NASA NTRS2000

Insights Developed Into the Damage Mechanism of Teflon FEP Thermal Control Material on the Hubble Space Telescope

Metalized Teflon FEP (DuPont; fluorinated ethylene propylene) thermal control material on the Hubble Space Telescope (HST) has been found to degrade in the space environment. Teflon FEP thermal control blankets retrieved during the first servicing mission were found to be embrittled on solar-facing surfaces and to contain microscopic cracks (the FEP surface is exposed to the space environment). During the second servicing mission, astronauts noticed that the FEP outer layer of the multilayer insulation blanketing covering the telescope was cracked in many locations. Large cracks were observed on the light shield, forward shell, and equipment bays. A tightly curled piece of cracked FEP from the light shield was retrieved during the second mission. This piece was severely embrittled, as witnessed by ground testing. A Failure Review Board was organized by NASA Goddard Space Flight Center to determine the mechanism causing the multilayer insulation degradation. This board included members of the Electro-Physics Branch of the NASA Glenn Research Center at Lewis Field. Density measurements of the retrieved materials obtained under the review board's investigations indicated that FEP from the first servicing mission was essentially unchanged from pristine FEP but that the second servicing mission FEP had increased in density in comparison to pristine FEP (ref. 1). The results were consistent with crystallinity measurements taken using x-ray diffraction and with results from solid-state nuclear magnetic resonance tests (see the table and ref. 1). Because the second servicing mission FEP was embrittled and its density and crystallinity had increased in comparison to pristine FEP, board researchers expected that the first servicing mission FEP, which was also embrittled, would also have increased in crystallinity and density, but it did not. Because the retrieved second servicing mission material curled while in space, it experienced a higher temperature extreme during thermal cycling (estimated at 200 C) than the first servicing mission material (estimated at 50 C). Therefore, Glenn initiated and conducted an investigation of the effects of heating pristine FEP and FEP that had been exposed on the Hubble Space Telescope. Samples of pristine and first and second servicing mission FEP were heated to 200 C and evaluated for changes in density and morphology. We hoped that the results would help explain why FEP degrades in the Hubble Space Telescope space environment.

deGroh, Kim K.↗
NASA NTRS2002

The Effect of Heating on the Degradation of Ground Laboratory and Space Irradiated Teflon(r) FEP

The outer most layer of the multilayer insulation (MLI) blankets on the Hubble Space Telescope (HST) is back surface aluminized Teflon(R) FEP (fluorinated ethylene propylene). As seen by data collected after each of the three servicing missions and as observed during the second servicing mission (SM2), the FEP has become embrittled in the space environment, leading to degradation of the mechanical properties and severe on-orbit cracking of the FEP. During SM2, a sample of aluminized-FEP was retrieved from HST that had cracked and curled, exposing its aluminum backside to space. Because of the difference in optical properties between FEP and aluminum, this insulation piece reached 200 C on-orbit, which is significantly higher than the nominal MLI temperature extreme of 50 C. This piece was more brittle than other retrieved material from the first and third servicing missions (SM1 and SM3A, respectively). Due to this observation and the fact that Teflon thermal shields on the solar array bi-stems were heated on-orbit to 130 C, experiments have been conducted to determine the effect of heating on the degradation of FEP that has been irradiated in a ground laboratory facility or in space on HST. Teflon FEP samples were X-ray irradiated in a high vacuum facility in order to simulate the damage caused by radiation in the space environment. Samples of pristine FEP, X-ray irradiated FEP and FEP retrieved from the HST during SM3A were heat treated from 50 to 200 C at 25 intervals in a high vacuum facility and then tensile tested. In addition, samples were tested in a density gradient column to determine the effect of the radiation and heating on the density of FEP. Results indicate that although heating does not degrade the tensile properties of non-irradiated Teflon, there is a significant dependence of the percent elongation at failure of irradiated Teflon as a function of heating temperature. Irradiated Teflon was found to undergo increasing degradation in the elongation at failure as temperature was increased from room temperature to 200 C. Rate of degradation changes, which were consistent with the glass I transition temperatures for FEP, appeared to be present in both tensile and density data. The results indicate the significance of the on-orbit temperature of Teflon FEP with respect to its degradation in the low Earth orbital space environment.

