NASA NTRS1989

The correlation between the temperature dependence of the CRSS and the formation of superlattice-intrinsic stacking faults in the nickel-base superalloy PWA 1480

The PWA 1480 nickel-base superalloy is known to exhibit a unique minimum in the critical resolved shear stress (CRSS) at about 400 C. This paper reports an observation of a deformation mechanism whose temperature dependence correlates exactly with the reduction in the CRSS. It was found that, after monotonic or cyclic deformation of PWA 1480 at 20 C, the deformation substructures typically contain high density of superlattice-intrinsic stacking faults (S-ISFs) within the gamma-prime precipitates. As the temperature of deformation is increased, the density of S-ISFs is reduced, until finally no faults are observed after deformation in the range from 400 to 705 C. The reduction in the fault density corresponds exactly to the reduction in the CRSS, and the temperature at which the fault density is zero corresponds with the minimum in the CRRS. Two possible mechanisms related to the presence of the S-ISFs in the alloy are considered.

Milligan, Walter W.↗
NASA NTRS1997

The Effects of Composition and gamma'/gamma Lattice Parameter Mismatch on the Critical Resolved Shear Stresses for Octahedral and Cube Slip in NiAlCrX Alloys

Prototypical single-crystal NiAlCrX superalloys were studied to examine the effects of the common major alloying elements, Co, Mo, Nb, Ta, Ti, and W, on yielding behavior. The alloys contained about 10 at. pct Cr, 60 vol pct of the gamma' phase, and about 3 at. pct of X in the gamma'. The critical resolved shear stresses (CRSSs) for octahedral and primary cube slip were measured at 760 C, which is about the peak strength temperature. The CRSS(sub oct) and CRSS(sub cube) are discussed in relation to those of Ni, (Al, X) gamma' alloys taken from the literature and the gamma'/gamma lattice mismatch. The CRSS(sub oct) of the gamma + gamma' alloys reflected a similar compositional dependence to that of both the CRSS(sub cube) of the gamma' phase and the gamma'/gamma lattice parameter mismatch. The CRSS(sub cube) of the gamma + gamma' alloys also reflected the compositional dependence of the gamma'/gamma mismatch, but bore no similarity to that of CRSS(sub cube) for gamma' alloys since it is controlled by the gamma matrix. The ratio of CRSS(sub cube)/CRSS(sub oct) was decreased by all alloying elements except Co, which increased the ratio. The decrease in CRSS(sub cube)/CRSS(sub oct) was related to the degree in which elements partition to the gamma' rather than the gamma phase.

Miner, R. V.↗
NASA NTRS1989

Deformation modeling and constitutive modeling for anisotropic superalloys

A study of deformation mechanisms in the single crystal superalloy PWA 1480 was conducted. Monotonic and cyclic tests were conducted from 20 to 1093 C. Both (001) and near-(123) crystals were tested, at strain rates of 0.5 and 50 percent/minute. The deformation behavior could be grouped into two temperature regimes: low temperatures, below 760 C; and high temperatures, above 820 to 950 C depending on the strain rate. At low temperatures, the mechanical behavior was very anisotropic. An orientation dependent CRSS, a tension-compression asymmetry, and anisotropic strain hardening were all observed. The material was deformed by planar octahedral slip. The anisotropic properties were correlated with the ease of cube cross-slip, as well as the number of active slip systems. At high temperatures, the material was isotropic, and deformed by homogeneous gamma by-pass. It was found that the temperature dependence of the formation of superlattice-intrinsic stacking faults was responsible for the local minimum in the CRSS of this alloy at 400 C. It was proposed that the cube cross-slip process must be reversible. This was used to explain the reversible tension-compression asymmetry, and was used to study models of cross-slip. As a result, the cross-slip model proposed by Paidar, Pope and Vitek was found to be consistent with the proposed slip reversibility. The results were related to anisotropic viscoplastic constitutive models. The model proposed by Walter and Jordan was found to be capable of modeling all aspects of the material anisotropy. Temperature and strain rate boundaries for the model were proposed, and guidelines for numerical experiments were proposed.

Milligan, Walter W.↗
NASA NTRS1991

Computed stress fields in GaAs during vertical Bridgman growth

The thermoelastic stress field of GaAs crystals grown by the vertical Bridgman method has been approximated using a linear elastic, axisymmetric stress model. The model included the effects due to the thermal field and the gravitational field, as well as the interaction with the ampoule, but did not fully account for the elastic anisotropy of the crystal. Realistic thermal fields for different furnace temperatures and insulation zone thicknesses were computed with a similar model. The difference between the Von Mises stress and the critical resolved shear stress (CRSS) was used as a measure of the number of dislocations present. Different sets of growth parameters were examined to determine which produced the lowest amount of stress in the crystal. Results show that the crystal-ampoule interaction is the most important parameter in dislocation generation. In addition, for the same sticking boundary conditions, concave interfaces have lower stress than convex interfaces.

Rosch, William↗
NASA NTRS2004

Slip Analysis in a Ni-base Superalloy

A Ni-base superalloy single crystal with Gamma/Gamma' structure was tested at room temperature along the , <110> and <111> directions. Consistent with previously reported investigations, this alloy did not obey the Schmid law and the CRSS (critical resolved shear stress) was noticeably lower for the <111>-oriented samples. Furthermore, the strain hardening rate decreased and the degree of deformation localization increased in the order of <111>, and <110> orientations. The appearance and orientation of deformation traces were found to depend on the loading orientation as well as the amount of strain. In general, when Gamma'-particles were sheared, the traces followed the expected octahedral shear planes. It is demonstrated that the wavy deformation traces that do not follow the {111} planes are associated with changes in the gamma-channels width and the falling off of the gamma-particles. In this paper the evolution of deformation bands are discussed in terms of plastic localization at microscopic, mesoscopic and macroscopic levels.

Westbrooke, Eboni F.↗