The role of cesium suboxides in low-work-function surface layers studied by X-ray photoelectron spectroscopy - Ag-O-Cs

The oxidation of cesium on silver substrates has been studied using photoyield measurements and X-ray photoelectron spectroscopy. The occurrence of two O1s peaks in the core-level spectrum at 527.5 and 531.5-eV binding energy for cesium and oxygen exposures giving the optimum photoyield proves that two oxides of cesium exist in high-photoyield surfaces, and not Cs2O alone as previously thought. From the shape and position of the cesium peaks and the Auger parameter, the assignment of the O1s peaks at 527.5- and 531.5-eV binding energies to oxygen in Cs2O and Cs11O3, respectively, can be made. Hence the total cesium-oxygen layer is a mixed phase consisting of Cs2O + Cs11O3, approximately 20-40 A thick.

Yang, S.-J.↗

NASA NTRS1973

Photoemission from cesium-oxide-activated InGaAsP.

Zinc-doped InGaAsP quaternary III-V material of the proper composition range shows superior photoemission properties to either InGaAs or InAsP ternary material. The minority-carrier diffusion length in the quaternary material is at least as long as that in InAsP and much longer than observed in InGaAs. The barrier height at the InGaAsP-Cs2O interface is lowered by cooling, giving increased electron escape probability and new highs in quantum efficiency over a wide wavelength range. For example, a 1.06-micron quantum efficiency of 7.5%/incident photon was observed at -90 C.

James, L. W.↗

NASA NTRS1977

Low-work-function surfaces produced by cesium carbonate decomposition

Cesium carbonate (Cs2CO3) was heated to the decomposition temperature of approximately 600 C. The nonvolatile decomposition products were condensed on a nickel substrate while the carbon dioxide was removed by pumping. The deposited material is characterized by an effective work function of between 1.05 and 1.15 eV at 450 K and by photoemission in the visible and near-infrared region of the spectrum. It is suggested that the deposited material consists of Cs2O, possibly Cs2O2, and adsorbed cesium. Silver, evaporated from a heated silver bead, produced the typical photoemissive and thermionic properties of a silver-oxygen-cesium (S-1) photocathode. The material may be of interest for thermionic energy converters and for the formation of silver-oxygen-cesium photocathodes.

Briere, T. R.↗

NASA NTRS1981

X-ray photoemission studies of superficially oxidized cesium antimonide photoemitters

Superficially oxidized cesium antimonide photoemitting surfaces prepared in ultrahigh vacuum were studied by X-ray photoelectron spectroscopy. Oxidation of Cs3Sb to produce a surface with enhanced photosensitivity converts part of the antimony to elemental antimony and part of the cesium to cesium suboxide. The latter is identified on the basis of an O1 s peak at 531.3 eV, characteristic of Cs11O3. The production of Cs2O is not ruled out in this process since its signature at 527.5 eV is masked by an antimony shake-up peak at 527 eV.

Bates, C. W., Jr.↗

NASA NTRS1984

Enhanced Raman scattering from cesium suboxides on silver particles and the structure of S-1 photocathodes

An explanation is given for the results of recent enhanced Raman scattering studies of photomultiplier tubes with S-1 photocathode surfaces which indicated the presence of Cs11O3 but not Cs2O. The reason for the discrepancy between the currently accepted model of the S-1 and this recent result is discussed.

Bates, C. W., Jr.↗