DOE OSTI2026

Modeling Radiolysis and Chemical Reactions during Dry Storage of Aluminum-clad Spent Nuclear Fuel

After aluminum-clad spent nuclear fuel (ASNF) is removed from the reactor, it is initially stored in spent fuel pools, which are specially designed water-filled basins that provide temporary cooling to reduce the temperature of the fuel assemblies and provide radiation shielding. ASNF continues to generate heat due to the radioactive decay of elements within the fuel, which persists for many years post-shutdown as the residual radioactive products decay into more stable elements. During the wet storage period, an oxyhydroxide layer composed of boehmite/bayerite forms on the surfaces of the aluminum cladding from exposure to water in the pools. Road-ready packaging for long-term disposition of the ASNF involves dry storage in helium backfilled DOE standard canisters (DSCs). When the ASNF is removed from water storage and dried, most of the water is removed, but some physisorbed and chemisorbed water remains in the oxyhydroxide layers. This residual water can produce hydrogen when exposed to radiation from the ASNF during dry storage. Predicting hydrogen accumulation over time in the DSCs is critical for long-term storage considerations. Previous modeling efforts have developed coupled computational fluid dynamics (CFD)-chemical models to simulate temperature, pressure, and gas phase concentrations within the DSCs. These models use the thermal field predicted by CFD as input to a radiolysis model for the gas phase and the surface oxyhydroxide layer chemistry. Given the long storage period of the DSCs and the impracticality of long-term experiments, a simulation-based approach is necessary to assess chemical evolution within the canisters. This study advances the development of a modeling framework designed to simulate the chemical evolution of spent fuel canisters. Both thermal and radiation-driven reactions are considered, with radiation kinetics quantified using G-values. Sensitivity analysis identifies key parameters influencing species composition. Reaction pathway diagrams offer insight into dominant species formation routes, enabling more effective comparisons between model predictions and experimental observations, particularly regarding the production of hydrogen. Results show that the model predicts significant hydrogen gas production with minimal oxygen generation, primarily due to hydrogen formation via boehmite pathways. These findings underscore the importance of accurately characterizing surface-bound species and radiolysis kinetics. A deeper understanding of these mechanisms is critical for evaluating the long-term safety of nuclear waste storage.

12 - MGMT OF RADIOACTIVE AND NON-RADIOACTIVE WASTE↗
DOE OSTI2024

Considerations for Defining G-Values for Aluminum-Clad Spent Nuclear Fuel

Sealed-canister dry storage of aluminum-clad spent nuclear fuel (ASNF) generated by research reactors is an alternative to current storage and disposition pathways as directed by the U.S. Department of Energy. The major challenge faced for this storage approach is radiolytic H 2 generation, including from the aluminum (oxy)hydroxide layers on the surface of ASNF. Experimental and modeling activities have been carried out to characterize the radiolytic yield as part of a DOE-sponsored research program to develop the technical basis for ASNF dry storage. The G-value is a commonly way to report results of radiolysis testing and is defined as the radiolytic yield of a species (e.g. molecular hydrogen) per unit radiation energy deposited into the material system. An independent technical review of the ASNF dry storage technical basis performed by Pacific Northwest National Laboratory raised questions about differences in G-value definitions used for experiments on ASNF surrogates consisting of aluminum samples with adherent (oxy)hydroxides compared to G-values reported in prior literature and how the magnitudes compared between different studies. Material systems resembling ASNF pose complications for measuring/defining G-values to predict the evolution of H 2 in a sealed canister, including i) accounting for radiolytic yields potentially arising from multiple sources, i.e., residual free (vapor), physisorbed, and chemisorbed/chemically bound waters; ii) deciding what portions of the multi-material system to include in the absorbed energy (radiation dose) calculation, considering possible energy exchange between materials as well as measurement limitations, and iii) capturing variations in G-value associated with non-linear yield vs. dose curves and/or dependence on the cover gas. This report summarizes previous literature information on radiolytic H 2 generation and associated G-values from mixed-material systems (generally oxides in contact with water or organic compounds) and from (oxy)hydroxides/hydrates to compare with the definitions and values for ASNF surrogate samples containing adherent aluminum (oxy)hydroxides.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Milestone 1.2.16. Reconciling the Impacts of Thermal Pretreatment on Radiation-Induced H2 Generation from Aluminum-Clad Spent Nuclear Fuel Surrogate Materials

