The growth of metastable peritectic compounds
The effects of directional solidification processing on the microstructural, compositional, and magnetic properties of high-melting-temperature, commercially important alloys which form from the liquid state via peritectic or eutectic type reactions were determined. Emphasis was placed on ferromagnetic compounds of the commercially important Co-Sm and Al-Mn systems. The primary dendrite spacing for eutectic Sm2Co17/Co scaled with negative square root of V and varied from approximately 50 microns for V 20 cm/h to hundreds of microns for V 10 cm/h. Since the crystal growth mechanism was dendritic rather than cooperative, the assoicated permanent magnet properties were rather poor. Magnetization as a function of sample orientation indicates that the easy axis of magnetization was primarily along the direction of solidification for the eutectic Sm2Co17/Co and peritectic SmCo5/Sm2Co17 compositions. For the Al-Mn case, magnetization and microstructural characterization suggest isotropic, polycrystalling growth for all solidification velocities studied.