Engineering Papers⌕ Search

SEARCH · Engineering Papers

Results for “CEOS”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Microstructural characterization and equibiaxial flexural strength of CeO 2 and Ti-doped CeO 2

In this study, the synthesis of CeO 2 and titanium dioxide (TiO 2 ) doped CeO 2 (TDC) monoliths are investigated, and their fracture strength is assessed using an equibiaxial flexure testing technique at room temperature. Pellets were synthesized using conventional powder processing and sintering methods to produce the desired characteristics. The TiO 2 dopant concentration was optimized at 0.1 wt % TiO 2 to obtain dense, solid-solution pellets with an enhanced grain microstructure. A ball-on-ring fixture was used to obtain the TRS and Weibull parameters of over 30 pellets for CeO 2 and 0.1 wt % TDC to compare fracture behavior. The TRS of CeO 2 pellets ranged from 88 to 160 MPa and the TRS of 0.1 wt % TDC pellets ranged from 102 to 171 MPa, both being consistent with published values. Weibull parameters, such as characteristic strength and Weibull modulus, were extracted as 129 MPa and 8.5 for CeO 2 and 150 MPa and 9.3 for 0.1 wt % TDC, respectively. Although Hertzian contact damage was observed on compressive surfaces, failure initiation occurred on the tensile surfaces of both types of samples. Fracture surface analysis for CeO 2 indicated a predominantly intergranular fracture while 0.1 wt % TDC had a predominantly transgranular fracture mode. Finally, the TRS of 0.1 wt % TDC resulted in increased Weibull parameters when compared to CeO 2 , indicating sample chemistry and microstructure impact mechanical behavior for these samples.

36 MATERIALS SCIENCE↗
DOE OSTI2025

CO 2 Oxidative Ethane Dehydrogenation on CeO 2 /SiO 2 ‐Supported NiFe 3 Catalysts

CO 2 -assisted oxidative dehydrogenation of ethane is a sustainable alternative to steam cracking for ethylene production. In this study, a series of CeO 2 on SiO 2 supported NiFe 3 catalysts were synthesized by incipient wetness impregnation and tested for oxidative dehydrogenation performance. The CeO 2 /SiO 2 supported catalysts with high weight loading of CeO 2 (50%–75%) provided higher activity than the lower CeO 2 (0%–25%) loaded catalysts (with ethylene production rates of 0.62–0.98 µmol/g cat /s and 0.19–0.3 µmol/g cat /s, respectively) while maintaining high ethylene selectivity (43%–45%). In contrast, the NiFe 3 supported on only CeO 2 also exhibited high activity (ethylene production rate of 0.71 µmol/g cat /s), but the ethylene selectivity (16%) was greatly decreased compared to the mixed system. Temperature programmed reduction, X-ray diffraction, and Raman spectroscopy all indicate the creation of a solid solution of the Fe and Ni doped into the CeO 2 crystal structure in the catalysts with high CeO 2 loading/bulk CeO 2 support. Here, the high ethylene selectivity in the high CeO 2 loading catalysts indicates that the Fe is preferentially creating the solid solution, with the decrease in selectivity observed in the CeO 2 -only supported catalyst likely resulting from CeO 2 interacting directly with Ni, creating Ni-CeO X interfaces that are known active sites for the unwanted side reaction of dry reforming.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2024

The Triple Component Interface of Ni–Co–Ce: Growth, Chemical State, and Stability of NiCo Bimetallic Particles on Reducible CeO 2 (111) Thin Films

