Results for “Advanced High-Strength Alloy Skins”

NASA NTRS2021

Regolith Adaptive Modification Systems (Rams) - Final Report

Establishing human habitation on the Moon or Mars requires a palette of reaction chemistries for deconstructing extraterrestrial soils to extract structural metals, fuels, and propellants, as well as consolidating the soils into load-bearing forms. This report outlines progress related to the fundamental chemistry of in-situ resource utilization that is the focus of our Regolith Adaptive Modification System (RAMS) NIAC project. The RAMS concept is a breakthrough approach for preparing surfaces for early landing sites–and subsequent settlement operations–on the Lunar and Martian surface, among others. The RAMS concept is aligned with aspirations and capabilities of planned NASA Artemis mission. The approach is predicated on the sequential delivery of microcapsules onto lunar and Martian surfaces, which upon rupture, release payloads that react with regolith to yield geopolymerized subsurface slabs and surface high-strength steel skin and anchors . Through successively more exothermic reactions, we are seeking to build subsurface geopolymer slabs and use thermite reactions to constitute micro-alloyed advanced high-strength steel (AHSS) and Ti—Al—V pads on surfaces of planetary bodies, thereby circumventing the need for energy-intensive sintering technologies. As a precursor delivery system used to constitute landingpads, RAMS can be scaled for robotic, human-class, and more prominent (i.e., Starship) landers and will be configured within pressurized delivery systems that use radio beacons to outline coordinates for precision landings. Microcapsule delivery systems are designed to impel precursors (nanothermite mixtures and organosilanes), which activate in response to stress, heat, or impact to constitute deep geopolymerized slabs and AHSS skins. Dust mitigation is accomplished by reaction/solidification chemistry that yields a subsurface slab and advanced high-strength steel skin and anchors.

2021 NIAC Phase I↗

NASA NTRS2003

Characterization of Al-Cu-Mg-Ag Alloy RX226-T8 Plate

Aluminum-copper-magnesium-silver (Al-Cu-Mg-Ag) alloys that were developed for thermal stability also offer attractive ambient temperature strength-toughness combinations, and therefore, can be considered for a broad range of airframe structural applications. The current study evaluated Al-Cu-Mg-Ag alloy RX226-T8 in plate gages and compared performance with sheet gage alloys of similar composition. Uniaxial tensile properties, plane strain initiation fracture toughness, and plane stress tearing resistance of RX226-T8 were examined at ambient temperature as a function of orientation and thickness location in the plate. Properties were measured near the surface and at the mid-plane of the plate. Tensile strengths were essentially isotropic, with variations in yield and ultimate tensile strengths of less than 2% as a function of orientation and through-thickness location. However, ductility varied by more than 15% with orientation. Fracture toughness was generally higher at the mid-plane and greater for the L-T orientation, although the differences were small near the surface of the plate. Metallurgical analysis indicated that the microstructure was primarily recrystallized with weak texture and was uniform through the plate with the exception of a fine-grained layer near the surface of the plate. Scanning electron microscope analysis revealed Al-Cu-Mg second phase particles which varied in composition and were primarily located on grain boundaries parallel to the rolling direction. Fractography of toughness specimens for both plate locations and orientations revealed that fracture occurred predominantly by transgranular microvoid coalescence. Introduction High-strength, low-density Al-Cu-Mg-Ag alloys were initially developed to replace conventional 2000 (Al-Cu-Mg) and 7000 (Al-Zn-Cu-Mg) series aluminum alloys for aircraft structural applications [1]. During the High Speed Civil Transport (HSCT) program, improvements in thermal stability were demonstrated for candidate aircraft wing and fuselage skin materials through the addition of silver to Al-Cu-Mg alloys based on Al 2519 chemistry [2]. Thermal stability of the resulting Al-Cu-Mg-Ag alloys, C415-T8 and C416-T8, was due to co-precipitation of the thermally stable . (AlCu) and ' (Al2Cu) strengthening phases [1-4]. The strength and toughness behavior was investigated for these alloys produced as 0.090-inch thick rolled sheet in the T8 condition and after various thermal exposures. The mechanical properties were shown to be competitive with conventional aircraft alloys, 2519-T8 and 2618-T8 [2]. During the Integral Airframe Structure (IAS) program, advanced aluminum alloys were examined for use in an integrally stiffened airframe structure where the skin and stiffeners would be machined from plate and extruded frames would be mechanically attached (see Figure 1) [5]. Advantages of integrally stiffened structure include reduced part count, and reduced assembly times compared to conventional built-up airframe structure. The near-surface properties of a thick plate are of significance for a machined integrally stiffened airframe structure since this represents the skin location. Properties measured at the mid-plane of the plate are more representative of the stiffener web. RX226 was developed to exploit strength-toughness improvements and thermal stability benefits of Al-Cu-Mg-Ag alloys in plate gages. This study evaluated the microstructure and properties of three gages of plate produced in the T8 condition.

Lach, Cynthia L.↗