NASA NTRS1977

Thermal degradation of the tensile strength of unidirectional boron/aluminum composites

The variation of ultimate tensile strength with thermal treatment of B-Al composite materials and of boron fibers chemically removed from these composites is studied systematically in an attempt to determine the mechanism of the resulting strength degradation. The results indicate that thermally cycling of B-Al represents a more severe condition than equivalent time at temperature. Degradation of composite tensile strength from about 1.3 GN/sq m to as low as 0.34 GN/sq m was observed after 3000 cycles to 420 C for 203-micron B-1100 Al composite. In general, the 1100 Al-matrix composites degraded somewhat more than the 6061 matrix material studied. Measurement of fiber strengths confirmed a composite strength loss due to the degradation of fiber strength. Microscopy indicated a highly flawed fiber surface. On the basis of various thermal-cycling studies and electron diffraction analysis, a mechanism is favored in which B reacts with Al, freshly exposed by cold working during cycling, to form AlB2. The nonuniform interface reaction leads to a highly flawed and weakened B fiber.

Grimes, H. H.↗

NASA NTRS1977

Continuous and cyclic thermal exposure induced degradation in boron reinforced 6061 aluminum composites

Boron reinforced 6061 aluminum (B/Al) composite was continuously exposed at 728 K for up to 240 hours and cyclically exposed between 293 K and 728 K for up to 6000 three-minute cycles. Room temperature tensile strengths were measured and the specimens were metallographically examined. The data suggest that, in addition to AlB2 formation, magnesium in the matrix diffused to the reaction layer and formed (Al,Mg)B2. This formation could weaken the matrix and embrittle the reaction layer. Continuous exposure degraded the strength of the B/Al specimens about 28% in 240 hours. However, the fracture mode, one indicative of high strength interfaces, did not change. The strength degradation was attributed to crack initiation in the brittle reaction layer causing stress concentrations in the fibers. Cyclic exposure degraded the strength of the B/Al about 34% in 6000 cycles. The fracture mode of the cyclic exposure specimens showed transition toward a mode characteristic of low interfacial strength. The lower interfacial strengths were attributed to stress fields induced by differential thermal expansion. Cyclic exposure degraded the strength of the B/Al specimens more than continuous exposure for similar cumulative exposure times.

Olsen, G. C.↗

NASA NTRS1978

Interface reaction and characterization in B/Al composites

Interfacial reactions, strength degradation, and fracture morphology have been characterized in B/Al(1100) and B/Al(6061) composite systems at a volume fraction of 0.55. Reaction was promoted by isothermal exposure at 350 C or 500 C for times up to 860,000 s. Tetragonal AlB12 was identified as the reaction product in the 6061 matrix and hexagonal AlB2 in the 1100 matrix. Interface development is analyzed based on a moving boundary model modified by the addition of ternary elements. While strength decreases in both systems, the time dependence of elevated-temperature exposure is different in the two matrix materials. In the 45 deg fiber orientation, failure occurs primarily by matrix shear, whereas in the 90 deg fiber orientation, fracture morphology is characterized by a mixture of fiber splitting, ductile matrix fracture, and failure at fiber-matrix interfaces.

Kim, W. H.↗

NASA NTRS1987

Silicon carbide sintered body manufactured from silicon carbide powder containing boron, silicon and carbonaceous additive

A silicon carbide powder of a 5-micron grain size is mixed with 0.15 to 0.60 wt% mixture of a boron compound, i.e., boric acid, boron carbide (B4C), silicon boride (SiB4 or SiB6), aluminum boride, etc., and an aluminum compound, i.e., aluminum, aluminum oxide, aluminum hydroxide, aluminum carbide, etc., or aluminum boride (AlB2) alone, in such a proportion that the boron/aluminum atomic ratio in the sintered body becomes 0.05 to 0.25 wt% and 0.05 to 0.40 wt%, respectively, together with a carbonaceous additive to supply enough carbon to convert oxygen accompanying raw materials and additives into carbon monoxide.

Tanaka, Hidehiko↗