Oxide Dispersion Strengthened Ferritic Steel Wire Feedstock Development for Larger Format Additive Manufacturing (CRADA Final Report)
This CRADA project funded through DOE’s INFUSE program sought to demonstrate the viability of fabricating large, complex parts from oxide dispersion strengthened (ODS) steel with advanced manufacturing. Exhibiting excellent radiation tolerance and high mechanical performance at elevated temperatures, ODS steel is a promising structural material candidate for near-plasma components in fusion energy systems. Its use, however, has been limited by a lack of manufacturability. This project sought to produce ODS steel wire through a solid-state shear assisted extrusion process and then demonstrate that the wire can undergo controlled local melting while being welded with the final part sufficiently retaining the beneficial properties of ODS steel. This would allow the use of wire-arc additive manufacturing (WAAM) to manufacture large-scale ODS parts, even though ODS is currently only available as a powder. WAAM is a promising technique for producing components like the replaceable ARC vacuum vessel in CFS’ fusion reactor design. Meanwhile, this project will also expand PNNL’s capability in producing custom wire feedstock with friction extrusion, enabling downstream large-scale manufacturing with WAAM and solid-state based additive manufacturing. The project achieved its goals of developing tooling and fixturing to produce ODS wire at smaller diameters than previous projects. Several small lengths of wire of 1.5 mm and 2.5 mm diameter in the range of 2.5-30 mm long were produced at tool temperatures that are known to cause ODS particle coarsening (~1200 °C). Fixtures and tooling for longer (>1 m) wires were developed but further process development is needed reduce tool temperature during extrusions and to increase wire length needed for WAAM testing and development.