deGroh, Kim K.↗
NASA NTRS2020

The Effect of Heating on the Degradation of Ground Laboratory and Space Irradiated Teflon® FEP

The outer most layer of the multilayer insulation (MLI) blankets on the Hubble Space Telescope (HST) is back surface aluminized Teflon® FEP (fluorinated ethylene propylene). As seen by data collected after each of the three servicing missions and as observed during the second servicing mission (SM2), the FEP has become embrittled in the space environment, leading to degradation of the mechanical properties and severe on-orbit cracking of the FEP. During SM2, a sample of aluminized-FEP was retrieved from HST that had cracked and curled, exposing its aluminum backside to space. Because of the difference in optical properties between FEP and aluminum, this insulation piece reached 200 C on-orbit, which is significantly higher than the nominal MLI temperature extreme of 50 C. This piece was more brittle than other retrieved material from the first and third servicing missions (SM1 and SM3A, respectively). Due to this observation and the fact that Teflon thermal shields on the solar array bi-stems were heated on-orbit to 130 C, experiments have been conducted to determine the effect of heating on the degradation of FEP that has been irradiated in a ground laboratory facility or in space on HST. Teflon FEP samples were x-ray irradiated in a high vacuum facility in order to simulate the damage caused by radiation in the space environment. Samples of pristine FEP, x-ray irradiated FEP and FEP retrieved from the HST during SM3A were heat treated from 50 to 200 C at 25intervals in a high vacuum facility and then tensile tested. In addition, samples were tested in a density gradient column to determine the effect of the radiation and heating on the density of FEP. Results indicate that although heating does not degrade the tensile properties of non-irradiated Teflon, there is a significant dependence of the percent elongation at failure of irradiated Teflon as a function of heating temperature. Irradiated Teflon was found to undergo increasing degradation in the elongation at failure as temperature was increased from room temperature to 200 C. Rate of degradation changes, which were consistent with the glass I transition temperatures for FEP, appeared to be present in both tensile and density data. The results indicate the significance of the on-orbit temperature of Teflon FEP with respect to its degradation in the low Earth orbital space environment.

Hubble Space Telescope↗
NASA NTRS1997

Investigation of Teflon FEP Embrittlement on Spacecraft in Low Earth Orbit

Teflon(registered trademark) FEP (fluorinated ethylene-propylene) is commonly used on exterior spacecraft surfaces in the low Earth orbit (LEO) environment for thermal control. Silverized or aluminized FEP is used for the outer layer of thermal control blankets because of its low solar absorptance and high thermal emittance. FEP is also preferred over other spacecraft polymers because of its relatively high resistance to atomic oxygen erosion. Because of its low atomic oxygen erosion yield, FEP has not been protected in the space environment. Recent, long term space exposures such as on the Long Duration Exposure Facility (LDEF, 5.8 years in space), and the Hubble Space Telescope (HST, after 3.6 years in space) have provided evidence of LEO environmental degradation of FEP. These exposures provide unique opportunities for studying environmental degradation because of the long durations and the different conditions (such as differences in altitude) of the exposures. Samples of FEP from LDEF and from HST (retrieved during its first servicing mission) have been evaluated for solar induced embrittlement and for synergistic effects of solar degradation and atomic oxygen. Micro-indenter results indicate that the surface hardness increased as the ratio of atomic oxygen fluence to solar fluence decreased for the LDEF samples. FEP multilayer insulation (MLI) retrieved from HST provided evidence of severe embrittlement on solar facing surfaces. Micro-indenter measurements indicated higher surface hardness values for these samples than LDEF samples, but the solar exposures were higher. Cracks induced during bend testing were significantly deeper for the HST samples with the highest solar exposure than for LDEF samples with similar atomic oxygen fluence to solar fluence ratios. If solar fluences are compared, the LDEF samples appear as damaged as HST samples, except that HST had deeper induced cracks. The results illustrate difficulties in comparing LEO exposed materials from different missions. Because the HST FEP appears more damaged than LDEF FEP based on depth of embrittlement, other causes for FEP embrittlement in addition to atomic oxygen and ultraviolet (UV) radiation, such as thermal effects and the possible role of soft x-ray radiation, need to be considered. FEP that was exposed to soft x-rays in a ground test facility, showed embrittlement similar to that witnessed in LEO, which indicates that the observed differences between LDEF and HST FEP might be attributed to the different soft x-ray fluences during these two missions.

