb core (HRH-327-3/8-4).

Camarda, C. J.↗