The growth of NiCo particles at low coverages over reducible CeO 2 (111) thin films producing a triple interface between Ni-Co-Ce was investigated by scanning tunneling microscopy (STM) and X-ray photoelectron spectroscopy (XPS), which was compared to that of monometallic Ni and Co particles. XPS data show that deposition of either Ni or Co on CeO 2 at 300 K causes a partial reduction of Ce 4+ cations to Ce 3+ ions. At 0.3 monolayer (ML), XPS detects Co 2+ on CeO 2 . However, both Ni 0 and Ni 2+ are present as major species at 300 K and annealing causes a significant increase of Ni 2+ in Ni particles. Deposition of 0.3 ML Co over 0.3 ML Ni on CeO 2 at 300 K induces reduction of Ni 2+ to metallic Ni and Ni 0 was found as predominant species. Unlike for Co/CeO 2 , metallic Co was also present over the Co-Ni/CeO 2 surface in addition to Co 2+ . Further, this behavior indicates the formation of NiCo bimetallic particles with the possibility of Co diffusion to the interface of Ni/ceria. With heating, the intermixing of Ni and Co atoms in bimetallic particles on CeO 2 was facilitated. Furthermore, oxidation of both metals and ceria occurred as a result of the diffusion of lattice oxygen from the bulk of ceria to the surface. A slight increase in Ni 2+ was observed after heating Co-Ni/CeO 2 to 500 K or higher. Co became Co 2+ with heating to 800 K. Our STM results confirm the formation of NiCo bimetallic particles on CeO 2 at 300 K and further suggest that the addition of Co can help inhibit the sintering of Ni particles at higher temperatures. Bimetallic particles were also obtained by depositing Ni over existing Co particles on CeO 2 . However, our XPS data demonstrate that the deposition order of Co and Ni plays a role in the chemical state of these two metals in bimetallic particles, likely attributed to the difference in their compositions at the bimetallic particle surface as well as the metal-support interface.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2025

CeO 2 Promoted CuO/MgO-Al 2 O 3 Catalyst with Enhanced Activity and Water-Resistance for CO Oxidation

Copper (Cu)-based catalysts have emerged as cost-effective and sustainable alternatives to noble metal systems (e.g., Pt, Pd) for catalytic CO oxidation. However, their practical application is hindered by insufficient low-temperature activity and rapid deactivation under wet conditions containing moisture. To address these challenges, this work introduces CeO 2 -modified CuO/MgO-Al 2 O 3 (Cu-Ce/MA) catalysts, strategically designed to enhance the catalytic performance and water resistance simultaneously. These catalytic materials were evaluated for CO oxidation under both dry and humid conditions, revealing that CeO 2 modification significantly improves the low-temperature activity. Specifically, the optimal catalyst, Cu-30Ce/MA, achieved a 50% CO conversion temperature (T 50 ) of 151 °C, a marked reduction from 218 °C on Cu/MA reference catalyst. Furthermore, the water resistance improves in a CeO 2 content-dependent manner, with higher CeO 2 loadings imparting greater stability in humid environments. Detailed characterizations demonstrate that CeO 2 promotes the dispersion of CuO and stabilizes Cu sites, while also enhancing the low-temperature reducibility and CO adsorption capacity. Crucially, CeO 2 modification suppresses the competitive H 2 O adsorption, mitigating water-induced deactivation. These synergistic effects collectively rationalize the superior activity and durability of Cu-Ce/MA catalysts. By elucidating the dual role of CeO 2 in optimizing Cu-based systems, this study advances the rational design of cost-effective catalysts for real-world CO emission control, particularly under water-rich industrial conditions.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2026

Enhancing Value-Added CO Production from CO 2 Hydrogenation by Tailoring the Ru-CeO 2 Interface on MgO

Catalytic CO 2 hydrogenation presents a promising route for converting CO 2 into valuable products, contributing to the mitigation of net CO 2 emissions. Supported Ru catalysts have recently gained considerable attention due to their tunability for 100% CO selectivity via the reverse water-gas shift pathway, effectively suppressing the competing methanation route. However, despite achieving full CO selectivity, the overall CO yield remains limited by low CO 2 conversion, necessitating further improvement. In this work, CeO 2 was introduced to modify a Ru/MgO single-atom catalyst for CO 2 hydrogenation. The resulting Ru-CeO 2 /MgO catalyst, featuring abundant Ru-CeO 2 interfacial sites, exhibited a favorable balance of CO 2 conversion and CO selectivity, delivering the highest CO yield (32.5% at 500 °C), which is 9.0 and 1.8 times higher than that on Ru/MgO (3.6%) and Ru/CeO 2 (18.4%), respectively. Although the CO selectivity was slightly compromised due to enhanced CO binding at Ru-CeO 2 interfacial sites, H 2 was more efficiently activated at these interfaces and readily reacted with CO 2 adsorbed on CeO 2 -MgO surfaces, thereby boosting the CO 2 hydrogenation activity and CO yield. This study underscores the critical role of Ru-metal oxide interface engineering in improving CO yield and advancing the rational design of highly efficient Ru catalysts for CO production from CO 2 hydrogenation.