deGroh, Kim K.↗
NASA NTRS1999

Effects of Heating on Teflon(Registered Trademark) FEP Thermal Control Material from the Hubble Space Telescope

Metallized Teflon(Registered Trademark) FEP (fluorinated ethylene propylene) thermal control material on the Hubble Space Telescope (HST) is degrading in the space environment. Teflon(Registered Trademark) FEP thermal control blankets (space-facing FEP) retrieved during the first servicing mission (SM1) were found to be embrittled on solar facing surfaces and contained microscopic cracks. During the second servicing mission (SM2) astronauts noticed that the FEP outer layer of the multi-layer insulation (MLI) covering the telescope was cracked in many locations around the telescope. Large cracks were observed on the light shield, forward shell and equipment bays. A tightly curled piece of cracked FEP from the light shield was retrieved during SM2 and was severely embrittled, as witnessed by ground testing. A Failure Review Board (FRB) was organized to determine the mechanism causing the MLI degradation. Density, x-ray crystallinity and solid state nuclear magnetic resonance (NMR) analyses of FEP retrieved during SM1 were inconsistent with results of FEP retrieved during SM2. Because the retrieved SM2 material curled while in space, it experienced a higher temperature extreme during thermal cycling, estimated at 200 C, than the SM1 material, estimated at 50 C. An investigation on the effects of heating pristine and FEP exposed on HST was therefore conducted. Samples of pristine. SM1, and SM2 FEP were heated to 200 C and evaluated for changes in density and morphology. Elevated temperature exposure was found to have a major impact on the density of the retrieved materials. Characterization of polymer morphology of as-received and heated FEP samples by NMR provided results that were consistent with the density results. These findings have provided insight to the damage mechanisms of FEP in the space environment.

deGroh, Kim↗
NASA NTRS1998

Soft X-Ray Exposure Testing of FEP Teflon for the Hubble Space Telescope

The FEP Teflon (DuPont) multilayer insulation (MLI) thermal-control blanket material on the Hubble Space Telescope is degrading in the space environment. During the first Hubble servicing mission in 1993, after 3.6 years in low Earth orbit, aluminized and silvered FEP Teflon MLI thermal-control blanket materials were retrieved. These materials have been jointly analyzed by the NASA Lewis Research Center and the NASA Goddard Space Flight Center for degradation induced in the space environment (ref. 1). Solar-facing blanket materials were found to be embrittled with through-the-thickness cracking in the 5-mil FEP. During the second Hubble servicing mission in 1997, astronauts noticed that several blankets had large areas with tears. The torn FEP was curled up in some areas, exposing the underlying materials to the space environment. This tearing problem, and the associated curling up of torn areas, could lead to over-heating of the telescope and to particulate contamination. A Hubble Space Telescope MLI Failure Review Board was assembled by Goddard to investigate and identify the degradation mechanism of the FEP, to identify and characterize replacement materials, and to estimate the extent of damage at the time of the third servicing mission in 1999. A small piece of FEP retrieved during the second servicing mission is being evaluated by this failure review board along with materials from the first servicing mission. Since the first servicing mission, and as part of the failure review board, Lewis has been exposing FEP to soft x-rays to help determine the damage mechanisms of FEP in the space environment. Soft x-rays, which can penetrate into the bulk of FEP, are generated during solar flares and appear to be contributing to the degradation of the Hubble MLI.

