For this work, a series of six quinary rare-earth sulfides Ce 4+ 1.85 Eu 2+ 1.15 Na 0.30 SiS 7 , Ce 4+ 1.91 Eu 2+ 1.09 K 0.18 SiS 7 , Ce 4+ 1.96 Eu 2+ 1.04 Rb 0.08 SiS 7 , Ce 4+ 1.98 Eu 2+ 1.02 Cs 0.05 SiS 7 , Ce 4+ 1.97 Eu 2+ 1.03 Ag 0.06 SiS 7 , and Ce 4+ 1.50 Eu 2+ 1.50 CuSiS 7 were obtained in an alkali iodide flux using the boron-chalcogen mixture (BCM) method. Single crystal X-ray diffraction was used to determine the structures of the high quality single crystals that were grown; their elemental compositions were confirmed by energy-dispersive spectroscopy (EDS). The compounds crystallize in the hexagonal crystal system in the noncentrosymmetric space group P63. The crystal structure consists of a three-dimensional network composed of mixed cerium and europium bicapped trigonal prisms, isolated SiS4 tetrahedra, and monovalent metals (Na, K, Rb, Cs, Ag, and Cu) located in cavities created by linked Ce/EuS 8 polyhedra. The structures are charge-balanced when Ce and Eu are in their +4 and +2 oxidation states, respectively. The effective magnetic moment of Ce 1.50 4+ Eu 1.50 2+ CuSiS 7 determined from the temperature dependence of the magnetic susceptibility data is consistent with the presence of Ce 4+ and Eu 2+ . Clear correlations between the alkali ion site occupancy, the ionic radius of the alkali cations, and the average bond length of Ce 4+ /Eu 2+ –S, were established. UV–vis diffuse reflectance data were collected for Ce 1.50 4+ Eu 1.50 2+ CuSiS 7 and a band gap of 1.9(1) eV was established.
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