36 MATERIALS SCIENCE↗
DOE OSTI2026

In Situ Studies of Ru-CeO 2 –TiO 2 Catalysts for Selective CO 2 Hydrogenation to Methane: Importance of Metal ↔ Oxide–Oxide Interactions

Here, this work investigates Ru-CeO 2 -TiO 2 catalysts for the CO 2 methanation reaction and compares their performance with previously studied Ru-CeO 2 systems. Despite the lower Ru loading, the TiO 2 -containing catalysts exhibit significantly higher activity. To understand this behavior, in situ X-ray absorption spectroscopy (XAS) was carried out at the Ru K-edge and Ce L 3 -edge. Unlike Ru-CeO 2 , which displays reversible redox behavior of Ru, the Ru-CeO 2 -TiO 2 catalysts show irreversible Ru reduction and a substantially higher fraction of Ce 3+ species under all tested conditions (H 2 , CO 2 , H 2 /CO 2 ). The stabilization of metallic Ru during methanation, together with the enhanced formation of Ce 3+ promoted by TiO 2 through interfacial electronic transfer, accounts for their superior performance. Complementary in situ DRIFTS measurements reveal the formation and rapid consumption of bidentate carbonates and formates. These species act as a key intermediate in methane formation. Overall, these findings highlight the crucial role of the mixed CeO 2 -TiO 2 oxide in tuning the surface chemistry of the catalysts by stabilizing metallic Ru, enhancing ceria reducibility, and promoting efficient reaction pathways for CO 2 methanation. The manipulation of metal↔oxide-oxide interactions can be a very useful tool when dealing with the valorization of CO 2 .

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2025

Visualizing Size-Dependent Dynamics of CeO 2-δ {100}-Supported CoO x Nanoparticles Under CO 2 Hydrogenation Conditions

Carbon dioxide is a major greenhouse gas. In order to optimize processes focused on its chemical valorization, one needs detailed information about the effects of CO 2 and/or CO 2 /H 2 mixtures on the structure and morphology of metal/oxide catalysts. Here, in this study, the evolution of a catalyst with cobalt supported on CeO 2 -cube nanostructures under CO 2 hydrogenation conditions was investigated by using a set of in situ characterization techniques (X-ray absorption fine structure, X-ray diffraction, diffuse reflectance infrared Fourier transform spectroscopy, and environmental transmission electron microscopy (TEM)). The {100} facets of the ceria support displayed an unexpectedly high stability due to strong interactions with the aggregates of cobalt oxide. A significant influence of interfacial bonding between CoO x and CeO 2-δ {100} is evident through a clear preference in the orientation of CoO x nanoparticles (NPs) with respect to the substrate. For initially reduced Co/CeO 2 -cube nanostructures, a kinetically controlled oxidation of cobalt upon the introduction of CO 2 was observed during the early stages of CO 2 hydrogenation. Environmental TEM revealed the size-dependent morphological behavior of cobalt oxide NPs due to strong interactions with the CeO 2 {100} surface. When the environment was switched from H 2 to a mixture of H 2 and CO 2 at 250 °C, small CoO x NPs (in the largest dimension < 2.5 nm) rapidly transformed from a pyramidal three-dimensional (3D) form to a planar, monatomic layer attached to the concurrently oxidized CeO 2-δ {100} surface. This maximizes the number of sites available for the binding of CO 2 or reaction intermediates. The shape transformation reflected the oxophilic character of cobalt and strong metal–support interactions. The removal of CO 2 from the gas phase led to a reduction of the cobalt oxide NPs by hydrogen and a reversible two-dimensional → 3D transformation. In contrast, no significant morphological changes, apart from further oxidation, were observed for big CoO x NPs (in the largest dimension > 3 nm). These trends are not seen for nanoparticles of noble metals. The observed morphological and structural changes in the small CoO x NPs affected the stability of reaction intermediates and modified the selectivity of the CoO x /CeO 2 catalyst system for methane production.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Sparsely Dispersed CeO x ‑Stabilized Pt Nanoparticles Overcome Pt Loading–Durability Trade-Off for Highly Durable Heavy-Duty Fuel Cells