deGroh, Kim K.↗
NASA NTRS1976

Comparison of type A and C Fluorinated Ethylene Propylene (FEP) as cover materials for silicon solar cells

Fluorinated ethylene propylene film (FEP, 0.0127 cm thick) was heat and pressure laminated to silicon solar cells as a low cost substitute for quartz covers. The FEP-C, treated on one side for bonding, was compared to FEP-A, an untreated FEP. With FEP-A, a silane adhesion promoter was applied to the cells. The FEP-C covers delaminated during accelerated temperature-humidity testing and Earth environmental exposure testing; FEP-A covers were unchanged. No differences were observed in peel tests, but FEP-A is superior in its resistance to tearing and in retention of transmission properties after exposure to ultraviolet radiation.

Broder, J. D.↗
NASA NTRS1999

Synchrotron Vacuum Ultraviolet Light and Soft X-Ray Radiation Effects on Aluminized Teflon FEP Investigated

Since the Hubble Space Telescope (HST) was deployed in low Earth orbit in April 1990, two servicing missions have been conducted to upgrade its scientific capabilities. Minor cracking of second-surface metalized Teflon FEP (DuPont; fluorinated ethylene propylene) surfaces from multilayer insulation (MLI) was first observed upon close examination of samples with high solar exposure retrieved during the first servicing mission, which was conducted 3.6 years after deployment. During the second HST servicing mission, 6.8 years after deployment, astronaut observations and photographic documentation revealed significant cracks in the Teflon FEP layer of the MLI on both the solar- and anti-solar-facing surfaces of the telescope. NASA Goddard Space Flight Center directed the efforts of the Hubble Space Telescope MLI Failure Review Board, whose goals included identifying the low-Earth-orbit environmental constituent(s) responsible for the cracking and embrittling of Teflon FEP which was observed during the second servicing mission. The NASA Lewis Research Center provided significant support to this effort. Because soft x-ray radiation from solar flares had been considered as a possible cause for the degradation of the mechanical properties of Teflon FEP (ref. 1), the effects of soft xray radiation and vacuum ultraviolet light on Teflon FEP were investigated. In this Lewisled effort, samples of Teflon FEP with a 100-nm layer of vapor-deposited aluminum (VDA) on the backside were exposed to synchrotron radiation of various vacuum ultraviolet and soft x-ray wavelengths between 18 nm (69 eV) and 0.65 nm (1900 eV). Synchrotron radiation exposures were conducted using the National Synchrotron Light Source at Brookhaven National Laboratory. Samples of FEP/VDA were exposed with the FEP surface facing the synchrotron beam. Doses and fluences were compared with those estimated for the 20-yr Hubble Space Telescope mission.

Dever, Joyce A.↗
NASA NTRS1998

A Comparison of Space and Ground Based Facility Environmental Effects for FEP Teflon

Fluorinated Ethylene Propylene (FEP) Teflon is widely used as a thermal control material for spacecraft, however, it is susceptible to erosion, cracking, and subsequent mechanical failure in low Earth orbit. One of the difficulties in determining whether FEP Teflon will survive during a mission is the wide disparity of erosion rates observed for this material in space and in ground based facilities. Each environment contains different levels of atomic oxygen, ions, and vacuum ultraviolet (VUV) radiation in addition to parameters such as the energy of the arriving species and temperature. These variations make it difficult to determine what is causing the observed differences in erosion rates. This paper attempts to narrow down which factors affect the erosion rate of FEP Teflon through attempting to change only one environmental constituent at a time. This was attempted through the use of a single simulation facility (plasma asher) environment with a variety of Faraday cages and VUV transparent windows. Isolating one factor inside of a radio frequency (RF) plasma proved to be very difficult. Two observations could be made. First, it appears that the erosion yield of FEP Teflon with respect to that of polyimide Kapton is not greatly affected by the presence or lack of VUV radiation present in the RF plasma and the relative erosion yield for the FEP Teflon may decrease with increasing fluence. Second, shielding from charged particles appears to lower the relative erosion yield of the FEP to approximately that observed in space, however it is difficult to determine for sure whether ions, electrons, or some other components are causing the enhanced erosion.