To support the technical basis for the extended dry storage of aluminum-clad spent nuclear fuel (ASNF), thermal pretreatment procedures to minimize the radiation-induced generation of molecular hydrogen (H2) have been investigated. The aim of thermal pretreatment is to eliminate the residual adsorbed water content on the ASNF’s corrosion layers, precursors for H2 generation. To date, irradiation studies in this area have found conflicting results for the effectiveness of thermal pretreatment procedures. The aim of this study was to reconcile those differences. However, the presented results, which utilized a modified in situ thermal pretreatment procedure, afforded H2 yield data that further indicates that thermal pretreatment does not significantly reduce the radiation-induced yield of H2 from gamma irradiated ASNF surrogate materials. Assessment of the differences between thermal pretreatment studies suggests that stainless-steel—present in the irradiation setup of studies that demonstrated a reduction in the yield of H2 with thermal pretreatment—may afford not only unanticipated interfacial chemistry, but also the formation and radiolytic contribution of iron oxides to the chemistry underpinning the formation of H2 in these systems. Given the Department of Energy Standard Canister—proposed for the extended dry storage of ASNF—is predominantly composed of stainless-steel, the potential contribution of stainless-steel and its corrosion layers to radiolytic H2 production should be further investigated. This research was funded by the U.S. Department of Environmental Management, Office of Technology Development, under contract DE-AC07-05ID14517.

38 RADIATION CHEMISTRY, RADIOCHEMISTRY, AND NUCLEA↗
DOE OSTI2024

Review and Summary of Corrosion Behavior for Aluminum-Clad Spent Nuclear Fuel in Dry Storage

A description of the corrosion behavior of aluminum alloys used for cladding on aluminum-based, aluminum-clad nuclear fuel used in research reactors under potential dry storage conditions has been compiled. An evaluation is made of potential additional corrosion with water postulated to not be removed during drying. The relative humidity (RH) produced by typical dryness criteria for industrial spent nuclear fuel drying is expected to be low, particularly at high temperatures (17% RH at 20°C and lower at higher temperatures). Existing corrosion data suggests that negligible vapor-phase corrosion of aluminum is expected at such low humidity, even for nominally bare aluminum surfaces. That is, the predicted relative humidity from free water (e.g., 17% RH) is below the “critical” relative humidity (~40% RH at room temperature), below which no significant corrosion is observed for bare aluminum. Furthermore, reported room-temperature corrosion rates are very low even under saturated (100% RH) water vapor. Existing results showing significant vapor-phase corrosion corresponded specifically to conditions of high temper ed with high relative humidity. A relatively large reservoir of (chemically bound) water exists in the aluminum (oxy)hydroxide films on the SNF cladding surface. The estimated total could saturate the gas even at relatively high temperature if fully released; however, its release as molecular water is expected to only be plausible if the temperature during storage exceeds both the drying temperature and the threshold for thermal decomposition of the trihydroxides (~220°C). Therefore, the combination of high temperature and high relative humidity that could drive significant corrosion is considered implausible during sealed dry storage following an appropriate drying process, to include >220°C drying for canisters that may approach or exceed this temperature during storage. Vapor-phase testing of aluminum samples with an adherent (oxy)hydroxide layer, prepared in liquid water to resemble those on actual aluminum-clad spent nuclear fuel (ASNF), did not observe evidence of additional corrosion even at combined high-temperature (up to 180°C) and high-humidity (up to 100% RH) conditions. Instead, small net mass losses were observed for most specimens and attributed to dehydration of the samples, which had been air-dried only prior to testing. ASNF being moved to dry storage is expected to have an existing (oxy)hydroxide film, suggesting that the cladding will be less prone to additional corrosion than bare aluminum metal. If significant corrosion did occur during sealed storage, the overall extent and impact is expected to be small. Corrosion post-closure of a canister would not alter the total amount of hydrogen in the canister, so it would have no effect on the maximum H 2 release already assessed in existing bounding calculations. In addition, the total amount of water in a 25-µm dense bayerite film would consume a only ~8 µm additional aluminum metal on average, if fully consumed by oxidizing aluminum metal to Al 2 O 3 . These conclusions are consistent with ASNF-in-canister simulations to date, which included a reaction pathway for corrosion using kinetics from previous literature and believed to be conservative and predicted very low rates of corrosion.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2025