Proton-exchange-membrane fuel cells (PEMFCs) are clean and sustainable mobile power sources for transportation. Recently, their deployment in heavy-duty vehicles (HDVs) has attracted growing interest owing to their high energy scalability and lower infrastructure requirements. However, to meet the stringent requirements for efficiency and long-term durability for HDV applications, PEMFCs typically employ a relatively high platinum group metal (PGM) loading (>0.2 mg PGM /cm 2 ). This elevated PGM loading significantly increases the stack and system costs, surpassing the U.S. Department of Energy (DOE) target of $\$ 60$/kW for commercial viability. Reducing PGM loading while maintaining performance and durability remains a central challenge for HDV fuel cells. Here we exploit metal oxide–Pt interactions and utilize the strong CeO x –Pt interaction to design a CeO x @Pt catalyst structure with exceptional durability. At a low total PGM loading (0.1 mg PGM /cm 2 ), the CeO x @Pt/C catalyst demonstrates high fuel cell performance (8.8 kW/g PGM ) and stability (power retention >90%) after the challenging HDV durability testing (90,000 accelerated-stress-test cycles). With the CeO x @Pt/C catalyst, we showcase over 70% reduction in Pt cost from the M2FCT target (to $\$ 9$/kW), highlighting its promising potential for enabling stable and cost-effective fuel cell systems for heavy-duty applications.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2025

Porous CeO 2 /CuO Heterostructure for Efficient Hydrogen Evolution Reaction in an Acidic Medium

A composite electrocatalyst CeO 2 /CuO is fabricated for the hydrogen evolution reaction (HER) via a simple, facile, one‐step hydrothermal method, using F‐127 as a template and structure directing agent. The prepared composite CeO 2 /CuO shows top‐notch HER activities with a small overpotential of 98 mV at 10 mA cm −2 and just 160 mV overpotential to attain a current density of 50 mA cm −2 with good stability for 20 h in an acidic medium. The enhanced catalytic activities of CeO 2 /CuO nanocomposite are attributed to their synergetic interface interaction, which lead to improved conductivity, reactive sites, and oxygen vacancies in their lattices. This study aims to advance the development of earth‐abundant transition metal oxides–based electrocatalysts as economical, durable, and efficient HER electrocatalysts to replace noble metal–based materials in the future.

Chemistry↗
DOE OSTI2024

Integration of CeO 2 -Based Memristor with Vertically Aligned Nanocomposite Thin Film: Enabling Selective Conductive Filament Formation for High-Performance Electronic Synapses

The CeO 2 -based memristor has attracted significant attention due to its intrinsic resistive switching (RS) properties, large on/off ratio, and great plasticity, making it a promising candidate for artificial synapses. However, significant challenges such as high power consumption and poor device reliability hinder its broad application in neuromorphic microchips. To tackle these issues, in this work, we design a novel bilayer (BL) memristor by integrating a CeO 2 -based memristor with a Co-CeO 2 vertically aligned nanocomposite (VAN) layer and compare it with the single layer (SL) memristor. Preliminary electrical testing reveals that the BL memristor offers a reduced set/reset voltage (~67% lower), a higher on/off ratio (~5 × 10 2 ), enhanced device reliability, and improved device-to-device variation compared to the SL memristor. Insight from COMSOL simulation, coupled with microstructural analysis, provides a comprehensive elucidation on how the VAN layer facilitates the selective conductive filament (CF) formation. Subsequently, the plasticity of the BL memristor is evaluated through long-term potentiation/depression (LTP/LTD), paired-pulse facilitation (PPF), and spike-time-dependent plasticity (STDP). The spiking neural network (SNN) built upon the BL memristor achieves remarkable accuracy (~94%) after only 12 iterations, underscoring its potential for high-performance neural networks.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2025

Tuning Catalytic Reactivity via Wetting Control through Oxygen Vacancies: Ru Clusters on Anatase TiO 2 and CeO 2 Supports