Rutledge, Sharon K.↗
NASA NTRS1975

Effect of electron irradiation in vacuum on FEP-A silicon solar cell covers

Fluorinated ethylene-propylene-A (FEP-A) covers on silicon solar cells were irradiated with 1-MeV electrons, in vacuum, to an accumulated fluence equivalent to approximately 28 years in synchronous orbit. The effect of irradiation on the light transmittance of FEP-A was checked by measuring the short-circuit current of the cells after each dose increment. The results indicate no apparent overall loss in transmission due to irradiation of FEP-A. Filter wheel measurements revealed some darkening of the FEP-A at the blue end of the spectrum. Although no delamination from the cell surface was observed while in vacuum, embrittlement of FEP-A occurred at the accumulated dose.

Marsik, S. J.↗
NASA NTRS1978

Ultraviolet irradiation at elevated temperatures and thermal cycling in vacuum of FEP-A covered silicon solar cells

Silicon solar cells covered with FEP-A were irradiated in vacuum with ultraviolet light and then subjected to thermal cycling. These accelerated laboratory conditions are believed to be equivalent to those experienced by FEP-A covered cells on the ATS-6 spacecraft and the results indicate a probable mechanism for the faster degradation of the FEP-A covered cells. Heat-bonded FEP-A covers apparently embrittle when exposed to four months of space UV radiation at elevated temperatures, and crack when subjected to thermal cycling during the eclipse period. Low energy proton radiation can then penetrate to the junction of the cell causing degradation of the open circuit voltage and maximum power to occur. An alternate method of application of FEP-A, such as with adhesives, may prevent such cracking.

Broder, J. D.↗
NASA NTRS2000

Effect of Air and Vacuum Storage on the Tensile Properties of X-Ray Exposed Aluminized-FEP

Metallized Teflon(Registered Trademark) FEP (fluorinated ethylene propylene), a common spacecraft thermal control material, from the exterior layer of the Hubble Space Telescope (HST) has become embrittled and suffers from extensive cracking. Teflon samples retrieved during Hubble servicing missions and from the Long Duration Exposure Facility (LDEF) indicate that there may be continued degradation in tensile properties over time. An investigation has been conducted to evaluate the effect of air and vacuum storage on the mechanical properties of x-ray exposed FEP. Aluminized-FEP (Al-FEP) tensile samples were irradiated with 15.3 kV Cu x-rays and stored in air or under vacuum for various time periods. Tensile data indicate that samples stored in air display larger decreases in tensile properties than for samples stored under vacuum. Air-stored samples developed a hazy appearance, which corresponded to a roughening of the aluminized surface. Optical property changes were also characterized. These findings indicate that air exposure plays a role in the degradation of irradiated FEP, therefore proper sample handling and storage is necessary with materials retrieved from space.

deGroh, Kim K.↗
NASA NTRS1997

Investigation of Teflon FEP Embrittlement on Spacecraft in Low-Earth Orbit

Teflon fluorinated ethylene propylene (FEP) (DuPont) is commonly used on exterior spacecraft surfaces for thermal control in the low-Earth orbit environment. Silverized or aluminized Teflon FEP is used for the outer layers of the thermal control blanket because of its high reflectance, low solar absorptance, and high thermal emittance. Teflon FEP is also desirable because, compared with other spacecraft polymers (such as Kapton), it has relatively high resistance to atomic oxygen erosion. Because of its comparably low atomic oxygen erosion yield, Teflon FEP has been used unprotected in the space environment. Samples of Teflon FEP from the Long Duration Exposure Facility (LDEF) and the Hubble Space Telescope (retrieved during its first servicing mission) were evaluated for solar-induced embrittlement and for synergistic effects of solar degradation and atomic oxygen.