An approach for spent nuclear fuel containment integrity verification using gas tagging

Verification of containment integrity is required for spent nuclear fuel (SNF) managed by the commercial nuclear industry and U.S. Department of Energy (DOE), especially after extended storage. Certain SNF storage systems, such as the DOE road-ready dry storage system, hold several packaged containments within a welded over-canister. These packaged containments are called Department of Energy Standard Canisters (DOESCs). DOESC leakage identification is challenging because their containment boundary cannot be accessed for testing and their contents (i.e., SNF and fill gas) are often similar. There are concerns that this could result in costly characterization and repackaging operations of DOE road-ready dry storage systems if compromised DOESCs are suspected. Here, to address these concerns, this paper presents an approach for applying a gas tagging process using xenon to uniquely identify compromised inaccessible containments following extended storage. The containments considered for this application are seven DOESCs, each packaged within a single over-canister. Two different SNF loading configurations from the Advanced Test Reactor and Fort Saint Vrain nuclear power plant are considered. These configurations are used to represent research reactor aluminum-clad spent nuclear fuel (ASNF) and TRi-structural ISOtropic (TRISO) SNF types. Results for this application show that for ASNF and TRISO type fuels for which the selected fuels are representative, the volume of taggant required at loading is determined primarily by the lower detection limit and leak rate of taggant from a compromised DOESC, rather than the amount of fission-generated xenon in the loaded fuel. While the application presented is suited for larger leaks, smaller leaks could be detected by modifying certain design parameters. This gas tagging approach can also be applied to other DOE containments and advanced reactor SNF storage systems.

07 - ISOTOPES AND RADIATION SOURCES↗
DOE OSTI2025

Impact of corrosion layer composition and thermal pretreatment on the radiolytic generation of molecular hydrogen from aluminum alloys

To fully evaluate the feasibility of extending the dry storage of aluminum-clad spent nuclear fuel (ASNF) in helium-backfilled cannisters, the amount of radiation-induced molecular hydrogen (H 2 ) generated and the impact of absorbed radiation dose on the ASNF corrosion layer composition must be accurately assessed. Here, in this study, we report a slowing in the rate of radiolytic H 2 generation for pre-corroded AA1100 and AA6061 aluminum alloy coupons irradiated to up to 53 MGy of absorbed cobalt-60 gamma dose. By exploring a variety of thermal pretreatment conditions for AA6061 coupons, we find that the “steady-state” yield of H 2 depends more on the aluminum alloy used than on the treatments applied prior to dry storage. Scanning electron microscopy and positron annihilation lifetime spectroscopy techniques also provided evidence for gamma radiation-induced defects in the corrosion layers of the investigated aluminum alloy coupons for high absorbed doses (~50 MGy), the consequences of which on cladding integrity and H 2 generation should be explored in future works.