The shape of supported metal particles regulates their catalytic reactivity and is determined by the degree of wetting between the metal particle and the support surface. Flattened particles that wet support surfaces were reported in various catalytic systems, particularly in the subnanometer size regime. Such consequential metal–support wetting phenomena are poorly understood, and methods to study them on powder catalysts under realistic conditions are lacking. Here, we investigate the size-dependent wetting behaviors of Ru particles on two reducible-oxide supports, anatase TiO 2 (TiO 2 -A) and CeO 2 , under reducing catalytic conditions. X-ray absorption spectroscopy (XAS), low-energy ion scattering (LEIS), and density functional theory (DFT) are combined to determine the shape of Ru particles. Ru particles remain three-dimensional without wetting the TiO 2 -A support within the coverage range studied (0.06–0.98 Ru nm –2 ). In contrast, at low coverages (<0.25 Ru nm –2 ), Ru wets the CeO 2 support to form flat, disordered structures. The higher wettability of CeO 2 than TiO 2 -A is attributed to oxygen vacancies in the near-surface region. The shape difference between small Ru particles or clusters on the two supports leads to drastically contrasting catalytic reactivities in polyolefin hydrogenolysis, despite similar diameters. As a result, this work highlights the implications of metal–support wetting, or cluster shape, on catalytic behaviors of small metal clusters, while establishing the foundation for future systematic studies of such a phenomenon in realistic systems, by delivering a multitechnique methodology and revealing governing fundamental principles.

42 ENGINEERING↗
DOE OSTI2026

Transformation of CeO 2 Nanoparticles into Atomically Dispersed Ce Cations Leads to Enhanced Reactivity for Automotive Emissions Control

Nanosized cerium oxide (CeO 2 ) has been extensively used as the oxygen storage component in automotive emission control systems. However, the possible influence of atomically dispersed Ce in these catalysts has not been recognized. Here, in this study, we demonstrate the controllable transformation of ceria nanoparticles into isolated cerium cations on γ-Al 2 O 3 via reductive atom trapping in 10% H 2 at 800 °C, achieving over half-monolayer coverage. Dispersed Ce 1 ions anchored by surface penta- and octa-coordinated Al sites exhibit outstanding thermal stability in air up to 500 °C, enabling further loading of active metals with well-defined catalyst structures. With this strategy, supported single-atom Rh 1 surrounded by dispersed Ce 1 is confirmed to exhibit much superior performance to Rh 1 on bare Al 2 O 3 or nanocrystalline CeO 2 in catalyzing NO reduction by CO, exhibiting a striking one-order-of-magnitude increase in activity. Dispersed Ce 1 exhibits greatly enhanced oxygen transfer capability compared to ceria nanoparticles and introduces a modified reaction mechanism that involves an adjacent Rh 1 –Ce 1 motif, resulting in a greatly decreased activation barrier (from 192 to 96 kJ/mol). The reactivity enhancements are also seen with Ce 1 -promoted Pt nanoparticles for oxidation of CO and hydrocarbons.

Jiang, Dong [Washington State Univ., Pullman, WA (↗
DOE OSTI2025

Enhancing the low-temperature performance of Pt-based three-way catalysts using CeO 2 (core)@ZrO 2 (shell) supports

Developing robust Pt/CeO 2 -based three-way catalysts (TWCs) with enhanced oxygen buffering capability and low-temperature activity is highly desirable. In this study, a new TWC family, Pt/(1 − x)CeO 2 (core)@xZrO 2 (shell) (where x = 0–0.5), was prepared and evaluated at degreened (DG) and hydrothermally aged (HTA) states. Incorporation of 0.1 molar concentration of ZrO 2 resulted in a decreased temperature that 50% (T 50 ) (CO: 167 °C, THCs: 218 °C, NO: 228 °C) and 90% (T 90 ) (CO: 207 °C, THCs: 237 °C, NO: 244 °C) conversions achieved over HTA 1.8 wt% Pt/0.9CeO 2 @0.1ZrO 2 compared to the HTA 1.8 wt% Pt/CeO 2 sphere (CO: T50,90 = 179, 222 °C, THCs: 234, 252 °C, NO x : 240, 260 °C). An enhanced oxygen storage capacity and oxygen release rate were observed over Pt/0.9CeO 2 @0.1ZrO 2 compared to the Pt/CeO 2 sphere. Increasing the ZrO 2 molar concentration to values greater than 0.2 resulted in increased T 50 s (224, 265 274 °C) and T 90 s (251, 289, 292 °C) for CO, THCs, and NO x , respectively, over 1.8 wt.% Pt/0.5CeO 2 @0.5ZrO 2 . Overall, this work highlights the potential of forming a ZrO 2 shell on CeO 2 spheres as a support for TWC applications.