deGroh, Kim K.↗
NASA NTRS2004

Effects of Various Wavelength Ranges of Vacuum Ultraviolet Radiation on Teflon FEP Film Investigated

Teflon Fluorinated Ethylene Propylene (FTP) films (DuPont) have been widely used for spacecraft thermal control and have been observed to become embrittled and cracked upon exposure to the space environment. This degradation has been attributed to a synergistic combination of radiation and thermal effects. A research study was undertaken at the NASA Glenn Research Center to examine the effects of different wavelength ranges of vacuum ultraviolet (VUV) radiation on the degradation of the mechanical properties of FEP. This will contribute to an overall understanding of space radiation effects on Teflon FEP, and will provide information necessary to determine appropriate techniques for using laboratory tests to estimate space VUV degradation. Research was conducted using inhouse facilities at Glenn and was carried out, in part, through a grant with the Cleveland State University. Samples of Teflon FEP film of 50.8 microns thickness were exposed to radiation from a VUV lamp from beneath different cover windows to provide different exposure wavelength ranges: MgF2 (115 to 400 nm), crystalline quartz (140 to 400 nm), and fused silica (FS, 155 to 400 nm). Following exposure, FEP film specimens were tensile tested to determine the ultimate tensile strength and elongation at failure as a function of the exposure duration for each wavelength range. The graphs show the effect of ultraviolet exposure on the mechanical properties of the FEP samples.

Dever, Joyce A.↗
NASA NTRS2002

Physical and Thermal Properties Evaluated of Teflon FEP Retrieved From the Hubble Space Telescope During Three Servicing Missions

Mechanical properties of aluminized Teflon fluorinated ethylene propylene (FEP) thermal control materials on the Hubble Space Telescope (HST) exposed to low Earth orbit for up to 9.7 years have significantly degraded, with extensive cracking occurring on orbit. The NASA Glenn Research Center and the NASA Goddard Space Flight Center have collaborated on analyzing the physical and thermal properties of aluminized FEP (FEP-Al, DuPont) materials retrieved in December 1999 during HST's third servicing mission (SM3A). Comparisons have been made to properties of FEP-Al retrieved during the first and second HST servicing missions, SM1 and SM2, in order to determine degradation processes for FEP on HST.

Dever, Joyce A.↗
NASA NTRS2020

FEP Extensible Proxy

The FEP Extensible Proxy (FEP) provides schema-less micro-service JSON communications for the Airspace Operations Laboratory at NASA Ames Research Center. The FEP grew out of a need to provide robust communications pathways for future airspace simulation capabilities for the lab. FEP provides a websocket based publish/subscribe communications pathway.

FEP Extensible Proxy↗
NASA NTRS1973

The use of FEP Teflon in solar cell cover technology

FEP plastic film was used as a cover and as an adhesive to bond cover glasses to silicon solar cells. Various anti-reflective coatings were applied to cells and subsequently covered with FEP. Short circuit currents were measured before and after application of the coating and of the FEP. FEP was bonded to seven of the nine differently coated cells, with no change in the total short circuit current in four cases.

Broder, J. D.↗
NASA NTRS1974

The use of FEP Teflon in solar cell cover technology

FEP plastic film was used as a cover and as an adhesive to bond cover glasses to silicon solar cells. Various anti-reflective coatings were applied to cells and subsequently covered with FEP. Short-circuit currents were measured before and after application of the coating and of the FEP. FEP bonded to seven of the nine differently coated cells, with no change in the total short circuit current in four cases.

Broder, J. D.↗