38 - RADIATION CHEMISTRY, RADIOCHEMISTRY, AND NUCL↗
DOE OSTI2024

Modeling Approach for the Aluminum-clad Dry Storage Pilot using HFIR Fuel

To confirm that the dry storage of aluminum-clad research reactor spent nuclear fuel (ASNF) will remain within the safety envelope after applied drying schemes and that the resulting evolution of the gas space composition, temperature, and pressure conditions are understood, a dry storage pilot project is being established. The pilot will incorporate an instrumented lid for discrete interval or for on-demand gas composition and temperature monitoring of two DOE Standard Canisters (DSCs) loaded with three High Flux Isotope Reactor (HFIR) inner cores per DSC. Each DSC would be subjected to a separate alternative candidate drying scheme. Canisters will undergo 1 to 5 years of monitoring, including internal temperature and gas sampling to track pressure and composition changes. This report outlines the approach for modeling the ASNF-in-canister behavior in terms of evolving gas space conditions for the ASNF dry storage pilot using HFIR fuel. The ASNF has an adherent surface oxyhydroxide layer comprised of boehmite/bayerite that generates hydrogen when subjected to irradiation. Three-dimensional multi-physics computational fluid dynamics simulations will be executed to compute the thermal field within the DSC and provide inputs to a chemical model employed to compute pressure buildup as hydrogen is generated in the system. Implemented in Cantera, the chemical model solves gas phase and aluminum oxyhydroxide surface-mediated radiolysis reactions. Gas phase reactions are sourced from Wittman and Hanson (2015), whereas surface-mediated reactions are incorporated by fitting experimental data using an optimization algorithm (Abboud, 2023). Water radiolysis reactions from Wren and Ball (2001) are adopted with modifications as described in Abboud (2023c). Understanding the effect of the hydrogen buildup over time is important for long-term storage safety considerations. Modeling results will include the canister pressure, temperature, and composition evolution from the initial helium backfill with the addition of radiolytically-evolved chemical species (e.g., hydrogen and oxygen). The specific HFIR cores for the pilot program have not yet been selected, and the overall design is still in development. The CFD-chemical model used for this work will be based on prior models with necessary updates to allow for improved accuracy and efficiency. The experimental data obtained from the HFIR demonstration will be used to improve and validate the computational models to predict the ASNF-in-canister behavior.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2024

Mini-Canister Radiolysis Testing of ASNF Materials and Surrogates

An experimental irradiation campaign to investigate radiolysis behavior of ASNF was conducted using in situ gas monitoring of small, sealed stainless-steel vessels (mini-canisters) containing aluminum samples with adherent (oxy)hydroxide films under helium backfill. The samples were irradiated with gamma radiation from a Co-60 irradiator. The samples tested included aluminum plate assemblies with lab-grown (oxy)hydroxides as surrogates for fuel as well as an end cropping from an actual ASNF assembly retrieved from long-term wet storage. These experiments enabled investigation of the impacts of various fuel drying approaches on the radiolytic generation rate and measurement of the H 2 yield associated with a reactor exposed sample with reactor-formed (oxy)hydroxide. The resulting data can be incorporated into model development for ASNF in dry storage. This report presents the cumulative results from four surrogate assemblies tested after application of different preparation (drying) conditions as well as the ASNF cropping; some post-irradiation testing was included. The mini-canister results are compared to data from related experimental campaigns that also tested the impact of drying conditions using samples irradiated in glass ampoules and discusses implications of the combined data

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2024

Oxygen Limit for Flammability of a Gas Mixture of Helium – Hydrogen – Oxygen in the U.S. Department of Energy Standard Canister