Liu, Chih-Han [State Univ. of New York (SUNY), Buf↗
DOE OSTI2024

LDRD 227829: Multifunctional Composite LDRD: Radiation Effect on CeO 2 -HDPE Composites

Commercial high-density polyethylene (HDPE) is lightweight with excellent mechanical properties but has limited thermal stability. To enhance this, lanthanide-based nanomaterials like CeO 2 were mixed with HDPE. Using a twin-screw extruder improved dispersion. This study examines the effects of neutron, X-rays and gamma radiation on the crystallinity of polymer of CeO 2 -HDPE composites.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Kinetic Understanding of Field-Induced Phase Transition from Tetragonal to Ferroelectric Orthorhombic Phase in Ferroelectric CeO 2 –HfO 2 –ZrO 2 Films

The ferroelectric properties and structural phase transition behaviors of fluorite-type CeO 2 −HfO 2 −ZrO 2 films were investigated. The epitaxial films on indium tin oxide (ITO) (111)/yttria-stabilized zirconia (YSZ) (111) substrates were grown through pulsed laser deposition at room temperature and subsequently heat-treated at 1000 °C under a N 2 gas flow. The crystalline phases and Curie temperatures of the films were investigated by X-ray diffraction. An increase in the Ce or Zr content in the films led to a higher crystallographic symmetry, such as orthorhombic or tetragonal. In addition, electrical characterization revealed that the orthorhombic films and some of the tetragonal films displayed ferroelectricity. This was due to the field-induced phase transition from the tetragonal to ferroelectric orthorhombic phase in the films, where the Curie temperatures were relatively low. The tetragonal metastable phase was kinetically frozen and could not change into the stable orthorhombic phase at such a low temperature. The critical electric field where the field-induced phase transition occurred was below 0.8 MV/cm, which was sufficiently small compared to the coercive field. These results evidence the kinetic driving force that causes a field-induced phase transition from the paraelectric tetragonal phase to the ferroelectric orthorhombic phase in HfO 2 -based ferroelectrics. They also enhance our understanding of the thermodynamic phase stabilities of HfO 2 -based material polymorphs.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Kinetics and Thermodynamics of Sr Permeation in CeO 2 -Based Barrier Layers for Solid-Oxide Electrolyzer Cells

Solid-oxide electrolyzer cells (SOECs) convert steam to hydrogen efficiently at high temperatures. However, during operation, the diffusion of cations or impurities through the cells due to electrode degradation can cause unwanted secondary phases to form, which may degrade device performance. Here, in this study, we use atomistic and mesoscale simulations coupled with experimental analysis to study the diffusion of Sr through the Gd-doped CeO 2 (GDC) barrier layer used to protect the yttria-stabilized zirconia (YSZ) electrolyte in SOECs. From our atomistic calculations, we find Sr diffusion to be negligibly slow in bulk GDC; however, surface diffusion is much more favorable. Subsequent mesoscale simulations show that Sr diffusion is activated when the porosity of GDC exceeds ∼10% and significantly exceeds diffusion in bulk and grain boundary regions. We also find that SrO-based species can accumulate at GDC surfaces; however, SrO aggregation and coarsening will be limited by the large lattice mismatch between GDC and SrO. Energy-dispersive X-ray spectroscopy (EDS) and electron diffraction confirm that Sr can accumulate within GDC pores and form disperse Sr-containing secondary phases. Altogether, Sr diffusion in dense GDC is unlikely to give rise to thick SrO layers, which would severely limit device performance. The formation of Sr-containing secondary phases can largely be avoided by restricting the porosity of the GDC layer as much as possible.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Spin Decoherence Dynamics of Er 3+ in CeO 2 Films

Developing telecom-compatible spin-photon interfaces is essential towards scalable quantum networks. Erbium ions (Er 3+ ) exhibit a unique combination of a telecom (1.5 mu m) optical transition and an effective spin-1=2 ground state, but identifying a host that enables heterogeneous device integration while preserving long optical and spin coherence remains an open challenge. In this work, we explore the potential of Er 3+ :CeO 2 films on silicon and study the Er 3+ spin coherence, offering low nuclear spin density and the potential for on-chip integration. We demonstrate a 38.8 mu s spin coherence, which can be extended to 176.4 mu s with dynamical decoupling. Pairing experiments with cluster correlation expansion calculations, we identify spectral diffusion induced by bath Er 3+ spin flip-flops as the dominant decoherence mechanism and provide pathways to millisecond-scale coherence.

36 MATERIALS SCIENCE↗