NASA NTRS1995

A Preliminary Investigation of the Cr3Si-Mo Pseudo-Binary Phase Diagram

An investigation was undertaken to study the phase relations in Cr3Si alloyed with Mo varying from 10 to 83.5 wt. % of the material. Specimens were prepared from arc-melted buttons that were subsequently heat treated at 1673 K for 200 h and air quenched to room temperature to structures. Alloys containing more than 20 wt. % MO were primarily two-phase materials of M3Si and M5Si3, where M is (Cr,Mo). Three alloys contained less than 5% of a third phase, which also had the M5Si3 crystal structure. Differential thermal analysis (DTA) was performed on several specimens at temperatures up to 2073 K in order to determine a solidus curve for the M3Si phase. Since only one DTA peak was observed in each alloy, the M5Si3 phase must melt above 2073 K, the maximum temperature examined. A preliminary pseudo-binary phase diagram for (Cr,Mo)3Si and a portion of the 1673 K isothermal section of the Cr-Mo-Si ternary phase diagram are presented.

Dickerson, R. M.↗

NASA NTRS2014

Comparison of the Thermal Expansion Behavior of Several Intermetallic Silicide Alloys Between 293 and 1523 K

Thermal expansion measurements were conducted on hot-pressed CrSi(sub 2), TiSi(sub 2), W Si(sub 2) and a two-phase Cr-Mo-Si intermetallic alloy between 293 and 1523 K during three heat-cool cycles. The corrected thermal expansion, (L/L(sub 0)(sub thermal), varied with the absolute temperature, T, as (deltaL/L(sub 0)(sub thermal) = A(T-293)(sup 3) + B(T-293)(sup 2) + C(T-293) + D, where A, B, C and D are regression constants. Excellent reproducibility was observed for most of the materials after the first heat-up cycle. In some cases, the data from the first heatup cycle deviated from those determined in the subsequent cycles. This deviation was attributed to the presence of residual stresses developed during processing, which are relieved after the first heat-up cycle.

silicides↗