The radiolytic breakdown of residual free, physisorbed, and chemisorbed waters is anticipated in the sealed dry storage of spent nuclear fuel (SNF), releasing H 2 gas into the initial cover gas of helium. For aluminum-clad SNF (ASNF) in particular, the expected total hydrogen in the canister is enough to dominate the cover gas mixture if fully released, and based on experimental rates of H 2 generation, H 2 percentages exceeding the lower flammability limit appear likely. However, no evidence of radiolytic generation of O 2 has been observed to date, so the potential for flammability is averted due to the lack O 2 . Lack of oxygen has been credited for avoiding flammability in some existing storage and transportation approaches for SNF and other waste. This report reviews literature on flammability limits with a focus on the limiting oxygen concentration to provide technical underpinnings to refine a flammability criterion for gas mixtures of helium, hydrogen, and oxygen where the oxygen is expected to be the limiting species. While there is general consensus on H 2 flammability limits at standard temperature and pressure, the decay heat and gas generation within ASNF sealed dry storage canisters could push them to elevated temperatures and pressures, so the goal is to identify an oxygen threshold that will bound the behavior over the temperature and pressure range of the U.S. Department of Energy (DOE) Standard Canister. The information reviewed in this document supports the criterion that the oxygen concentration in a He-H 2 -O 2 mixture should be less than 1.5% to avoid flammability at temperatures and pressures relevant to sealed dry storage of ASNF in the DOE Standard Canister, i.e., up to 343°C (650°F) and 500 psig, respectively. Note that while data covering the full range of temperature at atmospheric pressure and nearly the full range of pressure at room temperature were available, data for the combined effects was available only at moderate temperatures and pressures; the recommended 1.5% O 2 threshold is based on the breadth of available data reported here and apparent trends therein.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2025

Reference Fuel Development for Non-Aluminum Spent Nuclear Fuel Management

The Savannah River Site (SRS) L Area Facility provides for the safe receipt, storage, handling, and shipping of spent nuclear fuel (SNF) and has received more than 47,000 SNF assemblies since 1964. In order to consolidate receipt and storage analysis, L Area criticality safety has historically used several aluminum-clad “reference fuels” to establish bounding storage, handling, and cask loading limits and then applied a reactivity comparison approach to demonstrate that candidate fuels may be processed under the reference fuel limits. Currently, only aluminum-clad SNF from off-site research reactors are transferred on-site. The Accelerated Basin De-Inventory (ABD) program will begin the removal of bundled Non-Aluminum Spent Nuclear Fuel (NASNF) from the L Area disassembly basin for dissolution and disposition, which has driven the need for a non-aluminum reference fuel. This paper discusses the process and results of creating a new fictional homogenous NASNF highly enriched uranium reference fuel, “MITZ,” to be used in nuclear criticality safety evaluations for upcoming SNF disposition operations. Data demonstrating the relationship between neutron multiplication behavior and fuel spacing is generated for the new reference fuel MITZ as well as existing reference fuels representing several types of SNF assemblies.

Reference Fuel↗
DOE OSTI2025

Reference Fuel Development for Non-Aluminum Spent Nuclear Fuel Management

The Savannah River Site (SRS) L Area Facility provides for the safe receipt, storage, handling, and shipping of spent nuclear fuel (SNF) and has received more than 47,000 SNF assemblies since 1964. In order to consolidate receipt and storage analysis, L Area criticality safety has historically used several aluminum-clad “reference fuels” to establish bounding storage, handling, and cask loading limits and then applied a reactivity comparison approach to demonstrate that candidate fuels may be processed under the reference fuel limits. Currently, only aluminum-clad SNF from off-site research reactors are transferred on-site. The Accelerated Basin De-Inventory (ABD) program will begin the removal of bundled Non-Aluminum Spent Nuclear Fuel (NASNF) from the L Area disassembly basin for dissolution and disposition, which has driven the need for a non-aluminum reference fuel. This paper discusses the process and results of creating a new fictional homogenous NASNF highly enriched uranium reference fuel, “MITZ,” to be used in nuclear criticality safety evaluations for upcoming SNF disposition operations. Data demonstrating the relationship between neutron multiplication behavior and fuel spacing is generated for the new reference fuel MITZ as well as existing reference fuels representing several types of SNF assemblies.

Reference Fuel↗